Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be concluded that these variables may increase the graphitizing degree, and minimizing in interplanar distance for samples comparing with ideal one, when these variables may increased.
The local asphalt concrete fracture properties represented by the fracture energy, J-integral, and stress intensity factor are calculated from the results of the three point bending beam test made for pre notches beams specimens with deformation rate of 1.27 mm/min. The results revealed that the stress intensity factor has increased by more than 40% when decreasing the testing temperature 10˚C and increasing the notch depth from 5 to 30mm. The change of asphalt type and content have a limited effect of less than 6%.
The effect of annealing temperature (Ta) on the electrical properties like ,D.C electrical conductivity (σ DC), activation energy (Ea),A.C conductivity σa.c ,real and imaginary (ε1,ε2) of dielectric constants ,relaxation time (τ) has been measured of ZnS thin films (350 nm) in thickness which were prepared at room temperature (R.T) using thermal evaporation under vacuum . The results showed that σD.C increases while the activation energy values(Ea) decreases with increasing of annealing temperature.(Ta) from 303- 423 K .
The density of charge carriers (nH) and Hall mobility (μH) increases also with increasing of annealing temperature Hall effect measurements showed that ZnS films were n-type converted to p-type at high annealin
Cadmium Oxide thin films were deposited on glass substrate by spray pyrolysis technique at different temperatures (300,350,400, 500)oC. The optical properties of the films were studied in this work. The optical band-gap was determined from absorption spectra, it was found that the optical band-gap was within the range of (2.5-2.56)eV also width of localized states and another optical properties.
GaN thin films were deposited by thermal evaporation onto
glass substrates at substrate temperature of 403 K and a thickness of
385 nm . GaN films have amorphous structure as shown in X-ray
diffraction pattern . From absorbance data within the range ( 200-
900 ) nm direct optical energy gap was calculated . Also the others
optical parameters like transmittance T, reflectance R , refractive
index n , extinction coefficient k , real dielectric constant 1 Î , and
imaginary dielectric constant 2 Î were determined . GaN films
have good absorbance and minimum transmittance in the region of
the visible light .
The Asphalt cement is produced as a by-product from the oil industry; the asphalt must practice further processing to control the percentage of its different ingredients so that it will be suitable for paving process. The objective of this work is to prepare different types of modified Asphalt cement using locally available additives, and subjecting the prepared modified Asphalt cement to testing procedures usually adopted for Asphalt cement, and compare the test results with the specification requirements for the modified Asphalt cement to fulfill the paving process requirements. An attempt was made to prepare the modified Asphalt cement for pavement construction in the laboratory by digesting each of the two penetration grade Asphalt c
... Show More
In the present work, lead silicate glasses have been prepared with
different amount of lead oxide content. Structure properties such as
X-ray diffraction, AFM, and FTIR analyses have been done. The
exceeding of PbO content more than 25wt% revealed a decreasing in
density. The X- ray revealed that the strongest peak related to
Hexagonal silica dioxide and the other crystal phases formed were
related to silica oxide (SiO2) and lead oxide (PbO). Growth and
decayed phases in X-ray have been observed with changing lead
oxide content. Homogeneous surface was obtained using AFM
analyzer with an average diameter around 100 nm. Infrared spectrum
is characterized by the presence of large absorption band between
120
(7)
The aim of the present work is to develop a new class of natural fillers based polymer composites with sawdust (S.D) which used two particle sizes (1.2 μm & 2.3 μm) and different weight percentage from sawdust (10%, 15%, and 20%). The mechanical properties studied include hardness (shore D) for all samples at normal conditions (N.C). The unsaturated polyester (UPE) and its composites samples were immersed in water for 30 days to find the effect of particle size of sawdust (S.D) on the weight gain (Mt %) by water for all the samples, also to find the effect of water on their hardness. The results show that the composite materials of sawdust (S.D) fillers which has particle size (1.2 μm) better than (2.3 μm) particle size bef
... Show MoreImplantation of blastocyst is considered as a sensitive process in the life of growing embryo. Thus this critical period could be under threat from the harmful effect of many drugs ,among them is the carbamazepine which is used by many women for a treatment of epilepsy . The present experiment was designed to study the effect of this drug on the process of implantation ;especially during the days 7 and 9 of pregnancy. For those purpose 169 pregnant albino mice, of 25 gm weight for each one, were used .The mice were divided into control group given orally normal saline, and treated group given orally carbamazepine with concentration of 15 mg\kg. Samples from pregnant uteri containing the embryos were used. They were first fixed in Boun's sol
... Show MoreBackground: intravenous regional anaesthesia (IVRA) is an effective method of producing anaesthesia of the extremities. Disadvantages are the rapid loss of anaesthesia after the deflation of the tourniquet and the rapid development of postoperative pain. It is important to search for agents with longer durations of action, better nerve fibre selectivity, lesser degrees of motor blockade and lower incidences of systemic toxicity.Objectives: This study was designed to evaluate and compare the clinical effects of intravenous regional anaesthesia, with lidocaine alone, or in a combination with ketamine and atracurium for better analgesia, and to examine the possible clinical advantages of using muscle relaxants (i.e., atracurium) with intrav
... Show MoreAbstract
The study aims to find out the impact of expectations and perceptions in determining the position of the customer service quality received by him. Represent the expectations and perceptions customer’s key of service quality determinants. The customer's requirements and needs main pivot, who must be built all events and activities and efforts of service organizations, including the hotel and organizations that operate in an environment known as highly competitive , intensification and complexity of the conditions set by the customer and increasing day after day. The study sample of three Luxury hotels in Kurdistan region of Iraq a model. The use of service quality m
... Show More