Background The application of nanotechnology to biomedical surfaces is explained by the ability of cells to interact with nanometric features. The aim of this study was to consider the role of nanoscale topographic modification of CPTi dental implant using chemical etching method for the purpose of improving osseointegration. Materials and methods: Commercial pure titanium rod was machined into 20 dental implants. Each implant was machined in diameter about 3mm, length of 8mm (5mm was threaded part and 3mm was flat part). Implants were prepared and divided into 2 groups according to the types of surface modification method used: 1st group (10 implant) remained without nano surface modification (control), 2nd group include (10 implant) etched with 15N H2SO4 and 30% H2O2, Surfaces were characterized by scanning electron microscope (SEM), Xray diffraction (XRD), atomic force microscope (AFM), thickness measurement for the invitro experiments. While for invivo part tibia of 5 white new Zealand rabbits were chosen as implantation sites. The tibia of each rabbit received two screws. Biomechanical test was performed to understand the bone-implant interface, after two weeks healing periods. Implants from 4animals were tested for the torque required to remove the implant from the bone and the other one animal was prepared for histological examination. Results and Conclusion: For in vitro results, scanning electron microscope showed that the chemical etching of Ti substrate becomes highly porous and has surface consisting of nanosized pits. Removal torque means value after 2 weeks of implantation mentioned that, there was a gradual increase in the removal torque mean values as a follow (M±SD): 12.625(N.cm) ± 0.517, 30.500(N.cm) ± 4.071for machined surface(X), nano chemically etched (X1) respectively. In addition, the histological analysis showed improved quality of bone in response to the nano modified screws, that the chemically treated implants shows trabeculated thread.
This article presents the simultaneous adsorption of bimetal Cu2+ and Zn2+ from an aqueous solution using activated carbon synthesized from a plum seed precursor by sulfuric acid and microwave activation: plum seeds chemically activated by 45% (w/w) sulfuric acid with 2:1 ratio for 4 h, then carbonized for 2 h at 700 °C and the product obtained activated in a microwave oven for 20 min at 700 W for final of activation. Plum seeds and activated carbon produced were characterized in terms of their physical and chemical composition using Brunauer–Emmett–Teller measurements, field emission scanning electr
... Show More
(2)
(1)
(25)
(20)
Staphylococcus Sp.is the most common type of bacteria found in contamination place, we design this
study to compare the contamination accident between two hospitals in Baghdad.One of them isthe Burns
Specialist Hospital in the Medical CityinRusafa and another one is Al-Karama Hospital in Karkh. The
samples were collected fromOperativeWard No1 (OW1), Operative Ward No2 (OW2), Consulting Pharmacy
(CP), Emergency Room (ER), Reception Room (RR), Women's Ward (WW) and Men's Ward (MW).The
samples were taken from inside each clinical unit, surfaces, food, and air. The results showed that the
number of samples containing Staphylococcus sp. bacteria is 81, including 45 belonging to Al-Karama Burns
Ward Ho
(5)
(2)
(6)
(3)
Zinc oxide thin films were deposited by chemical spray pyrolysis onto glass substrates which are held at a temperature of 673 K. Some structural, electrical, optical and gas sensing properties of films were studied. The resistance of ZnO thin film exhibits a change of magnitude as the ambient gas is cycled from air to oxygen and nitrogen dioxide
Background: Poly (methyl methacrylate) has been widely utilized for fabrication of dentures for many years as it has good advantages but not achieved all demands of the mechanical properties such as low transverse strength, low impact strength, low surface hardness, high water solubility and high water sorption. Material and method: To provide bonding between ZrO2 nanoparticles and PMMA matrix, the ZrO2 Nano-fillers were surface-treated with a saline coupling agent. Plasma surface treatment of polyethylene (PE) fiber was done to change surface fiber by using DC- glow discharge system. For characterization of interring any functional groups, the (FTIR) spectrum were done .then the mechanical properties studied to choose the appropriate perc
... Show More
Industrial development has recently increased, including that of plastic industries. Since plastic has a very long analytical life, it will cause environmental pollution, so studies have resorted to reusing recycled waste plastic (sustainable plastic) to produce environmentally friendly concrete (green concrete). In this research, producing environmentally friendly load-bearing concrete masonry units (blocks) was considered where five concrete mixtures were compressed at the blocks producing machine. The cement content reduced from 400 kg/m3 (B-400) to 300 kg/m3 (B-300) then to 200 kg/m3 (B-200). While (B-380) was produced using 380 kg/m3 cement and 20 kg/m3 nano-sil
... Show More
(4)
Abstract In the current contribution, a novel binuclear nickel(II) and zinc(II) complexes were prepared from a hexadentate ligand prepared via condensation of 3,3'-Bipyridine-6,6'-dicarbaldehyde , 2-amino-5-chlorobenzaldehyde and 2-Aminophenol .The symmetric ligand (H2DTPE) and its metal complexes were illustrated utilizing various techniques of physicochemical containing magnetic moment, analytical analysis and spectroscopy of mass, IR, 13C and 1H NMR, TGA and UV-Vis. The particles of MO Nanoscale were created from the labeled complex applying the ways of pyrolysis and utilizing methods of XRD, FT-IR, and FE-SEM, that specified close compatibility with the typical pattern for nanoparticles of NiO, ZnO and appeared the reasonable size in
... Show MoreIn the present paper, chitosan Schiff base has been synthesized from chitosan’s reaction with the salicyldehyde. The AuNPs was manufacture by extract of onion peels as a reducing agent. The Au NPs that have been prepared were characterized through the UV-vis spectroscopy, XRD analyses and SEM microscopy. The polymer blends of the chitosan Schiff base / PVP has been prepared through using the approach of solution casting. Chitosan Schiff base / PVP Au nano-composites was prepared. Nano composites and polymer blends have been characterized by FTIR which confirm the formation of Schiff base by revealing a new band of absorption at 1651cm-1 as a result of the (C=N) imine group. SEM, DSC and TGA confirms the thermal stability of
... Show More
(13)
(3)