Background: Studying and investigating the transverse strength(Ts), impact strength(Is), hardness (Hr) and surface roughness(Ra) of conventional and modified autopolymerizing acrylic resin with different weight percentages of biopolymer kraftlignin, after curing in different water temperatures; 40°C and 80°C. Material and Methods: Standard acrylic specimens were fabricated according to ADA specification No.12 for transverse strength, ISO 179 was used for impact testing, Shore D for hardness and profilometerfor surface roughness. The material lignin first dispersed in the monomer, then the powder PMMA is immediately added. Ligninadded in different weight percentages. Then cured using pressure pot (Ivomet) in two temperatures;40°C and 80°C under 2 bar pressure, for 30 minutes.Atotal of 144samples were prepared for this study. Ts, Is, Ra, and Hr were tested, by using Instron universal testing machine, charpy impact tester, shore D tester, and profilometer respectively. Results: The transverse strength increased in both the conventional and modified onewhen compared with that cured in air. The addition of 0.5wt% lignin gave the higher effect (78.0017MPa) with highly significant difference found between groups at 40°C polymerizing temperature. While the impact strength in both temperatures in the modified resin revealed increased results than conventional one, 1.25wt% of kraft lignin gave the highest value (12.7355KJ/m2) with highly significant differences found between groups at 80°C polymerizing temperature. Hardness and surface roughness showed also highly significant differences found between groups at 40°C polymerizing temperature, all the groups had increased Hr. than the control one (78.95), while the Ra. decreased for 1.0% ,1.25,1.50 and 1.75 wt% lignin content to (0.26,0.10,0.063, 0.12µm) respectively in 40°C polymerizing temperature, the lowest value present in 1.75 wt% lignin (0.05 µm) at 80°Cpolymerizing temperature. Conclusions: It seems that increasing the polymerizing temperature to 40°C had a positive effect on the mechanical properties of autopolymerizing acrylic resin and the one enforced by kraft lignin biopolymer in low percentages. Increasing the polymerizing temperature to 80°C will doesn’t have much positive effect but it doesn’t deteriorate the mechanical properties. However, when submitted to increasing the temperature to 80°C, specimens showed a significant increase in impact strength.
Abstract
This research aims to reform the Iraqi public budget through going into the challenges the budget faces in applying item-line budget in its preparation, implementation and control; which encourage extravagance and waste instead of rationalizing expenditures. This is shown in the data analysis of Federal public budget laws in Iraq for the years from 2005 till 2013; there was a continuous increase in the aggregate public expenditures in the public budget for the years previously mentioned, as the public expenditures growth has reached into the percent 284.71% in 2013. In addition the public budget for these years (2005-2013) is being prepared with planned deficit without confirming that
... Show More
The present study was performed to evaluate the level of some risk factors (biochemical and immunological) in hypothyroid Iraqi patients considering the different thyroid functional states (hypothyroidism and subclinical hypothyroidism).The study includes 82 patients clinically diagnosed with hypothyroidism. Three study groups have been investigated: (47 clinical hypothyroid patients, 12 subclinical hypothyroid patients 23 healthy individuals) of different ages. This study, show that the proportion of females (83.3 %), (87.2%) in subclinical and clinical hypothyroidisim respectively higher than the proportion of males (16.7%),(12.8%) in subclinical and clinical hypothyrodism respectively of the total patients.The majority of subclinical hyp
... Show MoreA comparison study was made for the reaction of triruthenium carbonyl Ru3(CO)12 with azoarene ArN=NAr . This reaction was monitored in two kinds of solvents , toluene , and n- octane , which yielded new triruthenium carbonyl complex Ru3(μ3-NAr)2(CO)9 . The reactions of azoarenes ArN=NAr with Ru3(CO)12 formed the following trinuclear compound of Ru3((μ3- NAr)2(CO)9 (Ar-C6H4Br-4) in law yield . In addition , to new isomers species of mononuclear cyclometallated of Ru(BrC6H4N-NC6H4NBr-4)2(CO)2 in different percentages . The mechanism of the reaction domenstrates that the formation of trinuclear bis arylimido complexes , and ortho metallated was , the result of cleavage of nitrogen –nitrogen bond . Monitoring this gave evidence that the rea
... Show MoreAbstract
This research aims to study human error effects in the banking risks in the private banks through the measurement and testing of human error effect in every kind of banking risks types and stand on the most closely associated with the risks in order to focus on them and make appropriate processors have with respect to and increase the availability of skills and expertise required to carry out banking operations of error-free manner.
Find dealt with human error in terms of meaning and understandable, classifications and types, causes and consequences and its approaches and theories. Also addressed placed banking risks in terms of meaning and concept, species and entr
... Show More
(1)
The aim of the research is to demonstrate the impact of organizational diversity management on achieving success, The problem of research is to create an appropriate work environment that stimulates everyone regardless of each dimension of diversity, So as to reach the best levels of success, The importance of research is to identify how the organization in question can manage organizational diversity effectively and contribute to its success, The research started from two main hypotheses which were derived from sub-hypotheses to identify the correlation and influence between the search variables by analyzing the answers of the research sample which included (81)
... Show More
The preparation of a new Azo compounds of highly conjugated dimeric and polymeric liquid crystal to achieve the crystalline characteristics Which have structures assigned based on elemental analysis, IR 1HNMR and CHNS-O while mesogenic properties have been set for DSC and hot-stage polarizing optical microscopy. The compounds show enantiotropicnematic phase being displayed. The compounds show photoluminescence properties in the organic solution at room temperature, with the fluorescence band centered around 400 nm.
Polycrystalline ingots of cadmium telluride have been synthesized using the direct
reaction technique, by fusing initial component consisting from pure elements in
stoichiometric ratio inside quartz ampoule is evacuated 10-6 torr cadmium telluride has
been grown under temperature at (1070) oC for (16) hr. was used in this study, the phases
observed in growing CdTe compound depend on the temperature used during the growth
process. Crystallography studies to CdTe compound was determined by X-ray diffraction
technique, which it has zinc blend structure and cubic unit cell, which lattice constants is
a=6.478
oA
This work is divided into two parts first part study electronic structure and vibration properties of the Iobenguane material that is used in CT scan imaging. Iobenguane, or MIBG, is an aralkylguanidine analog of the adrenergic neurotransmitter norepinephrine and a radiopharmaceutical. It acts as a blocking agent for adrenergic neurons. When radiolabeled, it can be used in nuclear medicinal diagnostic techniques as well as in neuroendocrine antineoplastic treatments. The aim of this work is to provide general information about Iobenguane that can be used to obtain results to diagnose the diseases. The second part study image processing techniques, the CT scan image is transformed to frequency domain using the LWT. Two methods of contrast
... Show More