The thin films of SnO2,SnO2:TiO2 , SnO2:MoO3 , SnO2:WO3 , SnO2:Cr2O3 , and SnO2: Fe2O3 were prepared by pulsed laser deposition technique using (Nd:YAG) laser of λ=1064 nm average frequency (6) Hz and pulse duration (10 ns) under vacuum of 10 -2 mbar)deposited on glass, n-Si single crystals substrate room temperature with thickness of (100±10) nm. The structures of pure SnO2 and ,SnO2:TiO2 , SnO2:MoO3 , SnO2:WO3 , SnO2:Cr2O3 , SnO2:Co3O4 compounds were studied by X–ray diffraction .the results showed that there was red shift accompanied addition of MoO3 and TiO2 while a blue shift accompanied the addition of WoO3 , Cr2O3 , Fe2O3 to tin oxide . The gas sensing measurements of NO2 gas showed that S

Cadmium oxide thin films were prepared by D.C magnetron plasma sputtering using different voltages (700, 800, 900, 1000, 1100 and 1200) Volt. The Cadmium oxide structural properties using XRD analysis for just a voltage of 1200 volt at room temperature after annealing in different temperatures (523 and 623) K were studied .The results show that the films prepared at room temperature have some peaks belong to cadmium element along the directions (002), (100), (102) and (103) while the other peaks along the directions of (111), (200) and (222) belong to cadmium oxide. Annealed samples display only cadmium oxide peaks. Also, the spectroscopic properties of plasma diagnostic for CdO thin films were determined and the results show that the el

Hydrogen sulfide (H₂S) gas sensor based on cobalt–manganese spinel oxide MnCo₂O₄ thin films that were prepared by chemical precipitation and green synthesis methods. Structural, morphological, and compositional characterizations of MnCo₂O₄ thin films were performed using XRD, FE-SEM, EDS, and AFM. It was found through XRD patterns that MnCo₂O₄ was formed in a cubic spinel structure for both methods; however, the chemically precipitated thin films possessed better crystallinity and larger crystallite sizes, whereas the green-synthesized films exhibited slightly lower crystallinities and smaller sizes, as evidenced by the broader peaks observed. In addition, FE-SEM and AFM images revealed that the MnCo₂O₄ films prepared by

Pulsed-laser deposition (PLD) technique was used to prepare thin films from cerium oxide (CeO2) doped with erbium and indium oxides. In order to characterize the morphology and sensing features, these films were deposited on glass and/or single silicon substrates, respectively, with erbium and indium oxides. The morphological investigation conducted using atomic force microscope has shown an increase in the non-regularity of particle diameter with increasing doping ratios of both oxides. The maximum particle diameter of 61.45nm was obtained for 9% Eu2O3-doped CeO2. The surface roughness value of Eu2O3-doped ceria was higher than those of In2O3-doped ceria. The gas sensing measurements were done at

Tin oxide: titanium oxide: bismuth oxide (SnO2 )1–x(TiO 2 :Bi 2O3 ) x composites with different loading ratios (0, 0.1, 0.15, 0.2, 0.25 and 0.3) have numerous new application in microelectronics, sensors, and capacitors. This work concerned with the synthesis of (SnO 2 )1–x(TiO 2 :Bi 2O3 ) xcomposites as well as, thin films which were deposited on glass substrates as well as, silicon wafers by using pulsed laser deposition. The diffraction pattern confirms the anatase teteragonal phase of undoped tin oxide. It was observed some peaks related with titanium and bismuth oxides appeared at high loading ratios. Upon the transmission-spectra analysis, the undoped samples declared transmittance 60–67% in a visible spectrum, and the energy ga

In This paper, CuO thin films having different thickness (250, 300 , 350 and 400) nm were deposited on glass substrates by thermal vacuum evaporator. The thermal oxidation of this evaporated film was done in heated glass at temperature (300 in air at one hour. The study of X-ray diffraction investigated all the exhibit polycrystalline nature with monoclinic crystal structure include uniformly grains. Thin film’s internal structure topographical and optical properties. Furthermore, the crystallization directions of CuO (35.54 , 38.70 ) can be clearly observed through an X-ray diffraction analysis XRD, Atomic Force Microscope AFM (topographic image) showed that the surface Characteristics , thin films crystals grew with increases in either

In this work, pure and Ag-doped nickel oxide (NiO) thin films were deposited on glass substrates with different dopant concentrations (0.1, 0.2, 0.3 and 0.4 wt.%) by pulsed-laser deposition (PLD) technique at room temperature. These films were annealed at temperature of 450 °C. The structural and optical properties of the prepared thin films were studied. It was found that annealing process has lead to increase the transmittance of the deposited films. Also, the transmittance was found to increase with doping concentration of silver in the deposited NiO films. The optical energy gap was decreased from 3.5 to 3.2 eV as the doping concentration was increased to 0.4 %.

Toxic dyes are commonly discharged into waste waters and dyes are extensively used in the textile industry so it is necessary to find out efficient and eco-friendly method for treating waste waters resulting from industrial effluences. To achieve this aim the fungus Trichoderma sp. is employed into two lines: first line was self – immobilized fungal pellets in (Czapek – Dox medium) to adsorbs two dyes crystal violet, congo red by concentrations 0.01, 0.02, 0.03, 0.04, 0.05, 0.06 mg/L to both dyes, PH 2, room temperature with shaker in ( hrs.²,hrs.⁴,hrs.²⁴) , by Uv- Visible spectrum . the removal efficiency of 0.05 mg/L crystal violet by Trichoderma sp was 96%. but there was no remova