Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the most important problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2% chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours and three months of water storage. Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which were acid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth each according to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application for groups I and III which were tested after twenty-four hours and three months respectively, while the distal water was applied for 60 seconds before the application of adhesive for group II and IV which were tested after twenty-four hours and three months respectively.The Prime and Bond® NT™ adhesive (Dentsply) was applied and cured, Composite (Ceram X mono, Dentisply) was applied through special mold with 2 mm thickness and light cured, Then all specimens were stored in distilled water 37oC until the time of testing of each group.Shear bond strength test was performed at the end of the storage period (24 hours or 3 months). Results:T-test results showed high statistically significant reduction in shear bond strength (SBS) in non CHX group IV (tested after 3 months) compared to non CHX group II (tested after 24 hours)(P< 0.01). In CHX groups I (tested after 24 hours) and III (tested after 3 months), results showed no statistically significant differences in shear bond strength(p> 0.05).On the other hand result showed statistically no significant differences between groups I and II in 24 hours shear bond strength (P> 0.05). After 3 months water storage, there was statistically high significant differences between the groups III and IV (P< 0.01). Conclusion: the use of 2 % CHX glocounate solution after acid etching and before bonding of dentin have no adverse effect on immediate bond strength (24 hours storage), and was effective in reducing degradation of resin-dentin bond interface after three months of water storage.
In humans, Pseudomonas aeruginosa is the second most frequent gram negative nosocomial pathogen in hospitals and has the highest case-fatality rate of all hospital-acquired bacteremia because of the hardy resistance of these bacteria to mechanical cleansing as well as to disinfectant, and many antibiotics. The susceptibility of bacteria against the antibiotics is modulated by several local factors such as temperature which modified drug efficacy, so this study was carried out to evaluate the effect of different temperature (20,42,45)Ċon the susceptibility of Pseudomonas aeruginosa to the minimum inhibitory concentrations (MIC) of the antimicrobial agents before and after irradiation. The samples collected from 150 persons suffering from
... Show MoreThis in order to test the effect of food on growth and fecundity, two kinds of food have been used the algae Scendesmus quadricaudae and fresh water shrimp powder. For two generations, growth and productivity have been followed up. The fresh water shrimp has been noticed as a food better than algae, because it caused recording, for the two generation higher length rate for the weeks of experiment. The individuals length rate at the end of the forth week reached 9.35 and 9.48 mm for the first generation and second generation respectively. The average length weekly increase rate for the first and second generations individuals feeding on dried shrimp was higher through the first and second week compared to what was recorded when feeding alga
... Show More
The structural, optical properties of copper oxide thin films ( CuO) thin films which have been prepared by thermal oxidation with exist air once and oxygen another have been studied. Structural analysis results of Cu thin films demonstrate that the single phase of Cu with high a crystalline structure with a preferred orientation (111). X-ray diffraction results confirm the formation of pure (CuO) phase in both methods of preparation. The optical constant are investigated and calculated such as absorption coefficient, refractive index, extinction coefficient and the dielectric constants for the wavelengths in the range (300-1100) nm.
(6)
(2)
(11)
(11)
Farmers keep trying to avoid using chemical fertilizer without losing high yield. A field experiment was conducted in the fields of Agriculture College, University of Baghdad during winter seasons of 2015 and 2016 to investigate the response of three bread wheat (Triticum aestivum L.) cultivars (Ibaa99, Abu-Ghraib3 and Buhooth22) to the frequency of spraying with biofertilizer (EM-1) (one time at tillering stage, twice at tillering and stem elongation stages and three times at tillering, stem elongation and booting stages) in addition to the control (without spraying), to the increase of grain yield. Randomized complete block design (RCBD), in split plots arrangement and four replications, was used. Spraying treatments were placed as main p
... Show More
(8)
(6)
Abstract: Recombinant human bone morphogenetic protein-2 (rhBMP-2) and platelet-rich fibrin (PRF) bioactive materials have been used to enhance healing and improve dental implant stability. This study aimed to compare the effect of rhBMP-2 and PRF bioactive materials on dental implant stability at different intervals and to evaluate the correlation of implant length and diameter with implant stability. Two bioactive materials were compared to evaluate their effect on dental implant stability. A total of 32 patients (102 dental implants) were divided into 3 groups: 24 dental implants with bone morphogenetic protein (BMP), 27 dental implants with PRF, and 51 dental implants without BMP or PRF (control group). Data were statistically analyzed
... Show More
(17)
(21)
(2)
(2)
In recent years, there has been a rapid development in research on high performance ceramics for mechanical, electrical and medical industries. This development will be shown for alumina as a representative for oxide ceramics powders.
Dry–pressing forming technique was used to prepare different ceramic compacts for alumina grafted by polymethacrylate polymers. All Alumina compact were fired firstly at 1200 ◌ْ C, then
at 1600 ◌ْ C.
Mechanical strength was examined in different means, some
depends on compression and other depends on impact. Hardness was
also measured .The results obtained were compared with that of
Alumina compact prepared under the same condition from Alumina
especially made for pressing .