This work presents the study of the dark current density and the capacitance for porous silicon prepared by photo-electrochemical etching for n-type silicon with laser power density of 10mw/cm2 and wavelength (650nm) under different anodization time (30,40,50,60) minute. The results obtained from this study shows different chara that different characteristic of porous diffecteristics for the different porous Silicon layers.

A simple low-cost approach at various exposure times was utilized to generate cold plasma in the aim to fabricate AuNPs. UV-Visible spectra and X-ray diffraction were used to characterize the nanoparticles (XRD). Surface Plasmon resonance was observed in the synthesized AuNPs at 530, 540, and 533 nm. For all samples, the patterns of XRD show very intensive peaks implying the fcc crystalline structure of AuNPs. The average crystallite size of AuNPs is ranging between 20-30 nm. The observation of morphology by FESEM revealed the spherical formation of AuNPs. Doses of 100 and 200 ppm of AuNPs were adapted to investigate their effect on the blood-mixture with and without a 20-second of cold plasma exposure. The WBC components in the blood

An anatomical study was carried out at the College of Agricultural Engineering Sciences, University of Baghdad, in 2017, on lupine crop (Lupinus albus) as a comparison guide of three seed weights of three lupine cultivars viz. ‘Giza-1’, ‘Giza-2’ and ‘Hamburg’. The nested design was used with four replications. The results showed that cultivars had a significant effect on stem anatomical traits. ‘Hamburg’ cultivar recorded the highest stem diameter, cortex thickness and xylem vascular diameter, while cultivar ‘Giza-1’ recorded the lowest values for the same traits as well as the highest collenchyma layer thickness, vascular bundle thickness, and xylem thickness. Cultivar ‘Giza-2’ recorded the lowest vascular bundle th

An anatomical study was carried out at the College of Agricultural Engineering Sciences, University of Baghdad, in 2017, on lupine crop (Lupinus albus) as a comparison guide of three seed weights of three lupine cultivars viz. ‘Giza-1’, ‘Giza-2’ and ‘Hamburg’. The nested design was used with four replications. The results showed that cultivars had a significant effect on stem anatomical traits. ‘Hamburg’ cultivar recorded the highest stem diameter, cortex thickness and xylem vascular diameter, while cultivar ‘Giza-1’ recorded the lowest values for the same traits as well as the highest collenchyma layer thickness, vascular bundle thickness, and xylem thickness. Cultivar ‘Giza-2’ recorded the lowest vascular b

In the present research, the electrical properties which included the ac-conductivity (σac), loss tangent of dielectric (tan δ) and real dielectric constant (ε’) are studied for nano polycarbonate in different pressures and frequencies as a function of temperature these properties were studied at selective temperature gradients which are (RT-50-100-150-250)°C. The results of the study showed that the values of dielectric constant and dissipation factor increase with increasing pressure and temperature and decreases by increasing frequency. And the results of electrical conductivity showed that it increases with increasing temperature, pressure and frequency.

In this study, geopolymer mortar was designed in various experimental combinations employing 1% micro steel fibers and was subjected to different temperatures, according to the prior works of other researchers. The geopolymer mortar was developed using a variety of sustainable material proportions (fly ash and slag) to examine the influence of fibers on its strength. The fly ash weight percentage was 50%, 60%, and 70% by slag weight to study its effect on the geopolymer mortar's properties. The optimal ratio produced the most significant results when mixed at a 50:50 ratio of fly ash and slag with 1% micro steel fibers at curing temperature 240oC for 4 hours through two days. The compressive strength of the geopolymer mortar increas

Background: The longevity of any prosthesis depends on the materials from which it was fabricated, that is why, defects in the material properties may reduce the service life of prosthesis and necessitate its replacement. The aim of this study was to evaluate the effect of adding different concentrations of Polyamide-6 (Nylon-6) on the tear and tensile strength of A-2186 RTV silicone elastomer. Materials and Methods: 80 samples were fabricated by the addition of 0%, 1%, 3% and 5% by weight PA-6 micro-particles powder to A-2186 platinum RTV silicone elastomer. The study samples were divided into four (4) groups, each group containing 20 samples. One control group was prepared without PA-6 micro particles and three experimental groups were pr