In this report Silver doped Tin Sulfide (SnS) thin films with ratio of (0.03) were prepared using thermal evaporation with a vacuum of 4*10-6 mbar on glass with (400) nm thickness and the sample annealing with ( 573K ). The optical constants for the wavelengths in the range (300-900) nm and Hall effect for (SnS and SnS:3% Ag) films are investigated and calculated before and after annealing at 573 K. Transition metal doped SnS thin films the regular absorption 70% in the visible region, the doping level intensification the optical band gap values from 1.5- 2 eV. Silver doped tin sulfide (SnS) its direct optical band gap. Hall Effect results of (SnS and SnS:3% Ag) films show all films were (p-type) electrical conductivity with resistivity of

Nanofiltration (NF) ceramic membrane have found increasing applications particularly in wastewater and water treatment. In order to estimate and optimize the performance of NF membranes, the membrane should be characterized correctly in terms of their basic parameters such as effective pore radius (r_p) and equivalent effective thickness as well as effective surface charge ( ), the effective charge density ( ) and Donnan potential ( ). The impact of electrokinetic (zeta) potential on the membrane surface charge density, effective membrane charge density and Donnan potential at two different concentrations of the reference solutions 0.001, 0.01 M sodium chloride at various pH values from 3 to 9, and effective po

The influence of Cr3+ doping on the ground state properties of SrTiO 3 perovskite was evaluated using GGA-PBE approximation. Computational modeling results infered an agreement with the previously published literature. The modification of electronic structure and optical properties due to Cr3+ introducing into SrTiO 3 were investigated. Structural parameters assumed that Cr3+ doping alters the electronic structures of SrTiO 3 by shifting the conduction band through lower energies for the Sr and Ti sites. Besides, results showed that the band gap was reduced by approximately 50% when presenting one Cr3+ atom into the SrTiO 3 system and particularly positioned at Sr sites. Interestingly, substituting Ti site by Cr3+ led to eliminating the ban

  The study focused on the results of first paleostress from thrust fault slip data on Tertiary age of Hemrin North Structure, North of Iraq. The stress inversion was performed for fault slip data using an improved right dihedral model, and then followed by rotational optimization (Georient Software). The trend of the principal stress axes (σ1, σ2 and σ3) and the ratio of the principal stress differences (R) show the main paleostress field is NE-SW compression regime. As well as using Lisle graph and Mohr diagram to determine the magnitudes of palestress.  The values paleostress of the study area were σ1=1430 bars, σ2=632 bars and σ3=166 bar. The large magnitudes of the primary stress axes could be attributed to active tecto

Cu-Al-Ni shape memory alloy specimens has been fabricated using powder metallurgy technique with tube furnace and vacuum sintering environment , three range of Nb powder weight percentage (0.3,0.6,0.9)% has been added. Micro hardness and sliding wear resist has been tested followed by X-ray diffraction, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDX) for micro structure observation. The experimental test for the samples has showed that the increase of Nb powder weight percentage in the master alloy has a significant effect on increasing the hardness and decreasing the wear resist therefore it will enhance the mechanical properties for this alloy.

                The electrical characteristics of polyvinyl alcohol PVA doped with different concentrations (0, 1, 2, 3 and 4wt%) of sodium  iodide NaI powder were studied. The films are prepared using solution casting technique, in order to investigate the effect of sodium iodide NaI additions on the electrical properties of PVA host. The D.C conductivity measured by measuring the D.C electrical resistance using the Keithly Electrometer type 616C, and for different temperatures ranging from 30 – 70^oC.

          The dielectric properties measured by measuring the capacitor and the loss

In this research, titanium dioxide nanoparticles (TiO₂ NPs) were prepared through the sol-gel process at an acidic medium (pH3).TiO₂ nanoparticles were prepared from titanium trichloride (TiCl₃) as a precursor with Ammonium hydroxide (NH₄OH) with 1:3 ratio at 50 °C. The resulting gel was dried at 70 °C to obtain the Nanocrystalline powder. The powder from the drying process was treated thermally at temperatures 500 °C and 700 °C. The crystalline structure, surface morphology, and particle size were studied by using X-ray diffraction (XRD), Atomic Force Microscopy (AFM), and Scanning Electron Microscope (SEM). The results showed (anatase) phase of titanium dioxide with the average grain size

A Mini-TEA CO2 laser system was designed and operated to obtain a pulse at 10.6 μm. Output energy of 30 mJ, with preionization pins, and pulse duration of 100ns were obtained. While an output energy of 6mJ and pulse duration of 100 ns in absence of pre-ionization were obtained. The system was operated with Ernest profile main-discharge electrodes. Dependencies of supply voltage and output laser energy on the pressure inside laser cavity were investigated as well as dependencies of supply voltage and output energy on the main capacitor(8CO2 : 8N2 : 82He :2CO). Efficiency of was calculated to be 4.4%.