Background: Poly (methylmethacrylate) is the most widely used material in denture fabrication. The characteristics of acrylic resin which support microorganism development can threaten the oral health of denture users. This study was assigned to prepareand incorporate Ag-Zn zeolite powder into heat cured denture base material as antimicrobial material and to investigate its effect on some properties of heat cured acrylic denture base materials. Materials and methods: Sliver –zinc zeolite was prepared by ion exchange method and characterized then incorporated into poly (methylmethacrylate) powder in0.5% by weight. Specimens were constructed and divided into 6 groups according to the using tests; each group was subdivided into 2 groups. The tests conducted in this study were: impact strength test, transverse strength test, surface hardness test, surface roughness test, water sorption test, water solubility test and color change measurement after addition. The results were statistically analyzed by t-test at p value≤ 0.05. Results: Characterization methods results showed the incorporation of sliver and zinc ion without change of zeolite structure framework. A non-significant effect resulted from the addition of 0.5% sliver –zinc zeolite on the impact strength, transverse strength, surface hardness, surface roughness and cause no change in color of heat cure denture base. Also a highly significant decrease in water sorption and a significant increase of water solubility were observed. Conclusion: Preparation of sliver-zinc zeolite could be performed successfully and the addition of 0.5% of antimicrobial sliver-zinc zeolite into heat cure acrylic had a non significant effect on the impact strength, transverse strength, surface hardness, surface roughness and did not change the color, also there was a significant decrease in water sorption and increase in water solubility of acrylic resin. Key words: Denture stomatitis, Antimicrobial agent, Ag- Zn Zeolite.
This article studied some linear and nonlinear optical characteristics of different pH solutions from anthocyanin dye extract at 180 oC from red cabbage. First, the linear spectral characteristics, including absorption and transmittance in the range 400-800 nm for anthocyanin solution 5% v/v with different pHs, were achieved utilizing a UV/VIS spectrophotometer. The experimental results reveal a shift in the absorption toward the longer wavelength direction as pH values increment. Then, the nonlinear features were measured using the Z-scan technique with a CW 532 nm laser to measure the nonlinear absorption coefficient through an open aperture. A close aperture (diameter 2 mm) calculates the nonlinear refractive index. The open Z-scan sh
... Show More
(7)
(7)
In this research study Hardness (shore D), Water absorption,
Flexural, Impact Test, and Fracture Toughness of polymer nano
composites. The polymer nano composites based on unsaturated
polyester resin reinforced with Kevlar fibers (K.F). The samples are
attended by hand lay – up method according to (Rule mixture) for
various volume fractions of unsaturated polyester resin, fiber and
carbon nanotube. The polyester resin was matrix strengthened with
3% volume fraction from Kevlar fiber and (0.5%, 1%, 1.5%, 2%)
volume fractions of carbon nanotube. The water absorption, hardness
(shore D), flexural test, impact test and toughness fracture properties
were studied. Results showed that the water absorption increas
(1)
The aim of this study is interpretation well logs to determine Petrophysical properties of tertiary reservoir in Khabaz oil field using IP software (V.3.5). The study consisted of seven wells which distributed in Khabaz oilfield. Tertiary reservoir composed from mainly several reservoir units. These units are : Jeribe, Unit (A), Unit (A'), Unit (B), Unit (BE), Unit (E),the Unit (B) considers best reservoir unit because it has good Petrophysical properties (low water saturation and high porous media ) with high existence of hydrocarbon in this unit. Several well logging tools such as Neutron, Density, and Sonic log were used to identify total porosity, secondary porosity, and effective porosity in tertiary reservoir. For
... Show More
(4)
|
Copper oxide thin films were synthesized by using spray pyrolysis deposition technique, in the temperature around 400°C in atmosphere from alcoholic solutions. Copper (II) chloride as precursor and glass as a substrate. The textural and structural properties of the films were characterized by atomic force microscopy (AFM), X-ray diffraction (XRD). The average particle size determined from the AFM images ranged from 30 to 90 nm and the roughness average was equal to 9.3 nm. The XRD patterns revealed the formation of a polycrystalline hexagonal CuO. The absorption and transmission spectrum, band gap, film thickness was investigated. The films were tested as an |
