Background: Dental implants provide a unique treatment modality for the replacement of lost dentition .This is accomplished by the insertion of relatively inert material (a biomaterial) into the soft and hard tissue of the jaws, there by providing support and retention for dental prostheses. Low level laser therapy (LLLT) is an effective tool used to prompt bone repair and modeling post surgery; this has referred to the biostimulation effect of LLLT. The aims of this study were to evaluate the immmunohistochemical expression of vascular endothelial growth factor (VEGF) and transforming growth factor -beta (TGF-β) in experimental and control groups with mechanical test. Materials and Methods: Thirty two adult New Zealand white rabbits used, screw titanium implants inserted in the tibia. The right side is considered as experimental groups and the left side considered as control groups. Low power diode laser (GaAlAs) with wave length (904nm) and (5mW) power applied with the right screw implants. The sample divided into four groups, eight rabbits are sacrificed at four interval 4days, 1 weeks, 2weeks, and 6weeks respectively. immunohistochemical (VEGF&TGF-β), were done for each interval with mechanical test in 2 and 6 weeks . Results: Immunohistochemical findings revealed high positive expression for VEGF and TGF-β in experimental implant in comparison to control one and the acceleration of bone formation and more rapid healing process in the screw implant with laser irradiation than in the control implant. Removal torque test showed dramatic increase with the presence of laser irradiation especially with advancing time. Conclusion: This study was illustrated that the LLLT applications enhance bone formation and increase osseointegration.
The measurement of vitamin B1 in pure and pharmaceutical formulations was proposed by using a straightforward and sensitive spectrophotometric approach. Sulfacetamide (SFA) is diazotized, then coupled with vitamin B1 in alkaline media to produce a colored azo dye complex with a stability constant of 5.597 × 105 L/mol. The product is stable, with a maximum absorption wavelength of 489.5 nm, molar absorptivity of 10108 L/mol∙cm, Sandell's sensitivity of 0.0334 μg/cm2, detection limit of 0.0135 μg/mL, and Beer's law being observed over the concentration range of 0.2–20.0 μg/mL. The stability constant and stoichiometry of the produced azo dye were calculated using the continuous variation (Job's) and mole ratio methods. The suggested ap
... Show More
In the present work, different thicknesses of CdS film were prepared by chemical bath deposition. Z-Scan technique was used to study the nonlinear refractive index and nonlinear absorption coefficients. Linear optical testing were done such as transmission test, and thickness of films were done by the interference fringes (Michelson interferometer). Z-scan experiment was performed at 650nm using CW diode laser and at 532nm wavelength. The results show the effect of self-focusing and defocusing that corresponds with nonlinear refraction n2. The effect of two-photon absorption was also studied, which correspond to the nonlinear absorption coefficient B.
The influence of sintering and annealing temperatures on the structural, surface morphology, and optical properties of Ag2Cu2O4 thin films which deposited on glass substrates by pulsed laser deposition method have been studied. Ag2Cu2O4 powders have polycrystalline structure, and the Ag2Cu2O4 phase was appear as low intensity peak at 35.57o which correspond the reflection from (110) plane. Scan electron microscopy images of Ag2Cu2O4 powder has been showed agglomerate of oxide particles with platelets shape. The structure of thin films has been improved with annealing temperature. Atomic Force micrographs of Ag2Cu2O4 films showed uniform, homogenous films and the shape of grains was almost spherical and larger grain size of 97.85 nm has o
... Show More
Laser etching may be an alternative to acid etching of enamel and dentin. Several characteristics of irradiated dental hard tissues have been considered advantageous, microscopically rough surfaces without demineralization, open dentinal tubules without smear layer production and dentin surface sterilization. The aim of this study is to determine and compare histology the microleakage in class V cavity restored with a light cured composite after conditioning the samples(tooth surface) with 1-acid etching, 2-Q-switched Nd:YAG Laser etching and finally 3- acid and laser etching. Materials and methods: Twenty four non carious human extracted teeth were used in this study. The samples were equally grouped into four groups of six teeth each.
... Show MoreAims: To assess the success rate and implant stability changes of narrow dental implants (NDIs) during the osseous healing period. Materials and methods: This prospective observational clinical study included 21 patients with narrow alveolar ridge of restricted mesiodistal interdental span who received NDIs. The alveolar ridge width was determined by the ridge mapping technique. Implant stability was measured using Periotest® M immediately after implant insertion then after 4 weeks, 8 weeks and 12 weeks postoperatively. The outcome variables were success rate and implant stability changes during the healing period. The statistical analysis included one-way analysis of variance (ANOVA) and Tukey\'s multiple comparisons test, values < 0.05 w
... Show More
(2)
Advancements in horizontal drilling technologies are utilized to develop unconventional resources, where reservoir temperatures and pressures are very high. However, the flocculation of bentonite in traditional fluids at high temperature and high pressure (HTHP) environments can lower cuttings transportation efficiency and even result in problems such as stuck pipe, decreased rate of penetration (ROP), accelerated bit wear, high torque, and drag on the drill string, and formation damage. The major purpose of the present research is to investigate the performance of low bentonite content water-based fluids for the hole cleaning operation in horizontal drilling processes. Low bentonite content water-based drilling fluids were formulated by re
... Show More
(7)
(4)
(1)
The electrical properties of pure NiO and NiO:Au Films which are
deposited on glass substrate with various dopant concentrations
(1wt.%, 2wt%, 3wt.% and 4wt.%) at room temperature 450 Co
annealing temperature will be presented. The results of the hall effect
showed that all the films were p-type. The Hall mobility decreases
while both carrier concentration and conductivity increases with the
increasing of annealing temperatures and doping percentage, Thus,
indicating the behavior of semiconductor, and also the D.C
conductivity from which the activation energy decrease with the
doping concentration increase and transport mechanism of the charge
carriers can be estimated.