In this work, Soda Lime Glass (S.L.G.) powder was used ,as
fluxe in traditional porcelain instead of feldspar. Two ceramics
porcelain were compared; commercial or traditional porcelain that
content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar.
Feldspar mass was substituted by scraps soda lime glass yielding a
new porcelain composition, to determine the softening points and
then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water
was added. The resulting composite blends were then die pressed at
2N, to produce disk specimens with diameter of 1.5 cm, and then
they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and
1450) ˚C, for 2 hours in an electric furnace with a digital controller.
Physical parameters, such as density, water absorption, and
shrinkage were measured. It was concluded that the sintering
process and physical properties were improved by heat treatment.
However, the firing results showed that the addition of S.L.G.
replacing feldspar lowers the melting points of porcelain and the
addition of scrap powder has a positive effect on the quartz
dissolution
(4)
A significant increase in the incidence of non-O157 verotoxigenic Escherichia coli (VTEC) infections have become a serious health issues, and this situation is worsening due to the dissemination of plasmid mediated multidrug-resistant microorganisms worldwide. This study aims to investigate the presence of plasmid-mediated verotoxin gene in non-O157 E. coli. Standard microbiological techniques identified a total of 137 E. coli isolates. The plasmid was detected by Perfectprep Plasmid Mini preparation kit. These isolates were subjected to disk diffusion assay, and plasmid curing with ethidium bromide treatment. The plasmid containing isolates were subjected to a polymerase chain reaction (PCR) for investigating
... Show More
(3)
(1)
Background. Implant insertion in regions with poor bone quantity, such as the posterior maxilla, is potentially associated with an increased rate of implant failure. Calcium sulfate can be used as the coating material for commercially pure titanium (CpTi) and as the bone graft material around implants when bound to eggshell powder to enhance the bone quality and quantity of bone defect regions. This study performed a torque removal test to evaluate the effectiveness of eggshell powder as a bone substitute for filling bone defects around CpTi-coated implants coated with nanocrystalline calcium sulfate. Materials and Methods. Eighty screw implant designs were used in the tibiae of 20 white New Zealand rabbits. A total of uncoated 20 s
... Show More
(15)
Alpha shape theory for 3D visualization and volumetric measurement of brain tumor progression using magnetic resonance images
(32)
(27)
(31)
(27)
Bacterial strains were isolated from oil-contaminated soil, in 2018, these isolates were identified, and with the aim of finding out the ability of these isolates to degrede the oil compounds, the color change of medium which added to it isolates was read by the method of Pacto Bushnell Hans. Then the change in the petroleum compounds was read by gas chromatography, for the most effective isolates.
The nine isolated bacterial showed different degrees of color change, and the isolates (Pseudomonas, Bacillus, Micrococcus) outperformed the color change amount (78, 78, 77) %, respectively, compared to the control, and the three isolates together showed the best color change of 90.7. % Compared to the control, and the
... Show More
(4)
(1)
All the prepared metal complexes of Pt (IV), Au(III), Rh (III), Co (II) and V(IV) with new ligand sodium [5-(p-nitro phenyl)-/4-phenyl-1,2,4-triazole-3-dithiocarbamato hydrazide] (TRZ.DTC) have been synthesized and characterized in solid state by using flame atomic absorption, elemental analysis C.H.N.S, FT-IR ,UV-Vis Spectroscopy, conductivity and magnetic susceptibility measurements. The nature of the complexes formed in ethanolic solution has been studied following the molar ratio method also was studied stability constant and found to be stable in molar ratio1:1 of VL (IV) and CoL(II) while Pt(IV), Au(III) and Rh(III) complexes stable in molar ratio 1:2 as well as the molar absorptivity for these complexes were calculated. From the prev
... Show More
The new tridentate Schiff base ligand (HL)namely 2-{[1-(3-amino-phenyl)-ethylidene]-hydrazono methyl}- phenol containing (N N O)as donors atoms was prepared in two steps:Step (1): By the reaction of 3- aminoacetophenone with hydrazine monohydrate under reflux in methanol and drops of glacial acetic acid gave the intermediate compound 3-(1- hydrazono ethyl)-phenol amine.Step (2): By the reaction of 3-(1-hydrazono ethyl)-phenol amine with salicyaldehyde under reflux in methanol, gave the ligand (HL).The prepared ligand was characterized by I.R, U.V-Vis,1H- 13C NMR spectra and melting point and reacted with some metal ions under reflux in methanol with (1:1) ratio gave complexes of the general formula: [MClL]. Where: M= Mn(II), Fe(II), Co(II),
... Show MoreThis research is carried out to investigate the behavior of self-compacting concrete (SCC) two-way slabs with central square opening under uniformly distributed loads. The experimental part of this research is based on casting and testing six SCC simply supported square slabs having the same dimentions and reinforcement. One of these slabs was cast without opening as a control slab. While, the other five slabs having opening ratios (OR) of 2.78%, 6.25%, 11.11%, 17.36% and 25.00%. From the experimental results it is found that the maximum percentage decrease in cracking and ultimate uniform loads were 31.82% and 12.17% compared to control slab for opening ratios (OR
... Show MoreAbstract: Aluminum alloys grade 6061-T6 are characterized by their excellent properties and processing characteristics which make them ideal for varieties of industrial applications under cyclic loading, aluminum alloys show less fatigue life than steel alloys of similar strength. In the current study, a nanosecond fiber laser of maximum pulse energy up to 9.9 mJ was used to apply laser shock peening process (LSP) on aluminum thin sheets to introduce residual stresses in order to enhance fatigue life under cyclic loading Box-Behnken design (BBD) based on the design of experiments (DOE) was employed in this study for experimental design data analysis, model building and optimization The effect of working parameters spot size (ω), scannin
... Show More