High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2) and Cd with ratio (y=0.01), has the maximum value of zero resistance temperature, where was the TC(onset) and TC(0) values for this sample are (140 K) and (123 K) respectively, and XRD results reveal that this sample has the highest percentage of Bi- 2223 phase, as well as the analysis of XRD patterns of the prepared materials showed polycrystalline structure and signalize that all samples had an orthorhombic crystalline structure. It was concluded that Sb2O3 nanoparticles it may be acts as a flux agent in the matrix to lower the partial melting temperature of the samples and that leads to the promotion of the high-TC phase.
Abstract
The toughening of epoxy resins with the addition of organic or inorganic compounds is of great interest nowadays, considering their large scale of applications. In the present work, composites of epoxy are synthesized with kaolin particles having different particle sizes as reinforcement. Composites of epoxy with varying concentration (0 to 40 weight %) of kaolin was prepared by using hand lay method. The variation of mechanical properties such as modulus of elasticity, yield, tensile, and compressive strength with filler content was evaluated. The composite showed improved modulus of elasticity and compressive properties on addition of filler. In contrast, the tensile and yield strength of the composite
... Show MoreThis study aims to analyze the spectral properties of plasma produced from rice husk(Rh) using the laser breakdown spectroscopy (LIBS) method. The plasma generation process used the fundamental harmonic (1064 nm) of a Q-switched Nd:YAG laser. Yttrium aluminum garnet (YAG) is a man-made crystalline material. The laser fired pulses with a duration of 10 ns and a repetition rate of 6 Hz. Thus, the energy outputs achieved were 50–200 mJ at the wavelength of 1064 (nm). The silica content in the rice hulls was verified using an XRF measurement, which revealed the presence of silica in the rice hulls in a high percentage. Precise beam focusing was achieved by focusing the laser on the target material. This target material is placed with
... Show Moreيعد علم التدريب الرياضي الحديث عملية تربوية علمية مبنية على اسس صحيحة هدفها وصول اللاعبين الى التكامل في الاداء الفني وهذا يتم عن طريق التأثير المنظم والدقيق بواسطة استعمال التمارين البدنية التي تحدث تغيرات خاصة في عمل اعضاء واجهزة جسم الرياضي والتي بدورها تؤدي الى رفع كفاءة الاعضاء والاجهزة لتحقيق الانجازات الرياضية العالية ولقد استعملت الباحثتان اسلوب حديث من اساليب التدريب الرياضي من اجل تطوير تحم
... Show MoreMultiple eliminations (de-multiple) are one of seismic processing steps to remove their effects and delineate the correct primary refractors. Using normal move out to flatten primaries is the way to eliminate multiples through transforming these data to frequency-wavenumber domain. The flatten primaries are aligned with zero axis of the frequency-wavenumber domain and any other reflection types (multiples and random noise) are distributed elsewhere. Dip-filter is applied to pass the aligned data and reject others will separate primaries from multiple after transforming the data back from frequency-wavenumber domain to time-distance domain. For that, a suggested name for this technique as normal move out- frequency-wavenumber domain
... Show MoreBackground: Ostеoporosis is a systеmic disеasе of thе bonе that is charactеrizеd by rеducеd bonе mass, which lеads to incrеasеd bonе fragility and fracturеparticularly in postmеnopausal womеn.Thе aims of study was toеvaluatе thе rеlationship bеtwееn mandibular radiomorphomеtric indicеs obtainеd on digital panoramic radiographswith thе bonе minеral dеnsitiеs of thе lumbar spinееvaluatеd using dual-еnеrgy X-ray absorptiomеtry (DXA) scan, in a population of ostеoporotic and non-ostеoporotic fеmalеs. Matеrials and mеthods: In panoramic imagеs obtainеd from 60 fеmalе individuals dividеd еq
... Show More