Background: The longevity of any prosthesis depends on the materials from which it was fabricated, that is why, defects in the material properties may reduce the service life of prosthesis and necessitate its replacement. The aim of this study was to evaluate the effect of adding different concentrations of Polyamide-6 (Nylon-6) on the tear and tensile strength of A-2186 RTV silicone elastomer. Materials and Methods: 80 samples were fabricated by the addition of 0%, 1%, 3% and 5% by weight PA-6 micro-particles powder to A-2186 platinum RTV silicone elastomer. The study samples were divided into four (4) groups, each group containing 20 samples. One control group was prepared without PA-6 micro particles and three experimental groups were pr

This new azo dye 7-(3-hydroxy-phenylazo)-quinoline-8-ol was subsequently used to prepare a series of complexes with the chlorides of Fe, Co, Zn, Ru, Rh and Cd. The compounds identified by 1H and 13C-NMR, FT-IR, UV-Vis, mass spectroscopy, as well as TGA, DSC, and C.H.N., conductivity, magnetic susceptibility, metal and chlorine content. The results showed that the ligand behaves in a trigonal behavior, and that the complexes gave tetrahedral, except for Fe, Ru and Rh octahedral was given, that all of them are non-electrolytes. The effectiveness of both the compounds in inhibiting free radicals was evaluated by the ability to act as an antioxidant was measured using DPPH as a free radical and gallic acid as a standard substance, the

Amid the growing demand for multifunctional and environmentally benign materials, lead-free double perovskites have emerged as a strategically important development in advanced functional materials research. This study presents the synthesis of Ba2PrMnO6 (BPMO) double perovskite nanocrystals for the first time via a hydrothermal method, and a comprehensive evaluation has been conducted using the density functional theory (DFT) framework. Structural, thermodynamic, electronic, optical, and mechanical properties were investigated through X-ray diffraction (XRD), ultraviolet-visible (UV-vis) spectroscopy, FESEM/EDX, FTIR, and density functional theory (DFT) calculations. XRD confirms a stable tetragonal I4/m phase with experimental lattice con

Au nanoparticle-functionalized (TiO2)1−x(ZnO:MgO)x nanocomposite thin films (0≤x≤0.3) were effectively produced by chemical spray pyrolysis and annealed at 600 °C. The effects of ZnO incorporation and Au nanoparticle modification on the films' structural, optical, and antibacterial properties were studied using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), UV–Vis spectroscopy, and field-emission scanning electron microscopy (FESEM). XRD analysis confirms the formation of polycrystalline anatase TiO2 and shows a composition-dependent structural develop- ment with increasing ZnO concentration. The optical experiments revealed increased transmittance and a progressive wid- ening of the optical band gap f

Alloys from AgSb(SxSe1-x)2 with different compositions were prepared using quenching from the melt . This was done by put the appropriate amount of Ag, Sb,S and Se in an evaluated quartz ampoule , sealed and left at oven in temperature 1273 for 5 hours. Thin films with different composition were deposited by pulsed deposition technique PLD onto glass substrates at ambient temperature . This paper concerned on the investigate effect of composition on structural morphology, and electrical properties. The structure and morphology of the prepoared thin films were checked using X–ray diffraction and atomic force microscope. The D.C conductivity of the AgSb(SxSe1-x)2thin films with various x content was measured

One of the most effective ways of managing solid waste is microwave-assisted pyrolysis. This research used MW-assisted catalytic co-pyrolysis to extract essential oils from algae powder (AP) and date seed (DS). Graphite and a CaO nanocatalyst were utilized. As for the feedstock, it was a 1:1 mixture of AP and DS. The char content, oil production, and gas generation of co-pyrolysis yields varied between 18.8 wt% and 24.31 wt%, 43.08 wt%, and 55.295 wt%, and 25.905% to 32.60 wt%, respectively. The effect of the CaO nanocatalyst on product yields, feedstock conversion, and heating rates was analyzed. Product yields, average heating rates, and conversion factors were among the metrics studied to determine the synergistic effects and pyr

A series of new heterocyclic aromatic derivatives compounds were synthesized by reacted of Bis-methylene-di-(2-aminobenzoyl chloride) ‎with different chloride moieties such as piperidine-1-sulfonylchloride, Pryidine-3-sulfonylchloride, 4,4and#39;-(diazene-1,2-diyl)dibenzoyl-chloride and chloramphenicol respectively, to afforded a derivatives compound containing primary amine group [A-A4]. These derivative compounds [A-A4] were reacted with polyethanol using cold-warm esterification to synthesize of new graft polymers [B1-B4]. The structures of products were conforming by FT-IR and 1H-NMR spectroscopy. XRD-Diffraction of grafted polymer showed compound [B1 and B3] were crystal and semi-crystal respectively. As well as, derivatives

In this study, thin flms containing titanium dioxide (TiO₂), iron (III) oxide (Fe2O3) and cerium oxide (CeO2), with varying Fe2O3:CeO2 concentrations ranging from 0 to 30 wt% and 10 wt% gold nanoparticles (AuNPs), were prepared on glass using chemical spray pyrolysis. The structural, morphological, and sensing properties of the prepared thin flms were examined. XRD analysis revealed that a phase transformation occurred based on the dopant concentration: flms with x = 0 or 0.1 formed a polycrystalline anatase structure, whereas those with intermediate concentrations (x = 0.15 or 0.20) were amorphous. At higher doping concentrations (x = 0.25, 0.30), the structure developed a hematite Fe2O3, CeO2 and Au phase. Morphologicall