A new tool geometry was used to achieve friction stir spot welding (FSSW) in which the shoulder was designed separately from the rotating pin, and in order to examine weldment strength through the modified tool, a lap joints of AA2024 aluminum alloy plate 1 mm thick were welded successfully by using 6 mm pin diameter and varying process parameters (rotational speeds, tool nose geometry, and depth of tool penetration in the lower welded plate). Experimental tests indicate that the maximum average tensile shear load was 3100 N at the best selected condition. Microstructure examination and micro hardness test along the spot zones were investigated as well as measuring pin penetration load. Visual inspection of the welded spot surface shows a g

Titanium dioxide nanorods have been prepared by sol-gel template
method. The structural and surface morphology of the TiO₂ nanorods was
investigated by X-ray diffraction (XRD) and atomic force microscopy
(AFM), it was found that the nanorods produced were anatase TiO₂ phase.
The photocatalytic activity of the TiO2 nanorods was evaluated by the
photo degradation of methyl orange (MO). The relatively higher
degradation efficiency for MO (D%=78.2) was obtained after 6h of exposed
to UV irradiation.

Cu-Al-Ni shape memory alloy specimens has been fabricated using powder metallurgy technique with tube furnace and vacuum sintering environment , three range of Nb powder weight percentage (0.3,0.6,0.9)% has been added. Micro hardness and sliding wear resist has been tested followed by X-ray diffraction, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDX) for micro structure observation. The experimental test for the samples has showed that the increase of Nb powder weight percentage in the master alloy has a significant effect on increasing the hardness and decreasing the wear resist therefore it will enhance the mechanical properties for this alloy.

Chronic myeloid leukemia (CML) is a myeloproliferative disorder characterized by the presence Philadelphia chromosome (Ph) which was created by a reciprocal translocation between chromosomes 9 and 22 (t [9;22] [q34;q11]. The approval of the 2nd generation TKI ( Nilotinib) takes the treatment of CML patients into new erea with more efficiency and mild to moderate adverse effects. This study was aimed at evaluation of molecular cytogenetic response by (FISH) for Nilotinib in Iraqi patients with assessment for electrolytes disturbances of Nilotinb by measuring a panel of electrolyte (Na+, K+, Ca++, PO4--- and Mg++) , where thirty Iraqi patients with CML who have resistance or no response to Imatinib treatment, attending to Baghdad Teaching Ho

In this article the conventional "solid-state reaction" method was used to synthesize perovskite Li_0.4Cd_0.6Ba₂Ca₂Cu₃O_10+δ. Four main types of compounds were obtained by physically replacing calcium oxide with cadmium in proportions 0, 0.03, 0.06 and 0.09, the pure Li_0.4Cd_0.6Ba₂Ca₂Cu₃O_10+δ phase, and the phases Li_0.4Cd_0.6Ba₂Ca_1.97Cd_0.03Cu₃O_10+δ

Nutrient agar medium with various concentrations of cefotaxime was used for isolation spontaneous mutants from wild type strain of P.aeruginosa PHA-1. Eighty-two mutants were successfully isolated with the viable count 52×107 , these mutants were confirmed as spontaneous not physiological adaption mutants by reculture on the same medium. Then, wild type PHA-1 and mutants were examined for production pyocyanin; a blue greenish pigment was clearly noticed on King A medium. Remarkably the mutant strain named S300-8 was distinguished in productivity in comparison with wild type strain PHA-1; the amount of pigment was 56.0667mg/l and 74.53mg/l respectively. In addition, pyocyanin produced by mutant strain S300-8 revealed a potent efficacy again

The effect of approaching nozzle jet from the deposition surface
on structural, optical and morphology properties of copper oxide thin
films was studied. The film was prepared by homemade fully
computerized CNC spray pyrolysis deposition technique at
preparations speed (3, 4, 5, and 6 mm/sec). The repeated line mode
was used at deposition temperature equal 450 °C whereas the
spraying time was in the range of (15-30 min) according to the
deposition speed. The film exhibit polycrystalline structure with
preferred orientation along (-111), (022) and (011), (002) at a 2θ
value of (35.63o) and (38.8o) respectively. Optical band gaps were
recorded at these speed shows variance in value from (1.53-2.08 eV).
Fi

The study of determing Uranium concentration in samples of teeth is the first of its kind in the Iraq . In this study Uranium concentration has been measured was (32) samples of child teeth distributed on the some of middle and south governorate of Iraq (Muthana – Dekar – Basrah – Najaf – Karbalah – Waset – Babel – Baghdad) . The Uranium concentration in teeth samples has been measured by using fission tracks registration in (CR-39) track detector that caused by the bombardment of (U235) with thermal neutrons falx from (24Am.Be) neutron source that has flux of (5x103n.cm-2S-1). The result obtained show that the Uranium concentrations in governorates were (0.18ppm), (0.172ppm), (0.160ppm), 0.150ppm) (0.89ppm), (0.07ppm) , (0.

The aim of present study is to determine the optimum parameters of friction stir welding process and known the most important parameter along with percentage contribution of each parameter which effect on tensile strength and joint efficiency of FS welded joint of  dissimilar aluminum alloys AA2024-T3 and AA7075-T73 of 3 mm thick plates by applied specific number of experiments using Taguchi method .AA2024 was placed on the advancing side and AA7075 on the retreating side. FSW was achieved under three different rotation speeds (898, 1200 and 1710) rpm, three different welding speeds (20, 45 and 69) mm\min , three different pin profiles (cylindrical, threaded cylindrical and cone) and tool tilt angle 2^◦. Taguchi method w

The removal of congo red (CR) is a critical issue in contemporary textile industry wastewater treatment. The current study introduces a combined electrochemical process of electrocoagulation (EC) and electro-oxidation (EO) to address the elimination of this dye. Moreover, it discusses the formation of a triple composite of Co, Mn, and Ni oxides by depositing fixed salt ratios (1:1:1) of these oxides in an electrolysis cell at a constant current density of 25 mA/cm2. The deposition ended within 3 hours at room temperature. X-ray diffractometer (XRD), field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM), and energy dispersive X-ray (EDX) characterized the structural and surface morphology of the multi-oxide sedim