The technical of Flame Thermal Spray had been used in producing a cermet
composite based on powders of stabilized zirconium oxide containing amount of
Yatteria oxide (ZrO2- 8Y2O3) reiforced by minerals powders of bonding material
(Ni-Cr- Al- Y) in different rates of additions (25, 35, 50) on stainless steel base type
(304) after preparing it by the way of Grit Blasting.
Before heat treatment, the coated cermet layers were characterized for porosity
and electric resistivity. All samples were heat treated in vacuum furnace at different
temperature and times. The physical tests had been operated after heat treatment
and gave best results especially porosity, which found to be reduced dramatically
and producing high hardness. The best thickness of coating with bonding material
(25%) was (1.5 mm). The resistivity was found to increase after heat treatment but
it reduces with increasing the amount of self bonding additions
(6)
(1)
This study examines experimentally the performance of a horizontal triple concentric tube heat exchanger TCTHE made of copper metal using water as cooling fluid and oil-40 as hot fluid. Hot fluid enters the inner annular tube of the TCTHE in a direction at a temperature of 50, 60 and 70 oC and a flow rate of 20 l/hr. On the other hand, the cooling fluid enters the inner tube and the outer annular tube in the reverse direction (counter current flow) at a temperature of 25 oC and flow rates of 10, 15, 20, 25, 30 and 35 l/hr. The TCTHE is composed of three copper tubes with outer diameters of 34.925 mm, 22.25 mm, and 9.525 mm, and thicknesses of 1.27 mm, 1.143 mm, and 0.762 mm, respectively. TCTHE tube's length was 670
... Show More
ولاء طارق حميد, Mustansiriyah Journal of Sports Science, 2021
The education, especially higher education, is an essentially factor in the progress of any society, if we consider the higher education, represents the top of the education`s pyramid which take part in developing the human resources and provide the human staff to raise the productive efficiency, and improve the social , economic level
In order to face the increasing importance of higher education, great capabilities and expenditures must be available in a continous way, such expe
... Show More
(1)
GA Al Omran, AA Noaimi, Z Al Madfai, H Al Hamamy, Journal of the Faculty of Medicine Baghdad, 2012
Several types of laser are used in experimental works in order to study the effects of laser on blood vessel. They differ from each other by a lot of properties mainly in wavelength, energy of the laser and pulse duration. In this study argon laser (488 nm- 514 nm) and continuous Nd: YAG laSer (1064 nm), have been applied to 50 samples of sheep blgod tesselS. Histologically, tha results of the study were different According to the txpe of L`sar used; apgon larer had distrabtave effects on $he blood vessal while continuous Nd: YAG laser Appeaped to be the safesd one on the blmod vessel architecture. This study concluded that argoj laser has da-aging ef&ect on
... Show More
(1)
In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850oC) using single screw extruder and a mixing machine operated at a temperature between (190-200oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength
... Show More