The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during the test. Reinforcement PMMA with different kinds of glass fibers would increase the initial bending stresses for all specimens. The cracks would appear slowly during the test, and the specimens will not separate during the test except the samples which reinforced by Woven-Glass-Fibers
Abstract This study aims to compare British war poetry of the First World War with Iraqi poetry from the mid-20th century with special reference to Iraqi war poetry of the 1980’s Iraq-Iran War and the period that followed it. It will also investigate the influence of the designated British war poetry on the chosen body of Iraqi poetry. Through the comparison of sample poems the study presents, firstly, the direct influence of the British poetry of the Great War and its translation which formed the seeds of a more radical movement in Iraqi poetry during the 1980’s Iran/Iraq War and the period that followed it. The study also presents a comparison of the works of British and Iraqi civilian poets during and after the war time and their con
... Show More
ABSTRACT Background: Improving the properties of heat- cured and self-cured acrylic resin have been studied by many researchers. However, little studies concerned with visible light cured resin (VLCR) improved through addition of nanofiller are available. The purpose of this study was to evaluate some properties of (VLCR) after addition of SiO2 nanofiller. Materials and Methods: SiO2 nanofiller were added to (VLCR) tray material after being dissolved in tetrahydrofuran (THF) solvent. According to the pilot study 2% SiO2 nanofiller addition exhibited better properties than the other percentages (1%, 3%). The main study conducted involved (100) specimens divided into 5 groups according to the test included. (20) Specimens were selecte
... Show More
(3)
This study used a continuous photo-Fenton-like method to remediate textile effluent containing azo dyes especially direct blue 15 dye (DB15). A Eucalyptus leaf extract was used to create iron/copper nanoparticles supported on bentonite for use as catalysts (E@B-Fe/Cu-NPs). Two fixed-bed configurations were studied and compared. The first one involved mixing granular bentonite with E@B-Fe/Cu-NPs (GB- E@B-Fe/Cu-NPs), and the other examined the mixing of E@B-Fe/Cu-NPs with glass beads (glass beads-E@B-Fe/Cu-NPs) and filled to the fixed-bed column. Scanning electron microscopy (SEM), zeta potential, and atomic forces spectroscopy (AFM) techniques were used to characterize the obtained particles (NPs). The effect of flow rate and DB15 concent
... Show More
(3)
(1)
Background: Endodontically treated teeth have low resistance to fracture against occlusal forces. The strengthening effect of bonded esthetic onlay restoration on weakened tooth has been reported. This study aimed to assess the fracture resistance of endodontically treated premolars restored with composite with and without cuspal coverage by using direct and indirect techniques. Indirect technique done by CAD/CAM system (computer aided design –computer aided manufacturer) and laboratory processing. Material and methods: Forty human extracted maxillary premolars of approximately comparable sizes were divided into four groups: Group (A): Ten endodontically treated teeth directly filled with Filtek Z250xt without cuspal coverage. Group
... Show MoreBackground: Herbs are being widely explored to discover alternatives to synthetic antibacterial agents.Small Cardamom often referred to as queen of spices because of its very pleasant aroma and taste, have a history as old as human race. Most people use cardamom as a spice and are largely unaware of its numerous health benefits. The purpose of this study was to evaluate the effect of different concentrations of water and alcoholic cardamom extracts on sensitivities, growth, and adherence of Mutans streptococci in vitro. Materials and Methods: In this study, saliva was collected from ten volunteers (College students 18-22 years). Agar well technique was used to study the sensitivities of Mutans streptococci to different concentrations of s
... Show MoreBackground: Spices and herbs have been used by many cultures to enhance the flavor and aroma of food and for their medicinal value. Black cardamom is one of these spices widely used in cooking because of its unique taste and powerful flavor. The aim of study was to test the effect of black cardamom on Mutans Streptococci in comparison to chlorhexidine gluconate (0.2%) and de-ionized water. Materials and methods: Dried fruits of black cardamom were extracted by using alcohol (70% ethanol). Saliva was collected from seven volunteers. Agar well technique with different concentrations of black cardamom extracts was used to test the sensitivities of Mutans Streptococci, as well black cardamom extracts effect on viable counts of Mutans Streptococ
... Show More
(1)
This paper presents a study (experimentally) for strengthening reinforced concrete (RC) beams with Near-Surface-Mounted (NSM) technique. The use of this technique with CFRP strips or rebars is an efficient technology for increasing the strength for flexure and shear or for repairing damaged reinforced concrete (RC) members. The objective of this research is to study, experimentally, RC beams either repaired or strengthened with NSM CFRP strips and follow their flexural behavior and failure modes. NSM-CFRP strips were used to strengthen three RC beam specimens, one of them was initially strengthened and tested up to failure. Four beam specimens have been initially subjected to preloading to 50% and 80% of ultimate load. Two of the sp
... Show More
(1)
In this study, nanocomposites have been prepared by adding
multiwall carbon nanotubes (MWCNTs) with weight ratios (0, 2, 3,
4, 5) wt% to epoxy resin. The samples were prepared by hand lay-up
method. Influence of an applied load before and after immersion in
sodium hydroxide (NaOH) of normality (0.3N) for (15 days) at
laboratory temperature on wear rate of Ep/MWCNTs
nanocomposites was studied. The results showed that wear rate
increases with increasing the applied load for the as prepared and
immersed samples and after immersion. It was also found that epoxy
resin reinforced with MWCNTs has wear rate less than neat epoxy.
The sample (Ep + 5wt% of MWCNTs) has lower wear rate. The
immersion effect in base so
Carbon-fiber-reinforced polymer (CFRP) is widely acknowledged as a leading advanced material structure, offering superior properties compared to traditional materials, and has found diverse applications in several industrial sectors, such as that of automobiles, aircrafts, and power plants. However, the production of CFRP composites is prone to fabrication problems, leading to structural defects arising from cycling and aging processes. Identifying these defects at an early stage is crucial to prevent service issues that could result in catastrophic failures. Hence, routine inspection and maintenance are crucial to prevent system collapse. To achieve this objective, conventional nondestructive testing (NDT) methods are utilized to i