Background: Crown preparation of vital teeth involve the removal of a sound tooth structure, and when enamel removed this lead to exposed dentin with an   increase in the number of open dentinal tubules also the diameter of dentinal tubules will increase, furthermore lead to increase movement of fluids inside the tubules all that causes post preparation sensitivity. The aim of this study is to evaluate the effect of desensitizing by Er:Cr:YSGG laser on shear bond strength of prepared tooth and resin cement. Materials and methods: Thirty sound maxillary premolars, grouped into three groups(n=10). Group A is the control group, group B irradiated by Er:Cr:YSGG laser with (0.25 W, 20 Hz, 1

The present study was Conducted to evaluate the effect of amixture of three species of arbuscular mycorrhizal fungi ( Glomus etunicatum , G. leptotichum and Rhizophagus intraradices ) in Influence on the percentage of the components of NPK and protein of tomato leaves and roots infected with Fusarium oxysporum f.sp. Lycopersici wich cause Fusarial wilt disease , planted for 8 weeks in the presence of the organic matter ( peatmose) , using pot cultures in aplastic green house , Results indicated significant increase in the percentage of the elements of NK and protein of tomato leaves and roots In the control treatment (C), While the percentage of the element P was after infection with the pathogen 4 weaks after mycorrhizal colonization in al

Abstract The present study was Conducted to evaluate the effect of amixture of three species of arbuscular mycorrhizal fungi ( Glomus etunicatum , G. leptotichum and Rhizophagus intraradices ) in Influence on the percentage of the components of NPK and protein of tomato leaves and roots infected with Fusarium oxysporum f.sp. Lycopersici wich cause Fusarial wilt disease , planted for 8 weeks in the presence of the organic matter ( peatmose) , using pot cultures in aplastic green house , Results indicated significant increase in the percentage of the elements of NK and protein of tomato leaves and roots In the control treatment (C), While the percentage of the element P was after infection with the pathogen 4 weaks after mycorrhiza

Background: This study was performed to determine the effect of aging of different types of composite material restorations on: Shear bond strength (SBS) to light cure and no mix chemical cure orthodontic adhesives with sapphire bracket and the debonding failure sites. Materials and methods: One hundred forty four composite disks were made from three different composite resin materials which are: 3M Filtek Z250, 3M filtek Z350 and 3M Valux plus, each group with (48) disks each, then according to the duration of storage each group was subdivided into two equal groups one of them stored for one day and the other was stored for one month, then each group was further subdivided into two equal subgroups with (12) disks each one bonded with ligh

The effect of different doses of gamma rays that emitted from 60Co on the development of different stages of lesser grain borer Rhyzopertha dominica (Fab.) was investigated . The results showed that the eggs in both early (1-3 days) and late (7-9) old were very sensitive to gamma rays and its hatch was zero at 10 Gy for both ages in comparison with 83.3% for the control group. Furthermore, the results illustrated that the larval stage in its two old ages were different in the radiosensitivity, the percent of its death were 100% & 96.6% when they exposed to 100 & 120 Gy, respectively. Moreover, the results showed that the sensitivity of pupal stage at age of 1-3 days was increased with increasing the doses of gamma rays, the percent of no

Background: The displacement of artificial teeth during complete denture construction presents major processing errors in the occlusal vertical dimension which were verified at the previous trial denture stage. The aim of this study was to assess the effect of delay in processing after final flask closure and tension application on the vertical acrylic and porcelain teeth displacement of complete dentures constructed from heat cured acrylic and the results were compared with the conventional processing method. Materials and methods: forty samples of identical maxillary complete dentures were constructed from heat polymerized acrylic resin. These samples were subdivided into the following experimental subgroups in which each subgroup contai

Low conversion copolymerization of N-vinyl-2-pyrrolidon M.W = (111.14) VP (monomer-1) has been conducted with acrylic acid AA and methymethacrylate MMA in ethanol at 70ºC , using Benzoyl peroxide BPO as initiator . The copolymer composition has been determined by elemental analysis. The monomer reactivity ratios have been calculated by the Kelen-Tudos and Finman-Ross graphical procedures . The derived reactivity ratios (r1 , r2 ) are : (0.51 , 4.85) for (VP / AA ) systems and (0.34 , 7.58) for (VP , MMA) systems , and found the reactivity ratios of the monomer AA , MMA is mor than the monomer VP in the copolymerization of (VP / AA) and (VP /MMA) systems respectly . The reactivity ratios values were used for microstructures calculation.

In this research, geopolymer mortar had to be designed with 50% to 50% slag and fly ash with and without 1% micro steel fiber at curing temperature of 240℃. The molarity of alkaline solution adjusted with 12 molar sodium hydroxid to sodium silicate was 2 to 1, reaspectivly. The heat of curing increased the geopolymerization proceses of geoplymer mortar, which led to increasing strength, giving the best result and early curing age. The heat was applied for two days by four hours each day. It was discovered in the impact test that the value first crack of each mix was somewhat similar, but the failure increased 72%  for the mixture that did not contain fiber. For the energy observation results it was shown that the mixt

Positron annihilation lifetime (PAL) technique has been employed to
study the microstructural changes of polyurethane (PU), EUXIT 101
and epoxy risen (EP), EUXIT 60 by Gamma-ray irradiation with the
dose range (95.76 - 957.6) kGy. The size of the free volume hole and
their fraction in PU and EP were determined from ortho-positronium
lifetime component and its intensity in the measured lifetime spectra.
The results show that the irradiation causes significant changes in the
free volume hole size (V_h) and the fractional free volume (F_h), and
thereby the microstructure of PU and EP. The results indicate that
the γ-dose increases the crystallinity in the amorphous regions of PU
and increas