In this work, the surface of the telescope’s mirror is cleaned using an atmospheric-pressure radio frequency plasma jet (APRFPJ), which is generated by Argon gas between two coaxial metal electrodes. The RF power supply is set to 2 MHz frequencies with three different power levels: 20, 50, and 80 W. Carbon, that has adhered to the surface, can be effectively removed using the plasma cleaning technique, which also modifies any residual bonds. The cleaned surface was clearly distinguished using an optical emission spectroscopy (OES) technique and a water contact angle (WCA) analyzer for the activation property on their surfaces. The sample showed a super hydrophilic surface at an angle of 1° after 2.5 minutes of plasma tre

A Raman spectroscopy method was optimised to examine the chemical changes of aspirin tablets after interaction with helium temperatures. Several aspirin tablets were exposed to plasma-assisted desorption ionisation flame for different times (10, 30, 50, 60, 180 and 300s) and then analysed by Raman spectroscopy using optimal conditions. The changes in chemistry between exposed and fresh (without exposure to plasma) tablets were compared. The vibrational peaks of the aspirin molecule in the Raman spectrum were identified by checking the peak position. The results showed clear spectra with increases in intensity of vibrational peaks until 30s, whereas no spectra were measured for the exposed tablets to plasma flame after 50s. It can, the

Background: Thalassemia is characterized by the decrease or absence of the synthesis of one or more globin chains of hemoglobin. Thalassemia is distributed worldwide and is characterized by; regular blood transfusion which is creating alloimmunization to erythrocyte antigens is one of the major complications of regular blood transfusions in thalassemia, particularly in patients who are chronically transfused.Objectives: The aims of this study are to understand the immune system profile as the triggering factor for thalassemia.Methods: Thirty patients aging between one year and four months and twenty two years, twenty two of them were boys and eight were girls. Twenty nine patients, their parents are relative except one and studied in the

This study proposes a mathematical approach and numerical experiment for a simple solution of cardiac blood flow to the heart's blood vessels. A mathematical model of human blood flow through arterial branches was studied and calculated using the Navier-Stokes partial differential equation with finite element analysis (FEA) approach. Furthermore, FEA is applied to the steady flow of two-dimensional viscous liquids through different geometries. The validity of the computational method is determined by comparing numerical experiments with the results of the analysis of different functions. Numerical analysis showed that the highest blood flow velocity of 1.22 cm/s occurred in the center of the vessel which tends to be laminar and is influe

Critical buckling temperature of laminated plate under thermal load varied linearly along the thickness, is developed using a higher-order shape function which depends on a parameter ‘‘m’’, which is improved to obtain results for thin and thick plates. Laminated plates’ equations of motion are obtained using virtual work principle and solved for simply supported boundary conditions. Angle and cross laminates thermal buckled mode shapes with different E1/E2 proportion, number of plies, (α2/α1) proportion, aspect ratios, are investigated. It is observed that this shape function gives thermal buckling for thin and thick plates but with m = 0.05 that agree well with other theories and linear distribution of temperature giv

This study investigates the possibility of using waste plastic as one of the components of expired lead-acid batteries to produce lightweight concrete. Different percentages of lead-acid battery plastic were used in the production of lightweight concrete. The replacements were (70, 80 and 100%) by volume of the fine and coarse aggregate. Results demonstrated that a reduction of approximately 23.6% to 35% in the wet density was observed when replacement of 70% to 100% of the natural aggregate by lead-acid battery plastic. Also, the compressive strength decreased slightly with the increase in plastic content at different curing ages of 7, 28, 60, 90, 120 days. The lowest value of compressive strength was (20.7 MPa) for (wa

Mortar of ordinary Portland cement was blended with cockles shell
powder at different weight ratios to investigate the effect of powder
admixture on their strength and thermal conductivity. Results showed
that addition of cockles shell powder at 50% of mortar weight
improves hardness and compressive strength notably and reduces the
thermal conductivity of the end product. Results suggest the
possibility to incorporate cockles shell powders as constituents in
cement mortars for construction and plastering applications.