Criticism, as an evaluative criterion, is a significant speech act for English language learners to improve their speech and actions in their academic life. Yet, it is realized differently across diverse cultures. Few studies have shown that the linguistics forms of one language are different from those available in another language. Hence, this study aims to investigate the cross-cultural similarities and differences between 60 Iraqi and Malay university learners in the use of criticism strategies. The data are collected using a Discourse Completion Test (DCT) and a Focus Group Interview (FGI). The data are coded based on Nguyen’s (2005) coding scheme of criticism in terms of the realization strategies. Qualitative

Hydroisomerization of Iraqi light naphtha was studied on prepared Ni-Pt/H-mordenite catalyst at a temperature range of 220-300°C, hydrogen to hydrocarbon molar ratio of 3.7, liquid hourly space velocity (LHSV) 1 hr^-1 and at atmospheric pressure.

The result shows that the hydrisomerization of light naphtha increases with the increase in reaction temperature at constant LHSV. However, above 270 ⁰C the isomers formation decreases and the reaction is shifted towards the hydrocracking reaction, a higher octane number of naphtha was formed at 270 °C.

Some mechanical and thermal properties of mullite samples prepared by mixing different phases of alumina and silica powders have been studied according to ASTM methods the cold crushing strength of the sintcred bodies.With different porosity, at room temperature was in the range(18-54)Mpa

These factors, as well as disasters and wars that the Arab homeland exposed to and still under this exposure, in addition to the severe stress upon.

Iraqi Academics have been subjected to direct consequences of 2003 war. Exact figures are not known. It was mentioned. Many people were killed, sacked from their academics jobs, threatened to leave directly or indirectly their jobs, houses, and Iraq. Others have been imprisoned, tortured, or kidnapped / threatened to be kidnapped etc. Their families have been subjected to similar traumatic experiences or threats. All theses stressors may have lead to Post Traumatic (PTSD) Experiences. These Traumatic experiences have lead to Dislocation, relocation and Immigration etc. All sectors of

Fabrication of porous clay refractory insulating specimens from Iraqi kaolin with different percentage of Expanded Polystyrene (EPS) waste crumbs additions were investigated. After mixing and forming by hand molding, the specimens was dried and fired at 1300 oC. The structural, physical, mechanical and thermal properties of the refractory insulating products were measured. Maximum addition of EPS (1.25 wt%) lead to reduce the linear shrinkage to less than 1.7% and increased apparent porosity up to 50 %. As well as, the density, Modulus of rupture and thermal conductivity were reduced to 1.39 g/cm3, 4.1 MPa and 0.21 W/m.K, respectively. The final outcome, addition of EPS showed good results in the formation of pores without distorting the