In this study three inorganic nano additives, namely; CaCO3, Al2O3 and SiO2 were used to prepare nanocomposites of unsaturated polyester in order to modify their mechanical properties, i.e. tensile strength, elongation, impact and hardness. The results indicated that all the three additives were effective to improve the mechanical properties up to 4% by weight. The effectiveness of them follows the order : CaCO3 > Al2O3 > SiO2 This is due to their particle size in which CaCO3 (13nm), Al2O3 (20-30nm) and SiO2 (15-20nm).

Submerged arc welding (SAW) process is an essential metal joining processes in industry. The quality of weld is a very important working aspect for the manufacturing and construction industries, the challenges are made optimal process environment. Design of experimental using Taguchi method (L9 orthogonal array (OA)) considering three SAW parameter are (welding current, arc voltage and welding speed) and three levels (300-350-400 Amp. , 32-36-40 V and 26-28-30 cm/min). The study was done on SAW process parameters on the mechanical properties of steel type comply with (ASTM A516 grade 70). Signal to Noise ratio (S/N) was computed to calculate the optimal process parameters. Percentage contributions of each parameter are validated by using an

Therapeutically and prophylactically using Microspheres containing doxycycline isolated from shell of shrimp. Low molecule weight poly lactic acid was prepared. In this study, Poly lactic acid (PLA)/ poly vinyl alcohol (PVA)/poly ethyleneglycol(PEG) loading doxycycline blend solutions was prepared. Also Poly lactic acid (PLA)-Tannin blend via solvent evaporation method was prepared. Microspheres of chitosan/gelatin microsphere loading doxycycline was prepared by emulsion crosslinking technique. Both microsphere and blends were characterized by Fourier transform infrared (FTIR) spectrophotometer. The FTIR spectra were shown distinguish bands. The in vitro release of doxcycline from its matrix at pH 7 was studied. The prophylactic

􀀤􀁅􀁖􀁗􀁕􀁄􀁆􀁗􀀑􀀃􀀬􀁑􀀃􀁗􀁋􀁌􀁖􀀃􀁕􀁈􀁖􀁈􀁄􀁕􀁆􀁋􀀏􀀃􀀤􀁊􀀤􀁏􀀔􀀐􀁛􀀬􀁑􀁛􀀶􀁈􀀕􀀃􀀋􀀤􀀤􀀬􀀶􀀌􀀃􀁆􀁒􀁐􀁓􀁒􀁘􀁑􀁇􀀃􀁄􀁏􀁏􀁒􀁜􀁖􀀃􀁓􀁕􀁈􀁓􀁄􀁕􀁈􀁇􀀃􀁉􀁒􀁕􀀃􀁇􀁌􀁉􀁉􀁈􀁕􀁈􀁑􀁗􀀃􀁛􀀃􀀋􀀓􀀑􀀖􀀏􀀃􀀓􀀑􀀙􀀃􀁄􀁑􀁇􀀃􀀓􀀑􀀜􀀌􀀃􀁅􀁜􀀃􀁐􀁈􀁏􀁗􀁌􀁑􀁊􀀃 􀁗􀁋􀁈􀁐􀀃 􀁌􀁑􀀃 􀁄􀁑􀀃 􀁈􀁙􀁄􀁆􀁘􀁄􀁗􀁈􀁇􀀃 􀁔􀁘􀁄􀁕􀁗􀁝􀀃 􀁗􀁘􀁅􀁈􀀃 􀀋􀀕􀀑􀀘􀀍􀀔􀀓􀀐􀀖􀀃 􀁗􀁒􀁕􀁕􀀌􀀑􀀃 􀀤􀀤􀀬􀀶􀀃 􀁚􀁌􀁗􀁋􀀃 􀁇􀁌􀁉􀁉

This paper presents the Taguchi approach for optimization of hardness for  shape memory alloy (Cu-Al-Ni) . The influence of  powder metallurgy parameters on hardness has been investigated. Taguchi technique and ANOVA were used for analysis. Nine experimental runs based on Taguchi’s L9 orthogonal array were performed (OA),for two parameters was study (Pressure and sintering temperature) for three different levels (300 ,500 and 700) MPa ,(700 ,800 and  900)^oC respectively . Main effect, signal-to-noise (S/N) ratio was study, and analysis of variance (ANOVA) using  to investigate the micro-hardness characteristics of the shape memory alloy .after application the result of study shown the hei

In this work, copper substituted cobalt ferrite nanoparticles with
chemical formula Co1-xCuxFe2O4 (x=0, 0.3, and 0.7), has been
synthesized via hydrothermal preparation method. The structure of
the prepared materials was characterized by X-ray diffraction (XRD).
The (XRD) patterns showed single phase spinel ferrite structure.
Average crystallite size (D), lattice constant (a), and crystal density
(dx) have been calculated from the most intense peak (311).
Comparative standardization also performed using smaller average
particle size (D) on the XRD patterns of as-prepared ferrite samples
in order to select most convenient hydrothermal synthesis conditions
to get ferrite materials with smallest average particl