This paper investigates the experimental response of composite reinforced concrete with GFRP and steel I-sections under limited cycles of repeated load. The practical work included testing four beams. A reference beam, two composite beams with pultruded GFRP I-sections, and a composite beam with a steel I-beam were subjected to repeated loading. The repeated loading test started by loading gradually up to a maximum of 75% of the ultimate static failure load for five loading and unloading cycles. After that, the specimens were reloaded gradually until failure. All test specimens were tested under a three-point load. Experimental results showed that the ductility index increased for the composite beams relative to the reference specim

This paper investigates the experimental response of composite reinforced concrete with GFRP and steel I-sections under limited cycles of repeated load. The practical work included testing four beams. A reference beam, two composite beams with pultruded GFRP I-sections, and a composite beam with a steel I-beam were subjected to repeated loading. The repeated loading test started by loading gradually up to a maximum of 75% of the ultimate static failure load for five loading and unloading cycles. After that, the specimens were reloaded gradually until failure. All test specimens were tested under a three-point load. Experimental results showed that the ductility index increased for the composite beams relative to the refe

Glass Fiber Reinforced Polymer (GFRP) beams have gained attention due to their promising mechanical properties and potential for structural applications. Combining GFRP core and encasing materials creates a composite beam with superior mechanical properties. This paper describes the testing encased GFRP beams as composite Reinforced Concrete (RC) beams under low-velocity impact load. Theoretical analysis was used with practical results to simulate the tested beams' behavior and predict the generated energies during the impact loading. The impact response was investigated using repeated drops of 42.5 kg falling mass from various heights. An analysis was performed using accelerometer readings to calculate the generalized inertial load

Background: The aim of the study was to evaluate the amount of changes in the horizontal and vertical maxillary arch dimensions measurements following the premature loss of primary molars. Materials and methods: The sample consist of (50) children with unilateral prematurely extracted either first or second primary molars at the mixed dentition stage. Results and Conclusions: Results shows that there was an increase in the vertical incisor to canine distance (A) with both premature loss of first & second primary molars due to distal movement of primary canines and at the same time there were a significant loss of space in the extraction space with premature loss of second primary molar due to a mesial movement of maxillary first permanent

Many extracted material were used as mouthwash to settle different kinds of oral fungi and bacteria. In this study an extractive of Cyperus rotundus plant E.C.R. which is very active as a mouthwash, was used in concentration range (10-25) ppm in artificial saliva at pH=6.4 and temperature range (288-318) K, to study it’s inhibitory effect on the corrosion of dental amalgam. Potentiostatic and cyclic polarization were used to follow this study. The presence of E.C.R. lead to shift the corrosion potential to the active direction and decreased the corrosion rate to about 98.87%, the inhibition action of E.C.R. resulting from the adsorption of C.R.E. layer between amalgam and saliva as FTIR spectrums shows, where the variety of FTIR adsorptio

A precise evaluation of caries excavation endpoint is essential in clinical and laboratory investigations. Caries invasion differentiates dentin into structurally altered layers. This study assessed these changes using Raman spectroscopy and Vickers microhardness. Ten permanent molars with occlusal and proximal carious lesions were assessed and compared at 130 points utilizing four Raman spectroscopic peaks: phosphate v1 at 960 cm−1, amide I (1650 cm−1), amide III (1235 cm−1) and the C-H bond of the pyrrolidine ring (1450 cm−1). The phosphate-to-amide I peak ratio and collagen integrity peak ratio (amide III: C-H bond) of carious zones were calculated and compared in both lesions. The former ratio was correlated to 130 Vicke

ABSTRACT Background: This study aimed to study the effect of some acidic drinks (Vinegars and fresh Orange juice) and energy drinks (Red bull) on surface roughness of three types of bulkfill composite materials: Filtek posterior bulkfill (3M), Sonicfill (Kerr) and Filtek p60 (3M). Materials and Methods: Total number of 120 samples are prepared by using a mold of (12mm diameter and 3mm height), which were divided into three groups forty samples for each group: Group A: Filtek bulkfill posterior composite (3M), Group B: Sonicfill composite (Kerr), Group C: Filtek P60 (3 M) which then divided into four sub- groups (n=10) (1) samples were kept in distilled water as a control group (2) samples were immersed in Redbull (3) samples were immersed

To detect the amount of rifampicin in bulk and medicinal dosage formulations, an accurate and costeffective UV spectrophotometric technique has been developed using the area under the peak to estimate the presence of rifampicin. This range of wavelengths (300–356 nm) was chosen. The method showed linearity in the 2–22 μg/mL range, with R2 being2 0.9996. The developed method’s linearity, detection limit, quantification limit, precision, repeatability, and accuracy were all statistically and experimentally validated. The suggested methodology can be used for routine quality control analysis of rifampicin in pure form and in capsule dosage form, as demonstrated by the satisfactory recovery percentage results. This study explores the str

To detect the amount of Rifampicin in bulk and medicinal dosage formulations, an accurate, and cost-effective UV spectrophotometric technique has been developed using the area under the peak to estimate the presence of Rifampicin. This range of wavelengths (300–356) nm was chosen. The method showed linearity in the 2-22 μg/mL range, with R2 being 0.9996. The developed method' linearity, detection limit, quantification limit, precision, repeatability, and accuracy were all statistically and experimentally validated. The suggested methodology can be used for routine quality control analysis of Rifampicin in pure form and in capsule dosage form, as demonstrated by the satisfactory recovery percentage results. This study explores the struct