Objective: To enhance bonding strength between thermoplastic denture base and acrylic soft liner through ethyl acetate surface treatment. Materials and Methods: Modifications of thermoplastic acrylic denture base surface were investigated with SEM. FTIR was used to detect whether there was a chemical bond between thermoplastic acrylic and the organic solvent. A total of 80 samples were prepared and divided into 20 samples for the surface roughness test and 60 samples for the shear bond strength test. Failure type was assessed visually. Results: Shear bond strength and surface roughness values of un treated samples were lower in comparison to surface treated groups; the greatest post thermocycling bond strength value was recorded for the sam

Nanoparticles (NPs) based techniques have shown great promises in all fields of science and industry. Nanofluid-flooding, as a replacement for water-flooding, has been suggested as an applicable application for enhanced oil recovery (EOR). The subsequent presence of these NPs and its potential aggregations in the porous media; however, can dramatically intensify the complexity of subsequent CO2 storage projects in the depleted hydrocarbon reservoir. Typically, CO2 from major emitters is injected into the low-productivity oil reservoir for storage and incremental oil recovery, as the last EOR stage. In this work, An extensive serious of experiments have been conducted using a high-pressure temperature vessel to apply a wide range of CO2-pres

Background: Head and neck squamous cell carcinoma is the sixth most common cancer world wide. Despite greater emphasis on multi-modality therapy including surgery, radiation and chemotherapy, advanced stage head and neck squamous cell carcinoma continues to have poor 5-year survival rates (0-40%) that have not significantly improved in the last (30) years. To improve outcomes for this deadly disease , It is required a better understanding of the mechanisms underlying head and neck squamous cell carcinoma tumor growth, metastasis, and treatment resistance. This study evaluates the Immunohistochemical expression of E-cadherin and CD44 adhesion molecules in OSCC and to correlate the expression of either marker with each other, with lymph node

ABSTRACT : Fifteenth isolates of C. sakazakii were obtained from previous studies of the sample (infant formula, cerebrospinal fluid and blood). All isolates C. sakazakii identification based on microscopic, biochemical test and confirmed by 16SrRNA. We studied the movement of all isolates and study adhesion to polystyrene plate, adhesion and invasion to Esophageal adenocarcinoma (SKG-GT-4) for four isolates [Cerebrospinal fluid (CSF5), Bloods (B 1), Dialak (A1c), Novolac Allernova (C1)] and its cytotoxicity. Results showed that all isolates can move after 4 hours of incubation and increased after 8 hours, the isolates moved to different distances strong, medium, and weak. The results showed that the number of C. sakazakii colony adherent t

Background: 37% phosphoric acid (PA) is the traditional enamel etching technique prior to bracket ‎adhesion, yet it has been implicated in numerous enamel injuries. The purpose of the current study was to create a calcium phosphate (CaP) etching paste in a ‎‎simplified capsule ‎formula that can underpin clinically ‎adequate bracket bond strength ‎without jeopardizing the ‎integrity of enamel upon ‎the debracketing procedure. Materials and Methods: micro-sized hydroxyapatite (HA) powder was mixed with 40% PA solution to prepare ‎experimental acidic CaP paste. Sixty human premolars were ‎assigned into two groups of 30 each. ‎Enamel conditioning was accomplished using 37% PA-gel‎ for control group and CaP paste for e

This paper displays the effect of uncoated and coated chopped carbon fibers with alumina Al₂O₃ or Tri calcium phosphate (TCP) on the impact strength of acrylic poly methyl methacrylate (PMMA) denture base resin. To improve bonding between carbon fibers and coating materials powders, the surface of carbon fibers has been treated with Para amino benzoic acid (C₉H₁₀N₂O₃) and poly vinyl alcohol (PVA) was also used. The morphology of the coating layers has been examined by field emission scanning electron microscope (FE-SEM). From the results, PMMA reinforced with uncoated chopped carbon fiber has high impact strength value but still have bad aesthetic.  Samples prepared b

Ceramic coating compose from a ceramic mixture (MgO, Al₂O₃) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al₂O₃ and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character

in this worl three types of complexed phenolic resins were prepared using various additives such as and improving the aim of this work higher mechanical properties this work is done

Green biosynthesized selenium nanoparticles from Ralstonia insidiosa show potent activity against multidrug-resistant Acinetobacter baumannii , pathogenic Candida spp. and human prostate cancer cells.