Background: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirements, like low impact and transverse strength, poor thermal conductivity. The purpose of this study was to evaluate the effect of addition a composite of surface treated Nano Aluminum oxide (Al2O3) filler and plasma treated polypropylene fiber (PP) on some properties of denture base material. Materials and methods: One hundred fifty prepared specimens were divided into 5 groups according to the tests, each group consisted of 30 specimens and these were subdivided into 3 groups (unreinforced heat cured acrylic resin as control group),reinforced acrylic resin with( 0.5%wt Nano Al2O3 and2.5%wt plasma treated PP fibers) group and reinforced acrylic with(1%wt Nano Al2O3 and 2.5%wt plasma treated PP fibers group).The tests were impact strength, transverse strength, indentation hardness(shore D), surface roughness thermal conductivity. The results were statistically analyzed using ANOVA test. Results: A highly significant increase in impact strength, surface hardness, thermal conductivity with the addition of 0.5%wt. (Al2O3) and 2.5%wt PP fiber to(PMMA),also there is a significant increase in surface roughness and non significant increase in transverse strength. At the concentration of 1%wt nano (Al2O3) and 2.5%wt PP fiber there is a highly significant increase in impact strength surface hardness and thermal conductivity. Non-significant differences were shown in transverse strength and significant increase in surface roughness. Conclusion: The addition of a composite of Al2O3 nanoparticles and PP fiber to PMMA improves the impact strength, surface hardness and thermal properties, surface roughness while non-significant difference in transverse strength.
In study carried out in the cold storage in college of Agric./Univ. of Baghdad at 8 ? C. shows that Alternaria , Pencillium , Rhizoctonia , Mucor , are the fungi that causes tomato fruits decay. This is the first record of Rhizoctonia and Mucor as a Tomato fruits rot under 8º c in Iraq. There is no fungal infection on cucumber fruits under 8 ? C. . Waxing tomato fruits reduced the severity of the fungi infection and gave shelflife (19 days) under 8 ? C. There is an infection with Mucor was found in tomato fruits kept in perforated polyethylene bages with 16 bores prevent the infection and the lowest severity and frequency of infection was found in waxed tomato fruits. Part of M.Sc thesis of the Second author.
Aim: To evaluate the effect of two bonding systems and two curing systems on sealing ability of class V composite restorative materials. Materials and methods: This study was performed in vitro on 40 caries free upper first premolar teeth. The Standardized class V cavity preparation on buccal and lin- gual surfaces of each tooth was done. Then the teeth were randomly divided into two major groups each of twenty. 40 cavities were performed on these teeth and the first group7th generation bonding agent (i Bond) were applied according to the manufacturer instructions and single increment of univer- sal composite (XRV Herculite) from kerr were applied and twenty of the cavities were cured with con- ventional light cure device (astralis-5) and t
... Show More
A thin film of AgInSe2 and Ag1-xCuxInSe2 as well as n-Ag1-xCuxInSe2 /p-Si heterojunction with different Cu ratios (0, 0.1, 0.2) has been successfully fabricated by thermal evaporation method as absorbent layer with thickness about 700 nm and ZnTe as window layer with thickness about 100 nm. We made a multi-layer of p-ZnTe/n-AgCuInSe2/p-Si structures, In the present work, the conversion efficiency (η) increased when added the Cu and when used p-ZnTe as a window layer (WL) the bandgap energy of the direct transition decreases from 1.75 eV (Cu=0.0) to 1.48 eV (Cu=0.2 nm) and the bandgap energy for ZnTe=2.35 eV. The measurements of the electrical properties for prepared films showed that the D.C electrical conductivity (σd.c) increase
... Show More
(9)
(9)
(1)
(1)
This study examined the effect of essential oils extracted from peel of Citrus paradisi and Citrus sinensis on two species of fungi: Penicillium oxalicum and Fusarium oxysporum as well as effect of two fungicides: Carbendazim and Thiophanatemethyl against above fungi. Results showed that the essential oil of Citrus paradisi inhibited the radial growth of Penicillium oxalicum and Fusarium oxysporum at concentration 4%. Nevertheless, the essential oil of Citrus sinensis inhibited the radial growth at concentration 5 and 4%, respectively. Furthermore, the two studied fungicides inhibited radial growth of these fungi too. Therefore, there are a positive relationship between the evaluating of concentration and the percentage of inhibiting of rad
... Show More
(3)
In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d
(2)
Thin films of Nb2O5 have been successfully deposited using the DC reactive magnetron sputtering technique to manufacture NH3 gas sensors. These films have been annealed at a high temperature of 800°C for one hour. The assessment of the Nb2O5 thin films structural, morphological, and electrical characteristics was carried out using several methods such as X-ray diffraction (XRD), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS), Hall effect measurements, and sensitivity assessments. The XRD analysis confirms the polycrystalline composition of the Nb2O5 thin films with a hexagonal crystal structure. Furthermore, the sensitivity, response time, and recovery time of the gas sensor were evaluated for the Nb2O5 thin film
... Show More
(2)
(1)
(33)
(32)