Background: evaluate the effects of three different intracoronal bleaching agents on the shear bond strengths (SBS) and failure site of stainless steel and monocrystalline (sapphire) orthodontic brackets bonded to endodontically treated teeth using light cured orthodontic adhesive in vitro. Materials and methods: Eighty extracted sound human upper first premolars were selected, endondontically treated and randomly divided equally (according to the type of the brackets used) into two main groups (n = 40 per group). Each main group were subdivided (according to the bleaching agent used) into four subgroups 10 teeth each; as following : control (un bleached) group, hydrogen peroxide group (Hp) 35%, carbamide peroxide group (CP) 37% group and sodium perborate (SP) group . The bleaching process was applied three times (4 days intervals) sequentially and the bleached teeth were stored in artificial saliva four weeks before bonding. Orthodontic brackets were bonded with a light cure composite resin and cured with LED light. After passing 24 hours of bonding procedure, the brackets were debonded by a Tinius-Olsen universal testing machine, to measure the shear bond strength. After debonding, each bracket base and the corresponding tooth surface were examined using a stereomicroscope and their Adhesive Remnant Index (ARI) was recorded. Results: The ANOVA test showed that the SBS of stainless brackets was significantly reduced by intracorornal bleaching agents. Furthermore, LSD showed no significant difference in SBS between the three types of bleaching agents used in stainless steel group. Whilst for sapphire group, the results The ANOVA test showed no significant difference in SBS between the bleached groups and the control group. Chi-square comparison no significant difference in failure site between bleached and control groups in both brackets types used. Conclusion: The effect of intracoronal bleaching on SBS was reduced SBS of stainless steel and not for sapphire. However, the intracoronal bleaching had no effect on the failure site of orthodontic brackets used.
Background: Irrigation of the canal system permits removal of residual tissue in the canal anatomy that cannot be reached by instrumentation of the main canals so the aim of this study was to compare and evaluate the efficiency of conventional irrigation system, endoactivator sonic irrigation system,P5 Newtron Satelec passive ultrasonic irrigation and Endovac irrigation system in removing of dentin debris at three levels of root canals and to compare the percentage of dentin debris among the three levels for each irrigation system. Materials and methods: Forty extracted premolars with approximately straight single root canals were randomly distributed into 4 tested groups of 10 teeth each. All canals were prepared with Protaper Universal ha
... Show MoreAbstract
In the present work, thermal diffusivity and heat capacity measurements have been investigated in temperature range between RT and 1473 K for different duplex stainless steel supplied by Outokumpu Stainless AB, Sweden. The purpose of this study is to get a reliable thermophysical data of these alloys and to study the effect of microstructure on the thermal diffusivity and heat capacity value. Results show the ferrite content in the duplex stainless steel increased with temperature at equilibrium state. On the other hand, ferrite content increased with increasing Cr/Ni ratio and there is no significant effect of ferrite content on the thermal diffusivity value at room temperature. Furthermore, the heat capacity of all sam
... Show MoreBackground: Although bleaching is typically considered a safe procedure, various investigations have found minor negative effects and changes in mineral composition. The aim was to Evaluate and compare the efficacy of using Nanohydroxyapatite serum on surface microhardness of enamel surface before and after bleaching with chemically cured Boost bleaching. Material and methods: ten sound human permanent upper and lower premolar teeth were used and their roots were removed 2 mm apically to the cementoenamel junction, the crowns were sectioned mesiodistally into two halves buccal and lingual/palatal, the buccal surface was further subdivided into two halves. The samples were embeded in an acrylic resin, resulting in 30 specimens divide
... Show More
(1)
(1)
(3)
(5)
(1)
Background: Prophylaxis methods are used to mechanically remove plaque and stain from tooth surfaces; such methods give rise to loss of superficial structure and roughen the surface of composites as a result of their abrasive action. This study was done to assess the effect of three polishing systems on surface texture of new anterior composites after storage in artificial saliva. Materials and methods: A total of 40 Giomer and Tetric®N-Ceram composite discs of 12 mm internal diameter and 3mm height were prepared using a specially designed cylindrical mold and were stored in artificial saliva for one month and then samples were divided into four groups according to surface treatment: Group A (control group):10 specimens received no surfa
... Show MoreBackground: Ceramic veneers represent the treatment of choice in minimally invasive esthetic dentistry; one of the critical factors in their long term success is marginal adaptation. The aim of the present study is to evaluate the marginal gap of ceramic veneers by using two different fabrication techniques and two different designs of preparation. Material and methods: A typodont maxillary central incisor used in the preparation from which metal dies were fabricated, which were in turn used to make forty stone dies. The dies divided into four experimental groups, each group had ten samples: A1: prepared with butt-joint incisal reduction and restored with IPS e.max CAD, A2: prepared with overlapped incisal reduction and restored with IPS e.
... Show MoreGalvanic corrosion of stainless steel 316 (SS316) and carbon steel (CS) coupled in 5% wt/v sulfuric acid solution at agitation velocity was investigated. The galvanic behavior of coupled metals was also studied using zero resistance ammeter (ZRA) method. The effects of agitation velocity, temperature, and time on galvanic corrosion current and loss in weight of both metals in both free corrosion and galvanic corrosion were investigated. The trends of open circuit potential (OCP) of each metal and galvanic potential (Eg) of the couple were, also, determined. Results showed that SS316 was cathodic relative to CS in galvanic couple and its OCP was much more positive than that of CS for all investigated ranges of
... Show More