Background: Denture fracture is one of the most common problems encountered by the patients and prosthodontists. The objective of present study was to evaluate the transverse strength of nylon denture base resin repaired by using conventional heat polymerized, autopolymerized and visible light cure {VLC} resins, surface treatment that used for repair and adjustment of insufficient nylon denture bases and in case of addition of artificial teeth. As these corrective procedures are common chair side procedures in dental clinic. Materials and methods: One hundred twenty nylon specimens were prepared by using metal patterns with dimension of (65x10x2.5 mm) length, width, and thickness respectively for transverse strength test while for tensile bond strength a dumbbell-shaped with measurement (65x12.5x25mm) length, width, and thickness respectively were flasked with stone. The nylon specimens were molded by reflasked with dental stone that used as an index for these specimens in the repair procedure and repaired with 45 degree bevel joint by using metal holding device. The two parts of nylon specimen to be repaired were realigned in its repair index and adhere with special adhesive material to stabilize the combination during repair procedure. The dough of heat and cold cure resin was packed into the joint and then cured. The specimen repaired with cold cure resin was placed in the Ivomat containing water at (40°C) and pressure (30IB/inch²) for 15 minutes. The specimen repaired with {VLC} was placed in the light cure unit for 4 minutes following manufacturer’s instruction. The fractured nylon specimens were divided according to the type of repaired materials into (40) specimens received heat cure acrylic and the (40) specimens received cold cure acrylic and the other 40 specimens received {VLCR}. Each 40 specimens were subdivided according to the type of surface treatment received into 20 specimens were treated with coarse stone bur (control), 20 specimens were treated with combination of coarse stone bur and monomer of the heat cure acrylic. After that the specimens were subjected to transverse {Tr} and tensile bond {TB} strength tests. For each test 10 specimens. Results and conclusions: This study showed that specimens treated with combination of coarse stone bur and monomer of the acrylic (heat, cold or VL cure) had the highest transverse and tensile strength values, followed by the specimens treated with coarse stone bur. The results showed that the specimens repaired with heat cure acrylic had transverse and tensile strength values higher than the specimens repaired with cold and VL cure acrylic when compared between subgroups of heat, cold and VL cure acrylic that received the same treatments.
(8)
(3)
This paper presents a sight about the chemical structure deformation of poly (ethylene-co-vinyl acetate) (EVA) samples according to the change ratio of rate constant values. Spectroscopy kinetics fluorescence curves are fitted for two characteristic wavelength domains of fluorescent intensities. The short wavelengths (320-400 nm) domain show spectra overlapping, while at long wavelengths (400-800 nm) domain spectra are arranged in regular for each specific accelerated aging time. The ratio of kinetics rate constant at long wavelengths to kinetics rate constant of short wavelengths is the criterion of the degree chemical structure deformation. Molar extrin
... Show More
(13)
(11)
In this work, we have investigated optical properties of the thermally evaporation PbS/CdS thin films. The optical constant such as (refractive index n, dielectric constant εi,r and Extinction coefficient κ) of the deposition films were obtained from the analysis of the experimental recorded transmittance spectral data. The optical band gap of PbS/CdS films is calculate from (αhυ)1/2 vs. photon energy curve.
Abstract The surface of kaolin was diagnosed by an AFM and the results were shown The height of the highest peak reached by a quantity of Kaolin surface is 2.5 µm, the granules, and their diameter with an average diameter of 666.1nm. Using Kaolin's adsorption properties, erythrosine was removed of its aqueous solution. It was determined that the maximal dye adsorption ranged 36.53–40.61%. The results of using the Freundlich, Langmuir, and Temkin adsorption isotherms revealed that at temperatures of (298,308,318) K, the Freundlich model was followed, the Langmuir model did not match, and the Temkin model could only be partially applied. There is also physical adsorption. One of the three kinetic models of the
... Show More
We report here the observation of 16 µm superradiance laser action generated from optical pumping of CF4 gas molecules (which is cooled to 140 Kº by a boil-off liquid-N2) by a TEA-CO2 laser 9R12 line. Output laser pulses of 7 mJ and 200 ns have been obtained.
In this study, a Hydroxyapatite (HA) coating was prepared on a titanium implant by an electrochemical deposition process. The titanium pre-treatment by anodizing in 1.65 mol/L sulfuric acid with (10V) at room temperature. The deposition was all conducted at a constant voltage of 6.0 V, for 1 h at room temperature. The coatings thus prepared were characterized with Fourier transform infrared spectroscopy (FTIR) and thickness of the coated layer.The electrochemical deposition of HA occurred on the titanium as a cathode. Coated titanium by HA after anodizing revealed a good corrosion protection efficiency even at a temperature ranged (293-323) K in artificial saliva. Activation energy and pre-exponential factor (kinetic parameters) were calcul
... Show More
(14)
Investigation of the adsorption of Chromium (VI) on Fe3O4 is carried out using batch scale experiments according to statistical design using a software program minitab17 (Box-Behnken design). Experiments were carried out as per Box-Behnken design with four input parameters such as pH (2-8), initial concentration (50–150mg/L), adsorbent dosage (0.05–0.3 g) and time of adsorption (10–60min). The better conditions were showed at pH: 2; contact time: 60 min; chromium concentration: 50 mg/L and magnetite dosage: 0.3 g for maximum Chromium (VI) removal of (98.95%) with an error of 1.08%. The three models (Freundlich, Langmuir, and Temkin) were fitted to experimental data, Langmuir isotherm has bette
... Show MoreIn this paper, a construction microwave induced plasma jet(MIPJ) system was used to produce a non-thermal plasma jet at atmospheric pressure, at standard frequency of 2.45 GHz and microwave power of 800 W. The working gas Argon (Ar) was supplied to flow through the torch with adjustable flow rate using flow meter regulator. The influence of the MIPJ parameters such as applied voltage and argon gas flow rate on macroscopic microwave plasma parameters were studied. The macroscopic parameters results show increasing of microwave plasma jet length with increasing of applied voltage, argon gas flow rate where the plasma jet length exceed 12 cm as maximum value. While the increasing of argon gas flow rate will cause increasing into the ar
... Show More
(16)
(5)
The hydraulic conditions of a flow previously proved to be changed when placing large-scale geometric roughness elements on the bed of an open channel. These elements impose more resistance to the flow. The geometry of the roughness elements, the numbers used, and the configuration are parameters that can affect the hydraulic flow characteristics. The target is to use inclined block elements to control the salt wedge propagation pointed in most estuaries to prevent its negative effects. The Computational Fluid Dynamics CFD Software was used to simulate the two-phase flow in an estuary model. In this model, the used block elements are 2 cm by 3 cm cross-sections with an inclined face in the flow direction, with a length
... Show More
(1)
(2)