In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850^oC) using single screw extruder and a mixing machine operated at a temperature between (190-200^oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength

Patients are very concerned about the lengthy nature of orthodontic treatment. It is necessary to find a non-invasive way to quicken physiologic tooth movement. This study's objective was to assess the effectiveness of low-intensity laser therapy in shortening the time and discomfort of orthodontic treatment. Experimental work: Using a split-mouth study to compare tooth movement with conventional treatment and laser-accelerated orthodontic tooth movement. A patient presenting with a class II division I malocclusion characterized by the misalignment of the upper and lower teeth as classified by Angle’s molar classification system was indicated to undergo fixed orthodontic appliance orthodontic treatment. The treatment plan involved bila

Etoricoxib (EXB) is a highly selective cox-2 inhibitor which belongs to the non-steroidal anti-inflammatory drug (NSAID). EXB is a class II drug according to the biopharmaceutical classification system (BCS), which possess a very low aqueous solubility in water.  In the present study, many trials were made to improve the aqueous solubility and dissolution rate of EXB by solid dispersion technique.

Eighteenth EXB formulas were formulated as a solid dispersion using a variety of hydrophilic polymers (as carriers)   including poloxamer 407 (PXM 407), poloxamer 188 (PXM 188) and polyethylene glycol 4000 (PEG 4000) at different drug: polymer ratios (1:1, 1:3 and 1:5). These formulas were prepared by two methods; solvent

Semiconductor quantum dots (QDs) have attracted tremendous attentions for their unique characteristics for solid-state lighting and thin-film display applications. A simple chemical method was used to synthesis quantum dots (QDs) of zinc sulfide (ZnS) with low cost. The XRD) shows cubic phase of the prepared ZnS with an average particles size of (3-29) nm. In UV-Vis. spectra observed a large blue shift over 38 nm. The band gaps energy (Eg) was 3.8 eV and 3.37eV from the absorption and photoluminescence (PL) respectively which larger than the Eg for bulk. QDs-LED hybrid devices were fabricated using ITO/ PEDOT: PSS/ Poly-TPD/ ZnS-QDs/ with different electron transport layers and cathode of LiF/Al layers. The EL spectrum reveals a bro

INFLUENCE OF SOME FACTOR ON SOMATIC EMBRYOS INDUCTION AND GERMINATION OF DATE PALM BARHI C.V BY USING CELL SUSPENSION CULTURE TECHNIQUE

Background: The purpose of this study was to evaluate the effect of addition of surface treated silicon dioxide Nano filler (SiO2) on some properties of heat cured acrylic resin denture base material (PMMA). The properties were impact strength, transvers strength, and surface hardness. Materials and methods: In addition to controlled group SiO2 powder was added to PMMA powder by weight in three different percentages 3%, 5% and 7%, mixed by probe ultra-sonication machine.120 specimens were constructed and divided into 3 groups according to the test (each group consist of 40 specimens) and each group was subdivided into 4 sub-groups according to the percentage of added SiO2 (finally each subgroup consist of 10 specimens). The tests conducte

Recent research has examined the improvement of physical and dielectric properties of BaTiO₃ ceramic material by small addition of excess TiO₂ or BaCO₃. The prepared samples sintered at different temperatures and varying soaking time. The results show that increasing the sintering temperature within 1350°C and soaking time of 10 hrs give better electrical and physical properties, which indicate the reaction is complete at higher temperature and period.

High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2