This article showcases the development and utilization of a side-polished fiber optic sensor that can identify altered refractive index levels within a glucose solution through the investigation of the surface Plasmon resonance (SPR) effect. The aim was to enhance efficiency by means of the placement of a 50 nm-thick layer of gold at the D-shape fiber sensing area. The detector was fabricated by utilizing a silica optical fiber (SOF), which underwent a cladding stripping process that resulted in three distinct lengths, followed by a polishing method to remove a portion of the fiber diameter and produce a cross-sectional D-shape. During experimentation with glucose solution, the side-polished fiber optic sensor revealed an adept detection

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

Two nanocomposite corrosion inhibitors were synthesized from Aloe vera extract: one incorporating sodium thiosulfate and the other silver nitrate. Both nanocomposites were subjected to structural characterization using atomic force microscopy (AFM), which revealed distinct morphological features. The sodium thiosulfate-based nanocomposite exhibited uniform and well-dispersed nanoparticles with an average size of 47.51 nm, suggesting a stable and homogeneous distribution. In contrast, the silver nitrate-based nanocomposite displayed slightly larger particles with an average diameter of 58.34 nm, indicating a tendency toward moderate aggregation. The corrosion inhibition performance of these nanocomposites for carbon steel (CS1137) was invest

         In this study, a bioadhesive dosage form of eoconazole nitrate for vaginal delivery was designed using a combination of bioadhesive polymers: Carbopol 941 p and sodium carboxymethylcellulose or methylcellulose in different ratios. The bioadhesive strength was evaluated by measuring the force required to detach the tablet from sheep vaginal mucosal membrane. It was found that the bioadhesive force was directly proportional to Carbopol 941 p content in the different formulae. The formulae were tested for their swelling behavior using agar gel plate method. The results showed that formulae containing a combination of Carbopol 941 p and sodium carboxymethylcellulose had greater swelling index

   In the present research the flame retardancy to  buildings and industrial foundations which are manufacturing from advanced polymeric  composite material was increased by coating it with surface layer included flame retardant material.  A(3mm) thick antimony tetroxide was used as a coated layer to retard and prevent the flame spread to the coating surface of polyester resin (SIROPOL 8340-PI) reinforced with hybrid fibers as a woven roving (°45-°0) consist of carbon and kevlar (49) fibers, and exposed it to direct flame generated from gas torch at temperature of (2000ºC), at  different exposed distance (10,15,20mm)and study the rang of resistance for this layer and its ability to protec

The aim of research is to show the effect of Ferric Oxide (Fe2O3) on the electricity production and wastewater treatment, since 2.5% of Ferric Oxide (Fe2O3) (heated and non heated) nanoparticles has been used. Characterization of nanoparticles was done using X-ray Diffraction (XRD) and Scan Electron Microscopy (SEM). The influence of acidity was also studied on both wastewater treatmenton the Chemical Oxygen demand (COD) and Biological Oxygen Demand (BOD) and voltage output was studied. From the results, it was infused that the dosage of 0.025 g/l and an initial pH 7 were founded to be optimum for the effective degradation of effluents. The results concluded that the treatment of anaerobic sludge wastewater using Ferric Oxide (Fe2O3) in

Helicobacter pylori (H. Pylori) is one of the most common infectious human pathogens. H. pylori could induce inflammation, that causes illnesses and disorders of upper gastrointestinal which including peptic ulcer diseases, dyspepsia, gastroesophageal reflux disease and gastric mucosa-associated lymphoid tissue (MALT) lymphoma. It is important to use a better tolerated and greatly effective eradication regimen. In this study, 75 newly diagnosed adult patients with H. pylori infection were included and completed the study, they were allocated into three groups with three different treatment regimens for H. pylori eradications; Group A (25 patients) received oral standard clarithromycin-based tr