Background: Lack of durability of the bond of the dental adhesive systems to tooth structure is one of the most important problems in tooth colored restorative work. This in vitro study was performed to evaluate the effect of 2% chlorhexidine gluconate(CHX) on dentin bond strength by using total etch adhesive system at twenty-four hours and three months of water storage. Material and methods:A flat dentin surface was prepared for forty sound human maxillary premolar teeth which were acid etched with 36% phosphoric acid gel after being divided randomly into four groups of ten teeth each according to storage time and CHX application, theCHX was applied for 60 seconds before adhesive application for groups I and III which were tested after twenty-four hours and three months respectively, while the distal water was applied for 60 seconds before the application of adhesive for group II and IV which were tested after twenty-four hours and three months respectively.The Prime and Bond® NT™ adhesive (Dentsply) was applied and cured, Composite (Ceram X mono, Dentisply) was applied through special mold with 2 mm thickness and light cured, Then all specimens were stored in distilled water 37oC until the time of testing of each group.Shear bond strength test was performed at the end of the storage period (24 hours or 3 months). Results:T-test results showed high statistically significant reduction in shear bond strength (SBS) in non CHX group IV (tested after 3 months) compared to non CHX group II (tested after 24 hours)(P< 0.01). In CHX groups I (tested after 24 hours) and III (tested after 3 months), results showed no statistically significant differences in shear bond strength(p> 0.05).On the other hand result showed statistically no significant differences between groups I and II in 24 hours shear bond strength (P> 0.05). After 3 months water storage, there was statistically high significant differences between the groups III and IV (P< 0.01). Conclusion: the use of 2 % CHX glocounate solution after acid etching and before bonding of dentin have no adverse effect on immediate bond strength (24 hours storage), and was effective in reducing degradation of resin-dentin bond interface after three months of water storage.
This study was conducted to determine the effects of concentration of hydrochloric acids, temperature, and time on the hydrolysis of soya proteins (defatted soya flour) by determining the value of total protein nitrogen concentration, and amino nitrogen concentration of protein, peptides, and amino acids, and then calculated the hydrolysis rate of proteins.
The variables of the conditions of hydrolysis process was achieved in this study with the following range value of tests parameter:
- Concentration of HCl solution ranged between 1-7 N,
- Hydrolysis temperature ranged between 35-95 °C, and
- The time of hydroly
Background: Squamous cell carcinoma is a disease of elderly peopleand it is uncommon in people with less than 40 years old; however many literatures revealed that tumor developing in patients younger than forty years appears more aggressive at the time of diagnosis. The purpose of the present study was to focus on the clincopathological features of the oral SCC in different age groups. Material and methods: In this study thirty five cases of paraffin embedded tissue blocks of oral squamous cell carcinoma were studied. The age range was from 16 to 80 years. The clinicopathological data were recorded for evaluating the tumor characters according to age of patients. Results : The age was not significantly correlated to the clinicopathological
... Show More
(3)
(3)
The effect of the concentration of the colloidal nanomaterial on their optical limiting behavior is reported in this paper. The colloids of sliver nanoparticles in deionized water were chemically prepared for the two concentrations (31 ppm and 11ppm). Two cw lasers (473 nm Blue DPSS laser and 532 nm Nd:YAG laser) are used to compare the optical limiting performance for the samples. UV–visible spectrophotometer, transmission electron microscope (TEM) and Fourier Transformation Infrared Spectrometer (FTIR) were used to obtain the characteristics of the sample. The nonlinear refractive index was calculated to be in the order of 10-9 cm2/W. The results demonstrate that the observed limiting response is significant for 532nm. In addition, t
... Show MoreZSM-5 zeolite was synthesis under hydrothermal conditions at 175oC. The synthesis parameters have been investigated to find optimum synthesis method. Firstly, the crystallization time has been investigated to find the optimum crystallization time. Also, the ageing time was studied. The morphology, structure, and composition of the synthesized ZSM-5 zeolite were characterized using scanning electron microscopy (SEM), pH meter, viscometer, and X-ray powder diffraction (XRD). The bulk Si/Al ratio of ZSM-5 zeolite was in the range of 9.5—11.7. The synthesized ZSM-5 zeolite with appropriate ageing time could adjust crystal size and degree of the crystallinity. The crystal size of ZSM-5 zeolite obtained at an agei
... Show More
(3)
The current study aimed at identifying the impact of each of the full and part time summer enrichment programs on the performance of gifted students. Moreover, it aimed to study the difference between the full and part time programs on the performance of gifted students. The study sample consisted of (115) students from the full time programs and (137) students from the part time programs, they have been randomly selected from the gifted students participating in the full and part time summer enrichment programs. The researcher used the scale of student performance. The results indicated that there were statistically significant differences between the averages of the pre and post applications of the
... Show MoreIn this research, hand lay- up technique is used to prepare samples from epoxy resin reinforced with multi- walled carbon nanotubes in different weight fractions (0, 2, 3, 4, 5) wt%. The immersion effect by sodium hydroxide solution (NaOH) at normality (0.3N) for a period of (15 days) on the thermal conductivity of nanocomposites was studied, and compared to natural condition (before immersion). The thermal conductivity of epoxy nanocomposites specimens were carried out using Lee’s disk method. The experimental results showed that thermal conductivity increased with increase weight fraction before and after immersion for all specimens, while the immersion effect leads to decrease thermal conductive values compared to thermal conductivi
... Show More
Recently, some of Iraq's newly constructed asphalt concrete pavements showed premature failures with significant negative impacts on roadway safety and the economy. Using Nano hydrated lime (NHL) in pavement construction could be one of the possible steps to improve pavement durability. This article discusses how NHL affects the durability of hot mix asphalt. NHL was added in two methods to the asphalt concrete mixture for the wearing course. The first is the dry method, i.e., on the aggregate, whereas the second is the wet addition method, i.e., to the bitumen. The percentages were tried for each additional method; 1, 2, and 3% by weight of aggregate for the dry method and 0.5, 1, and 1.5% by weight of asphalt concrete for the wet