Background: The bond strength of root canal sealers to dentin was important for maintaining the integrity of the seal in root canal filling in both static and dynamic situations. In a static situation, it should eliminate any space that allowed the percolation of fluids between the filling and the wall while in a dynamic situation; it was needed to resist dislodgement of the filling during subsequent manipulation. Materials and Methods: Forty mandibular premolars were selected for this study. All canals were instrumented using ProTaper rotary instruments. Instrumentation was done with copious irrigation of 5.25% sodium hypochlorite. Roots were randomly divided into four groups according to the type of cleaning and method of root canal irrigation (ten teeth for each group): Group A. The root canals were irrigated with 5 ml of 17% of EDTA for 1 minute and 5 ml of 5.25% NaOCl. Group B. Cleaning with waterlase laser. Group C. The root canals were irrigated with 5 ml of 5mg/ml of siwak (Salvadora persica) extract for one minute. Group D. The root canals were irrigated with 5 ml of 5% of green tea (camellia sinensis) extract for one minute. All groups were rinsed with distilled water and then obturated with cold lateral condensation technique and i Root sp sealer (Bioceramic sealer, the roots then stored in moist environment at 37°C for one week. Three horizontal sections were prepared at a thickness of 1 mm ±0.1 in the apical, middle and coronal parts of each root. The test specimens were subjected to the push-out test method using a Universal Test Machine that carried 1-mm, 0.5- mm and 0.3-mm plungers for coronal, middle and apical specimens, respectively. The loading speed was 0.5 mm/ min. The computer showed the higher bond force before dislodgment of the filling material. These forces were divided by the surface area to obtain the bond strength in MPa. Results: In all groups the mean value of push-out strength was greatest in apical area and least in coronal area and the middle area was in between, except in Waterlase the middle area showed the least mean push-out strength. Conclusion: Herbal extracts used in this study (Siwak and green tea) can be used safely as an intra-canal irrigant for smear layer removal with efficiency that is comparable with conventional synthetic materials (EDTA) and more complicated methods (Waterlase).
The present work aimed to study effect of (N749 & N3) dyes on TiO2 optical and electrical properties for optoelectronic application. The TiO2 paste prepared by using a doctor blade method. The samples were UV-VIS specterophometricall analyzes of TiO2 before and after immersed in dyes (N749 & N3). The results showed absorption spectra shift toward the visible region due to the adsorption of dye molecules on the surface of oxide nanoparticles. It is seen that the Eg determined to give a value of 3.3eV for TiO2 before immersing in dyes, and immersing in dyes (N749 & N3) are (1.4 &1.6 eV) respectively. The structural properties (XRD), (FTIR) and (SEM) for the sample prepared were investigated and (J-V) characteristics was stu
... Show More
Objective: This study aimed to evaluate the effect of coating titanium (Ti) dental implant with polyether ketone ketone (PEKK) polymer using magnetron sputtering on osseointegration, trying to overcome some of the problems associated with Ti alloys. Material and Methods: Implants were prepared from grade (II) commercially pure titanium (CP Ti), then laser was used to induce roughness on the surface of Ti. PEKK was deposited on the surface of Ti implants by radiofrequency (RF) magnetron sputtering technique. The implants were divided in to three groups: without coating (Ls), with PEKK coating using argon (Ar) as sputtering gas (Ls-PEKK-Ar), and with PEKK coating using nitrogen (N) as sputtering gas (Ls-PEKK-N). All the implants were implante
... Show More
(2)
Aim: The Aim of the study is to compare between Er,Cr:YSGG 2780 nm laser and carbide fissure bur in root-end resection regarding the morphological variations, temperature changes and the duration of resection process.
Settings and Design: 5 W, 25 Hz, 50% water, 80% air,25.47 J/cm2 .
Material and method: twenty-one extracted single rooted teeth endodontically were treated, twenty teeth were obturated and divided into two groups according to method of resection. Group 1 root-end resected using cross cut carbide bur while group 2 root-end resected using laser with MGG6 sapphire tip of 600 μm diameter. Temperature on external root surface and duration of resection were recor
... Show More
(1)
(1)
(18)
(15)
This work aimed to study the effect of laser surface treatment on the mechanical characteristics and corrosion behaviour of grey cast iron type A159. Many technical applications used conventional surface treatment, but laser surface hardening has recently been used to enhance the surface properties of many alloys. The mechanical characteristics, including microstructure, microhardness, and wear resistance of A159 grey cast iron, were studied, in addition to corrosion behaviour. The experimental laser parameters in this work were 0.9, 1.2, and 1.5 KW power with continuous wave carbon dioxide lasers with scanning speeds of 10 and 12 mm/s were used. The results found that phase-transitional alterations in microstructure were influenced by lase
... Show More
(2)
Laser etching may be an alternative to acid etching of enamel and dentin. Several characteristics of irradiated dental hard tissues have been considered advantageous, microscopically rough surfaces without demineralization, open dentinal tubules without smear layer production and dentin surface sterilization. The aim of this study is to determine and compare histology the microleakage in class V cavity restored with a light cured composite after conditioning the samples(tooth surface) with 1-acid etching, 2-Q-switched Nd:YAG Laser etching and finally 3- acid and laser etching. Materials and methods: Twenty four non carious human extracted teeth were used in this study. The samples were equally grouped into four groups of six teeth each.
... Show More