(1)
Rate of penetration plays a vital role in field development process because the drilling operation is expensive and include the cost of equipment and materials used during the penetration of rock and efforts of the crew in order to complete the well without major problems. It’s important to finish the well as soon as possible to reduce the expenditures. So, knowing the rate of penetration in the area that is going to be drilled will help in speculation of the cost and that will lead to optimize drilling outgoings. In this research, an intelligent model was built using artificial intelligence to achieve this goal. The model was built using adaptive neuro fuzzy inference system to predict the rate of penetration in
... Show More
The aim of present work is to improve mechanical and fatigue properties for Aluminum alloy7049 by using Nano composites technique. The ZrO2 with an average grain diameter of 30-40 nm, was selected as Nano particles, to reinforce Aluminum alloy7049 with different percentage as, 2, 4, 6 and 7 %. The Stir casting method was used to fabricate the Nano composites materials due to economical route for improvement and processing of metal matrix composites. The experimental results were shown that the adding of zirconium oxide (ZrO2) as reinforced material leads to improve mechanical properties. The best percentage of improvement of mechanical properties of 7049 AA was with 4% wt. of ZrO2 about (7.76% ) for ultim
... Show More
(3)
The properties of structural and optical of pure and doped nano titanium dioxide (TiO2) films, prepared using chemical spray pyrolysis (CPS) technique, with different nanosize nickel oxide (NiO) concentrations in the range (3-9)wt% have been studied. X-Ray diffraction (XRD) technique where using to analysis the structure properties of the prepared thin films. The results revealed that the structure properties of TiO2 have polycrystalline structure with anatase phase. The parameters, energy gap, extinction coefficient, refractive index, real and imaginary parts were studied using absorbance and transmittance measurements from a computerized ultraviolet visible spectrophotometer (Shimadzu UV-1601 PC) in the wavelength
... Show More
(3)
The aim of this work is to enhance the mechanical properties of the glass ionomer cement GIC (dental materials) by adding Zirconium Oxide ZrO2 in both micro and nano particles. GIC were mixed with (3, 5 and 7) wt% of both ZrO2 micro and nanoparticles separately. Compressive strength (CS), biaxial flexural strength (BFS), Vickers Microhardness (VH) and wear rate losses (WR) were investigated. The maximum compression strength was 122.31 MPa with 5 wt. % ZrO2 micro particle, while 3wt% nanoparticles give highest Microhardness and biaxial flexural strength of 88.8 VHN and 35.79 MPa respectively. The minimum wear rate losses were 3.776µg/m with 7 wt. % ZrO2 nanoparticle. GIC-contai
... Show More
(16)
Abstract Exotoxin A is the most lethal virulence factor produced by Pseudomonas aeruginosa. It inhibits elongation factor-2 by ADP-ribosylation of EF2. This causes stop of the elongation of polypeptides. In recent study, the effect of low concentration of exotoxin A on some important internal organs of mice was studied. Four groups white mice were injected intraperitonialy with pure exotoxin A in the following manner 0.1, 0.2, 0.3, 0.4 ng\ animals. One mouse receives normal saline inrtaperitonialy as a control. After 72 hours the mice were killed and four organs were taken, liver, spleen, lung and heart from each killed mice. Histological sections were made from each organ and stained with hematoxylin and eosin stain then examined under mic
... Show MoreThis paper presents the synthesis and study of some new mixed-ligand complexes containing nicotinamide(C6H7N2O) symbolized (NA) and phenylalanine (C9H11NO2)symbolized (pheH)] with some metal ions. The resulting products were found to be solid crystalline complexes which have been characterized by :Melting points, Solubility, Molar conductivity. determination the percentage of the metal in the complexes by flame(AAS), magnetic susceptipibility, Spectroscopic Method [FT-IR and UV-Vis]. The proposed structure of the complexes using program , chem office 3D(2006) . The general formula have been given for the prepared complexes : [M(NA)2(phe)]cl M(II): Mn(II) ,Co(II) , Ni(II) , Cu(II) , Zn(II) , Cd(II) & Hg(II)). NA = Nicotinamide= C6
... Show More