Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups. The tests conducted in this study were: impact strength test, transverse strength test, surface hardness test, surface roughness test, water sorption test, water solubility test and color change measurement after addition. The results were statistically analyzed by t-test at p value≤ 0.05. Results: Characterization methods results showed the incorporation of sliver and zinc ion without change of zeolite structure framework. A non-significant effect resulted from the addition of 0.5% sliver –zinc zeolite on the impact strength, transverse strength, surface hardness, surface roughness and cause no change in color of heat cure denture base. Also a highly significant decrease in water sorption and a significant increase of water solubility were observed. Conclusion: Preparation of sliver-zinc zeolite could be performed successfully and the addition of 0.5% of antimicrobial sliver-zinc zeolite into heat cure acrylic had a non significant effect on the impact strength, transverse strength, surface hardness, surface roughness and did not change the color, also there was a significant decrease in water sorption and increase in water solubility of acrylic resin. Key words: Denture stomatitis, Antimicrobial agent, Ag- Zn Zeolite.
Browse Iraqi academic journals and research papers
(3)
Low conversion copolymerization of N-vinyl-2-pyrrolidon M.W = (111.14) VP (monomer-1) has been conducted with acrylic acid AA and methymethacrylate MMA in ethanol at 70ºC , using Benzoyl peroxide BPO as initiator . The copolymer composition has been determined by elemental analysis. The monomer reactivity ratios have been calculated by the Kelen-Tudos and Finman-Ross graphical procedures . The derived reactivity ratios (r1 , r2 ) are : (0.51 , 4.85) for (VP / AA ) systems and (0.34 , 7.58) for (VP , MMA) systems , and found the reactivity ratios of the monomer AA , MMA is mor than the monomer VP in the copolymerization of (VP / AA) and (VP /MMA) systems respectly . The reactivity ratios values were used for microstructures calculation.
This research studies the possibility of producing Bone China with available local and geological substitutes and other manufactured ones since it’s traditionally produced by Bone ash, Cornish stone, and China clay, while the substitutes are Kaolin instead of China clay and Feldspar potash instead of Cornish stone. Because of the unavailability of Feldspar in Iraq, it was substituted with the manufactured alternative Feldspar. Bone ash was prepared from cow bones with heating treatments, grinding and sifting. The alternative Feldspar was prepared by chemical analysis of the natural Feldspar potash with local materials that include Dwaikhla Kaolin, Urdhuma Silica sand, Potassium Carbonate, and Sodium Carbonate. The mixture was burned at
... Show More
(40)
(37)
Background: The displacement of artificial teeth during complete denture construction presents major processing errors in the occlusal vertical dimension which were verified at the previous trial denture stage. The aim of this study was to assess the effect of delay in processing after final flask closure and tension application on the vertical acrylic and porcelain teeth displacement of complete dentures constructed from heat cured acrylic and the results were compared with the conventional processing method. Materials and methods: forty samples of identical maxillary complete dentures were constructed from heat polymerized acrylic resin. These samples were subdivided into the following experimental subgroups in which each subgroup contai
... Show More