In the present work, silver nanoparticles were prepared. Nonlinear optical properties and
optical limiting of silver nanoparticles were investigated.Standard chemical synthesis method was used at
diffrent weight ratio(0.038, 0.058 and 0.078) of silver nitrate. Several testing were done to obtain the
characteristics of the sample. Z-Scan experiments were performed using 30 ns Q-switched Nd:YAG
laser at 1064 nm and 532 nm at different intensities. The results showed that the nonlinear refractive
index is directly proportional to the input intensities, which caused by the self-focusing of the material.
In addition, the optical limiting behavior has been studied. The results showed that the sample could be
used as an opt

Furfural is a toxic aromatic aldehyde that can cause a severe environmental problem especially the wastewater drown from petroleum refinery units. In the present work, a useless by-product from local furniture manufacturing industry; sawdust was used as raw material for the preparation of activated carbon which is chemically activated with phosphoric acid. The effect of adsorption variables which include initial pH of solution (2-9), agitation speed (50-250) rpm, agitation time (15-120) min, initial concentration of furfural (50-250) ppm, and amount of adsorbent material (0.5-2.5) g for the three adsorbents used (prepared activated carbon, commercial activated carbon and raw sawdust) were investigated in a batch process

Background: The insertion torque (IT) values and implant stability quotient (ISQ) values are the measurements most used to assess primary implant stability. This study aimed to assess the relationship between ISQ values and IT. Materials and methods: This study included 24 patients with a mean (SD) age of 47.9 (13.64) years (range 25-75 years). The patients received 42 dental implants (DI), 33 in the mandible and 9 in the maxilla. The DI were installed using the motorized method with 35 Ncm torque, When DI could not be inserted to the requisite depth by the motorized method, a hand ratchet was used and the IT was recorded as ˃ 35 Ncm. Implant stability was measured utilizing Osstell® ISQ. The secondary stability was measured after 16

Abstract: Recombinant human bone morphogenetic protein-2 (rhBMP-2) and platelet-rich fibrin (PRF) bioactive materials have been used to enhance healing and improve dental implant stability. This study aimed to compare the effect of rhBMP-2 and PRF bioactive materials on dental implant stability at different intervals and to evaluate the correlation of implant length and diameter with implant stability. Two bioactive materials were compared to evaluate their effect on dental implant stability. A total of 32 patients (102 dental implants) were divided into 3 groups: 24 dental implants with bone morphogenetic protein (BMP), 27 dental implants with PRF, and 51 dental implants without BMP or PRF (control group). Data were statistically analyzed

A novel technique for nanoparticles with a chemical method and impact for resistance bacteria methicillin-resistant Staphylococcus aureus (MRSA), UV-visible analysis confirmed the by Fourier transform infrared spectroscopy (FT-IR) and Energy dispersive X-Ray (EDX), Scanning electron microscope (SEM) and X-ray diffraction pattern estimation antimicrobial excellent antibacterial activity against MRSA (with zone of inhibition of 11 ± 02 mm , 9 ± 01 mm,8 ± 03 mm and 7.5 ± 02 mm and 6.5 ± 02 mm) at different concentrations (0.5 ,0.25, 0.125, 0.0625, 0.03125) mg/ml while good activity was 16 ± 03 mm at 17 ± 02 mm zone at 0.25, 0.125 mg/mL, respectively. The increase in microorganism resistance to antibiotics a couple of have caused

This study was done to compare the morphometric parameters of placentas in well controlled patients with preeclampsia, diabetes, and preeclampsia-diabetes with that of normal uncomplicated placentas. Patients & Methods: A total of Twenty four placentas were freshly collected. Six placentas for control group and eighteen placentas for complicated group (preeclamptic-diabetic and preeclamptic--diabetic subgroups). The placentas were grossly examined (shape, number of cotyledons, weight, and thickness). After suitable fixation, tissue processing and sectioning, the sections were stained by hematoxylin and eosin to study the general morphology and morphometry of the following parameters: number of terminal villi, number of syncytial knots, numb

Silver nanoparticles synthesized by different species

Out of a total of fifty samples, thirty-five isolates were identified as Serratia marcescens. Thesediverse clinical samples were collected over a three-month period, from October 2023 to December 2023, fromseveral hospitals in Baghdad, including Fatima Al-Zahraa Hospital, Al-Sader Hospital, Ibn Al-Balady Hospital,and Al-Imam Ali Hospital. The clinical samples primarily included urine from patients with urinary tractinfections (UTIs). All isolates were cultured on nutrient agar, MacConkey agar, and blood agar, and theiridentities were confirmed through biochemical testing and the Vitek 2 compact system. Based on phenotypicvirulence factors, the S. marcescens isolates showed varying positive patterns: 32 out of 35 (91.42%) forprotease

A total of 165 clinical sample included Urine, Swab wounds and Burns were collected from Baghdad Governorate. Results showed that rate all isolates of E. coli was 50(30.3%) and rate of urine infection was 46(92%) and rate of swab wounds infection 4(8%). Where was diagnostic based on streaked on MacConkey agar, then single colony was transferred to Eosin Methylene Blue (EMB). Identification some of the biochemical test included: Catalase test, Oxidase test, Indole test, Methyl red, Vogues - Proskauer test and Citrate Utilization test. Then confirmed by the Vitek - 2 Compact System. The ability of E.coli isolate to biofilm formation to be studied it is considered one of the most important factors of virulence and has role in causing injury an