The adhesion strength between Polyethylene (PE) film and Aluminum surface by using the adhesive material (Cyanoacrylate) has been studied. Aluminum (Al) was used as a substrate, and polyethylene (PE) was used as a film adhered to the Al surface. Standard specimens were prepared to use in the peeling test in dry condition, other specimens were immersed in water for 12 days at room temperature. the results for the specimens in the dry condition had shown that high value in the peel force and the peel energy, the peel force was 0.38*103 N/m and the peel energy was 0.605*103 N/m, peeling the film from Al surface leaves a residual of the adhesive material on both adherend, the failure for this specimen were combination of adhesive and cohesive f

The sintering behavior of Alumina was investigated by adding TiO2. The addition of TiO2 lowered the sintering temperature of the Alumina compared with those of pure Alumina. The result suggests that TiO2 acts as an activator for sintering of Alumina. Water absorption, apparent porosity and density were examined for both pure and TiO2 added to Alumina samples. The variations of sintering behavior were discussed in terms of shrinkage, porosity, water absorption and density. Thermal shock resistance was also examined. In term of this work, the way of improving the thermal shock resistance in oxide- based materials by adding reactive Titania powder to the Alumina samples. The laboratory results showed an improvement in thermal shock resistance

Background: Kinesiologists, Physical Anthropologists, and Anatomists have all long been captivated by the structure and development of the superficial forearm flexor, the Palmaris longus.

Objective: To study the effect of Palmaris Longus on certain handwriting skills.

Subjects and Methods: Three Palmaris Longus occurrence tests were conducted on 200 students (100 males and 100 females) affiliated to Colleges of Medicine of Baghdad University then the participants were tested for certain handwriting skills to correlate the presence of Palmaris Longus in the dominant side with handwriting.

Results: 89% of all subject

This study sought to determine malformation caused by Ochratoxin-A (OTA) on mouse embryos. Twenty adult female white Swiss mice (mus msculus) were divided into four groups, with five females per group, and with one male placed with two females in a cage. Avaginal plug was observed in the early morning and the day of mating was considered as day of pregnancy followed by the first day of pregnancy. Three sub lethal concentrations of OTA were applied to the respective groups (other than the control), 1mg/kg, 2mg/kg and 4mg/kg. The animals were given 0.1 ml per 10 gm body weight per concentration of OTA once a day during days 7-14 of pregnancy. The control group animals were given distilled water. The pregnant mice were dissected, and the embry

The civil engineering field currently focus on sustainable development. It is important to develop new sustainable and economic generations of concrete, using eco-friendly materials in the construction industry with a fair amount of costs and minimizing the impact upon the environment by reducing CO2 emissions from the cement industry as a whole while still obtaining high cement quality and strength. The main objective of this research is to clarify the mechanical behavior and ability to use Portland limestone cement in producing self compacted concrete, due to the beneficious effec of the limestone cement economically and enviromently. The research investigates the effect of using steel and polymer meshs as reinforcement, where the results

The aim of this study is to understand the effect of addition carbon types on aluminum electrical conductivity which used three fillers of carbon reinforced aluminum at different weight fractions. The experimental results showed that electrical conductivity of aluminum was decreased by the addition all carbon types, also at low weight fraction of carbon black; it reached (4.53S/cm), whereas it was appeared highly increasing for each carbon fiber and synthetic graphite. At (45%) weight fraction the electrical conductivity was decreased to (4.36Scm) and (4.27Scm) for each carbon fiber and synthetic graphite, respectively. While it was reached to maximum value with carbon black. Hybrid composites were investigated also; the results exhibit tha

Autorías: Jehan Faris Yousif, Read Idrees Mahmood. Localización: Utopía y praxis latinoamericana: revista internacional de filosofía iberoamericana y teoría social. Nº. 1, 2020. Artículo de Revista en Dialnet.