Natural dye sensitized solar cell was prepared using strawberry and pomegranate dyes with anatase nanocrystalline titanium dioxide powder. A study of the optical properties of the two dyes, involving the absorption spectrum was determined in the visible region. I-V characteristics under illumination were performed. The results showed that the two prepared dye sensitized solar cells have acceptable values efficiency about (0.94 with Fill factor (45)) and (0.74 with Fill factor (44)) for strawberry and pomegranate dyes, respectively.

A reinforced concrete frame is referred as "RIGID FRAMES". However, researches indicate that the Beam-Column joint (BCJ) is definitely not rigid. In addition, extensive research shows that failure may occur at the joint instead of in the beam or the column. Joint failure is known to be a catastrophic type which is difficult to repair.
This study was carried out to investigate the effect of hoops and column axial load on the shear strength of high-strength fiber reinforced Beam-Column Joints by using a numerical model based on finite element method using computer program ANSYS (Version 11.0). The variables are: diameter of hoops and magnitude of column axial load.
The theoretical results obtained from ANSYS program are in a good a

This paper presents the results of investigating the vibrational characteristics of oblate dish with and without framed structure . A finite element method, was applied to the dynamic analysis of oblate spheroidal shell. Different types of elements were considered in one dimension and two dimensions. It was found that the natural frequencies of oblate shells had two types of behavior against increasing the shell thickness and eccentricity, which are the membrane mode and bending mode –Since – the membrane modes natural frequencies tend to increase with the increasing the eccentricity of oblate, while the bending modes natural frequencies decrease with the increasing the eccentricity till reach the optimum eccentricity.

تستهدف هذه الدراسة وبشكل أساس، الكشف عن طبيعة وخصائص البعد السياسي لهندسة/صناعة الخصائص الاجتماعية والسياسية للإنسان والمجتمع، بوصفها العملية المسؤولة عن تصميم هذه الخصائص وصناعتها وتغييرها جزئيا أو كليا، دون أبعادها الأخرى المتعددة والمتنوعة، لا لمجرد الانسياق وراء دوافع الرغبة الذاتية، أو اعتبارات التخصص الدقيق وأحكامه، لأن معهما أيضا، بل وقبلهما أحيانا، دوافع واعتبارات أخرى موضوع

Abstract: The premise of the study is that populism is a process of building political views and critical intellectual orientations among the general public. It is transformed into mass beliefs by mobilizing the society ideologically and continuously in order to reach or control the circle of authority. We distributed the study topics to four sections: In the second, we will discuss the contents of contemporary populism and how other forms of populism evolved historically. The third is to discuss the political discourse of populism among the military regimes and the comparative Islamic parties in the Middle East, especially in terms of the essence and the intellectual foundations. The fourth section seeks to examine the characteristics o

: Porous silicon (n-PS) films can be prepared by photoelectochemical etching (PECE) Silicon chips n - types with 15 (mA /cm2), in15 minutes etching time on the fabrication nano-sized pore arrangement. By using X-ray diffraction measurement and atomic power microscopy characteristics (AFM), PS was investigated. It was also evaluated the crystallites size from (XRD) for the PS nanoscale. The atomic force microscopy confirmed the nano-metric size chemical fictionalization through the electrochemical etching that was shown on the PS surface chemical composition. The atomic power microscopy checks showed the roughness of the silicon surface. It is also notified (TiO2) preparation nano-particles that were prepared by pulse laser eradication in e

A modified chemical method was used to prepare titanium dioxide nanoparticles (TiO2 NPs), which were diagnosed by several techniques: X-ray diffraction, Fourier transform infrared, field emission scaning electron microscopy, energy disperse X-ray, and UV-visible spectroscopy, which proved the success of the preparation process at the nanoscale level. Where the titanium oxide particles have an average particle size equal to 6.8 nm, titanium dioxide particles were used in the process of adsorption of Congo red dye from its aqueous solutions using a batch system. The titanium oxide particles gave an adsorption efficiency of Congo red dye up to more than 79 %. The experimental data of the adsorption process were analyzed with kinetic models and

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a