In this work, magnesium aluminate spinel (MA) (MgO 28 wt%, Al2O3 72 wt%) stoichiometric compound , were synthesized via solid state reaction (SSR) Single firing stage, and the impact of sintering on the physical properties and thermal properties as well as the fine structure and morphology of the ceramic product were examined. The Spinel samples were pressed at of (14 MPa) and sintering soaking time (2h). The effect of adding oxide titania (TiO2) was studied. The obtained powders were calcined at a temperature range of 1200 and 1400 °C. The calcined samples spinel were characterized by XRD, it showed the presence of developed spinel phase end also showed that the best catalyst is titania. The SEM image showed the high sintering temperat

     In the present work effect of recycled heating and cooling on the values of concrete compressive strength due to high temperature of 400⁰C was studied.

    The tests show that the percent of reduction in compressive strength of the samples which exposed to a temperature of 400⁰C for one cycle was 32.5%, while the reduction was 52.7% for the samples which were exposed to recycled heating and cooling of ten times .      

   Moreover a study of the effect of specimen sizes on the percentages of compressive strength reduction due to high temperature

The aim of this research is to identify the effect of Webinar technique on digital culture in the College of Education for pure sciences at Ibin Haitham, University of Baghdad. The research samples consisted of (68) male and female students from the Chemistry Department who are following classes during the (2019- 2020) academic year. The samples represent (42%) of the total number of (162) students split into control and experimental groups. For this purpose, the scientific contents for testing were determined. The experimental part is based on analysis of the results from experiments in (preliminary standard solutions, refractive index, Beer-Lambert law). To achieve the aim of the research in testing the measure of student's digital cultur

The effect of using different R -molar ratio under variable reaction conditions (acidic as well as basic environment and reaction temperature) have been studied. The overall experiments are driven with open and closed systems. The study shows that there is an optimum value for a minimum gelling time at R equal 2. The gelling time for all studied open system found to be shorter than in closed system. In acidic environment and when R value increased from 2 to 10, the gelling time of closed systems has increased four times than open systems at T=30 ?C and fourteen times when temperature reaction increased to 60 ?C. While in basic environment the influence of increasing R value was limited.

In order to achieve optimal plant growth and production, essential nutrients must be readily available in adequate quantities and in a balanced proportion to give a good yield, especially broccoli which has health benefits that may not be found in many other plants. For this purpose, this experiment was carried out during the seasons 2019/2020 in the botanical garden of the Department of Biology, College of Science for Women, University of Baghdad, to study the effects of nitrogen and sulphur and their interaction on eight parameters reflecting the overall traits of vegetative growth, yield, and chlorophyll content of broccoli Brassica oleracea L. (var. italic JASSMINE F1 Hybrid). A factorial design with three replicates was use

the behavior of the first-order black and gray solitons propagtedin optical fiber in the presence of frequency chirp is studied analytically and numerically results show that phase profile of black solitons changes abruptly

The whole research paper examines the impact of ozone as either a just use-alone and coagulation benefit, mainly upon the reduction of dissolved organic carbon from the water with a moderate rate of DOC 10.75 mg/land CaCO3 calcium hardness 300 mg/l. A raw water sample has been taken from the Tigris River (Baghdad, Iraq) was being adopted in research work. The performance of ozone therapy has been assessed by calculations of DOC, DOC quantities, UV254, as well as total trihalomethane (TTHM). Research findings have shown that with 0.9 mg O3/mg DOC ozone use-alone, approximately 60% UV254 reduction and approximately 28% DOC reduction will occur.DOC fractionation analysis indicates that within the water samples, ozone could alter the co

In this work preparation of antireflection coating with single layer of MgO using pulsed laser deposition (PLD) method which deposit on glass substrate with different thicknesses (90 and 100) nm annealed at temperature 500 K was done.
The optical and structural properties (X-ray diffraction) have been determined. The optical reflectance was computed with the aid of MATLAB over the visible and near infrared region. Results shows that the best result obtained for optical performance of AR'Cs at 700 shots with thickness 90 nm nanostructure single layer AR'Cs and low reflection at wavelength 550 nm.

The effect of different doping ratio (0.3, 0.5, and 0.7) with thickness in the range 300nmand annealed at different temp.(Ta=RT, 473, 573, 673) K on the electrical conductivity and hall effect measurements of AgInTe2thin film have and been investigated AgAlxIn(1-x) Te2 (AAIT) at RT, using thermal evaporation technique all the films were prepared on glass substrates from the alloy of the compound. Electrical conductivity (σ), the activation energies (Ea1, Ea2), Hall mobility and the carrier concentration are investigated as a function of doping. All films consist of two types of transport mechanisms for free carriers. The activation energy (Ea) decreased whereas electrical conductivity increases with increased doping. Results of Hall Effect