Background: The PMMA polymer denture base materials are low in thermal and strength properties. The aim of the study was to investigate the change in glass transition temperature, E-Moudulus and coefficient of thermal expansion of acrylic denture base material by addition of Al2O3, TiO2 and SiO2nano-fillers in 5% by weight. Materials and methods: The type of polymerization is free radical bulk polymerization. one hundred twenty (120) specimens were prepared , the specimens were divided into four groups according to the material had been added (one control and three for Al2O3, TiO2 and SiO2nanocomposite) each group was subdivided in to three groups according to the test had been done on it, the degree of transition (Tg) was measured by The differential scanning calorimeter (DSC), E-Modulus and coefficient of thermal expansion and contraction was measured by Thermo Mechanical Analyzer (TMA) .Each sample was tested at different temperatures (30,40,50,60,70C°). Results: Highly significant decrease in coefficient thermal expansion and contraction and in E-Modulus occurred in acrylic incorporated with Al2O3, TiO2 and SiO2 nano-fillers in 5% by weight when compared to control group. For glass transition temperature a significant increase had occurred with the addition of nanofillers at 5% when compared to control group. Conclusion: The results showed that the polymer nanocomposites possess material properties different from that of unmodified PMMA, nanocomposite has thermal and mechanical stability more than heat neat PMMA.
Polyvinal alcohol was Cynoethylated , complex compound with Iodin in presence of Cu++ ions were preparated and their ultra violet (U.V) and infra red( IR) spectra were investigated. The prepared derivative and complexes were evaluated as antibacterial and antifungal agents following the standard dilution method. MIC(minimum inhibitory concentration) for each polymer using ten types of gram + ve and gram _ ve bacteria were determinated in addition to three types of fungi. The results obtainded showed that MIC, s were around 0.0011 × 103 molar for different polymetric derivatives tried.
This review article summarizes our research focused on Cu(In, Ga)Se2 (CIGS) nanocrystals, including their synthesis and implementation as the active light absorbing material in photovoltaic devices (PVs). CIGS thin films were prepared by arrested precipitation from molecular precursors consisting of CuCl, InCl3, GaCl3 and Se metal onto Mo/soda-lime glass (SLG) substrates. We have sought to use CIGS nanocrystals synthesized with the desired stoichiometry to deposit PV device layers without high temperature processing. This approach, using spray deposition of the CIGS light absorber layers, without high temperature selenization, has enabled up to 1.5 % power conversion efficiency under AM 1.5 solar illumination. The composition and morphology
... Show MoreA laboratory experiment has been carried out in the College of Science-University of Salahaddin to study the effect of different levels (0,5,10 and 15%) and sizes(250 and 1000µm) of walnut seeds residues and (160mg.kg-1) phosphorus fertilization on the concentration of phosphorus availability and alkaline phosphatase activity in calcareous soil during 15 and 30 days period of incubation, the experimental design in factorial complet randomize design (C.R.D) with three replications. The results indicated that the application of different levels of walnut seed residues decreases the concentration of phosphorus availability and alkaline phosphatase activity, however the results revealed that combination between levels and sizes o
... Show More
(1)
Background: All diseases concerning bone destruction such as osteoporosis and periodontal diseases share common pattern in which the osteoclast cells are absolutely responsible for bone resorption that occurred when osteoclast activity exceeds osteoblast activity. Osteoprotegrin (OPG) considered as novel soluble decoy receptor known as “bone protector†since it prevents extreme bone resorption through inhibition of differentiation and activity of osteoclast by competing for binding site. It binds to receptor activator of nuclear factor kappa-B ligand (RANKL) and prevent its interaction with receptor activator of nuclear factor kappa-B (RANK), thus inhibits osteoclast formation. TNF-α is a pro-inflammatory cytokines having
... Show More
This work investigates generating of pure phase Faujasite-type zeolite Y at the ranges chosen for this study via a static aging step in the absence of seeds synthesis. Nano-sized crystals may result when LUDOX AS-40 is used as a silica source for gel composition of range 6 and the crystallization step may be conducted for a period of 4 to 19 hr at 100 ⁰C. Moreover, large-crystals with high crystallinity pure phase Y zeolite can be obtained at hereinabove conditions but when hydrous sodium metasilicate is used as a silica source. The other selected ranges also offer pure phase Y zeolite at the same controlled conditions.
(15)