Background: Limited data are available on the dimensional stability and surface roughness of ThermoSens, which is a material used in denture processing. This study aimed to measure the vertical teeth changes and surface roughness of ThermoSens dentures prepared using three different investment materials. Materials and methods: For the dimensional changes test, 30 complete maxillary dentures were prepared using different investment methods: group I, dental stone; group II, silicone putty; and group III, a mixture of dental stone and plaster (ratio, 1:1; n = 10 for each group). Four screws were attached to the dentures: two were attached to the buccal surface of the canine and first molar, and the other two were attached in the flange areas of the canine and first molar in line with the previously mentioned screws. Measurements were made using a micrometer microscope in the wax stage before flasking and in the deflasking stage. The above investment techniques were also used to prepare samples for a surface roughness test (n = 10 per group). These samples were prepared according to the specifications of the American Dental Association. Data were examined using analysis of variance (ANOVA) and the least significant difference (LSD) test. Results: One-way ANOVA and LSD revealed that dimensional changes significantly differed among all groups, except that the vertical teeth changes on the left side did not differ between groups I and II for both the canine and molar regions. Surface roughness was significantly higher in group I than in group II, and in group III than in group II. Conclusion: The use of putty silicone for investing ThermoSens complete dentures reduced dimensional changes and resulted in dentures with a better fit. Surface roughness could be reduced by the addition of a putty silicone layer over the denture before the addition of the second investment layer during denture processing.
This research is concerned with a new type of ferrocement characterized by its lower density and enhanced thermal insulation. Lightweight ferrocement plates have many advantages, low weight, low cost, thermal insulation, environmental conservation. This work contain two group experimental : first different of layer ferrocement, second different of ratio aggregate to cement. The experiments were made to determined the optimum proportion of cement and lightweight aggregate (recycle thermestone ). A low W/C ratio of 0.4 was used with super plasticizer conforming to ASTM 494 Type G. The compressive strength of the mortar mixes is 20-25 MPa. The work also involved the determination of thermal properties .Thermal conductivity value of thi
... Show More
(2)
The aim of this work was to prepare zeolite type 13X from locally available kaolin and to study the effects of using some binding materials through the process of agglomeration of this zeolite. This study was focused on using kaolin binder in different weight percents (10,15,25,35 and 45%).Physical and mechanical properties of the agglomerates such as porosity , apparent density , pore volume, crushing strength , loss on attrition , surface area and finally the adsorption capacity had been measured and evaluated .The preparation step was achieved by mixing the reactants consisting of metakaolin , source of silica as ( sodium trisilicate ) and sodium hydroxide . The conditions was temperature of 70° C and time of mixing as 8, 10,24,34,50
... Show More
(5)
(9)
A factorial experiment was applied with four replicates on rosemary plants (Rosmarinus officinalis L.) grown in pots inside the glasshouse of the Department of Biology, College of Science, Salahaddin University, Erbil, Iraq, during April, 2019 to July, 2020, to determine the effects of soil moisture content ( SM1: 100% and SM2: 60% field capacity), nitrogen fertilizer (N1: 100, N2: 200 and N3: 300kg/hectare), and magnesium fertilizer (Mg1: 0.0, Mg2: 30 and Mg3: 60kg/hectare) and their interactions on some growth characteristics and essential oil content of rosemary plants. Two cuttings were taken from rosemary shoots (on March, 2020 and July, 2020) after 12 and 15 months of planting respectively. Results showed that cutting 1:
... Show More
(1)
(1)
The current study aims to show the importance of plant products as mosquitocides against Culex quinquefasciatus. Castor oil Nanoemulsions were subedit in various ratios including castor oil, ethanol, tween 80, and deionized water by using ultrasonication. Thermodynamic, centrifugation, PH, assay which improved that the formula of 10 ml of castor oil, ethanol 5ml, tween 80 (14 ml) and deionized water 71ml was more stable than other formulas. The stable formula of castor oil nanoemulsion was characterized by transmission electron microscopy (TEM) and dynamic light scattering (DLS). Nanoemulsion droplets were spherical in shape and were found to have a Z-average diameter of 87.4nm. A concentration of ca
... Show More
(3)
(2)
The corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ΔH, and activation entropies, ΔS, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the
... Show MoreBackground: This study aimed to compare the surface microhardness (MH) and mineral content of white spot lesions(WSLs) after using bioactive glass (BAG)casein phosphopep-tides-amorphous calcium phosphate(CPP-ACP),and nanohydroxyapatite(Nano-HAP) under pHcycling. Material and method:18 sound maxillary first premolar were used for the study.10 were selected for the vickers microhardness test, For Energy-dispersive X-ray spectroscopy analysis (EDX), the remaining 8 premolar teeth were used, 40 sections of enamel blocks (Four from each tooth) were produced from the middle part of the buccal and palatal surfaces of teeth for MH test while 48 sections of enamel blocks (Six from each tooth) were produced for EDX analysis. Enamel slabs were
... Show More
(11)
(7)
Background: This study aimed to compare the surface microhardness (MH) and mineral content of white spot lesions(WSLs) after using bioactive glass (BAG)casein phosphopep-tides-amorphous calcium phosphate(CPP-ACP),and nanohydroxyapatite(Nano-HAP) under pHcycling. Material and method:18 sound maxillary first premolar were used for the study.10 were selected for the vickers microhardness test, For Energy-dispersive X-ray spectroscopy analysis (EDX), the remaining 8 premolar teeth were used, 40 sections of enamel blocks (Four from each tooth) were produced from the middle part of the buccal and palatal surfaces of teeth for MH test while 48 sections of enamel blocks (Six from each tooth) were produced for EDX analysis. Enamel slabs were divi
... Show More
(11)
(7)
The objective of this study was to investigate the release profile of different fat and water soluble bases using diazepam as a model drug , and then to develop a satisfactory formula with a rapid release of diazepam from suppository bases .The study was conducted using theobroma oil ,glycerol-gelatin and glycerol-PEG1540 bases using conventional mold method for preparation .while the later base was utilized to incorporate diazepam ( buffered solution ) in a hollow type suppositories. The results indicated that all types of bases can be utilized to formulate diazepam as rectal suppositories with acceptable disintegration time ( 12, 10, 6, and 6min.), respectively . While 100% of the released drug had been shown differen
... Show More
(1)