In the current study, CuAl0.7In0.3Te2 thin films with 400 nm thickness were deposited on glass substrates using thermal evaporation technique. The films were annealed at various annealing temperatures of (473,573,673 and 773) K. Furthermore, the films were characterized by X-ray Diffraction spectroscopy (XRD), field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM), and Ultra violet-visible (UV–vis). XRD patterns confirm that the films exhibit chalcopyrite structure and the predominant diffraction peak is oriented at (112). The grain size and surface roughness of the annealed films have been reported. Optical properties for the synthesized films including, absorbance, transmittance, dielectric constant, and refr

NiO0.99Cu0.01 films have been deposited using thermal evaporation
technique on glass substrates under vacuum 10-5mbar. The thickness
of the films was 220nm. The as -deposited films were annealed to
different annealing temperatures (373, 423, and 473) K under
vacuum 10-3mbar for 1 h. The structural properties of the films were
examined using X-ray diffraction (XRD). The results show that no
clear diffraction peaks in the range 2θ= (20-50)o for the as deposited
films. On the other hand, by annealing the films to 423K in vacuum
for 1 h, a weak reflection peak attributable to cubic NiO was
detected. On heating the films at 473K for 1 h, this peak was
observed to be stronger. The most intense peak is at 2θ = 37

Transparent thin films of CdO:Ce has been deposited on to glass and silicon substrates by spray pyrolysis technique for various concentrations of cerium (2, 4, and 6 Vol.%). CdO:Ce films were characterized using different techniques such as X-ray diffraction (XRD), atomic force microscopy(AFM) and optical properties. XRD analysis show that CdO films exhibit cubic crystal structure with (1 1 1) preferred orientation and the intensity of the peak increases with increasing's of Ce contain when deposited films on glass substrate, while for silicon substrate, the intensity of peaks decreases, the results reveal that the grain size of the prepared thin film is approximately (73.75-109.88) nm various with increased of cerium content. With a sur

Nano-structural of vanadium pentoxide (V2O5) thin films were
deposited by chemical spray pyrolysis technique (CSPT). Nd and Ce
doped vanadium oxide films were prepared, adding Neodymium
chloride (NdCl3) and ceric sulfate (Ce(SO4)2) of 3% in separate
solution. These precursor solutions were used to deposit un-doped
V2O5 and doped with Nd and Ce films on the p-type Si (111) and
glass substrate at 250°C. The structural, optical and electrical
properties were investigated. The X-ray diffraction study revealed a
polycrystalline nature of the orthorhombic structure with the
preferred orientation of (010) with nano-grains. Atomic force
microscopy (AFM) was used to characterize the morphology of the
films. Un-do

Objective: To diagnose the function of natural biomolecules in the biological reduction of metal salts during nanoparticle synthesis.Study Design: Experimental studyPlace and Duration of Study: This study was conducted at the College of Education for Pure Sciences/Ibn Al- Haitham at the University of Baghdad from 1st January 2024 to 31st March 2025. Methods: Capsicum plant extract was used and treated with a readily available inorganic salt (CaSO4 2H2O). It was used as a basic material to obtain particles.Results: Calcium peroxide nanoparticles in the form of a yellowish-white powder were confirmed by using, UV, XRD, SEM, TEM, AFM, and EDX, confirmed that the compound is calcium peroxide nanoparticles with an average nano size of 31

In this study, gold nanoparticle samples were prepared by the chemical reduction method (seed-growth) with 4 ratios (10, 12, 15 and 18) ml of seed, and the growth was stationary at 40 ml. The optical and structural properties of these samples were studied. The 18 ml seed sample showed the highest absorbance. The X- ray diffraction (XRD) patterns of these samples showed clear peaks at (38.25^o, 44.5^o, 64.4^o, and 77.95^o). The UV-visible showed that the absorbance of all the samples was in the same range as the standard AuNPs. The field emission-scanning electron microscope (FE-SEM) showed the shape of AuNPs as nanorods and the particle size between 30-50 nm. Rhodamine-610 (RhB) was prepared at 10<

Objective: To diagnose the function of natural biomolecules in the biological reduction of metal salts during nanoparticle synthesis.Study Design: Experimental studyPlace and Duration of Study: This study was conducted at the College of Education for Pure Sciences/Ibn Al- Haitham at the University of Baghdad from 1st January 2024 to 31st March 2025. Methods: Capsicum plant extract was used and treated with a readily available inorganic salt (CaSO4 2H2O). It was used as a basic material to obtain particles.Results: Calcium peroxide nanoparticles in the form of a yellowish-white powder were confirmed by using, UV, XRD, SEM, TEM, AFM, and EDX, confirmed that the compound is calcium peroxide nanoparticles with an average nano size of 31

Background: It is well-known that silicon oil (SO) injection into the vitreous cavity after pars plana vitrectomy is usually associated with high intraocular pressure.

Objectives: To determine the influence of silicon oil (SO) removal on IOP level after pars plana vitrectomy for spontaneous rhegmatogenous retinal detachment (RRD)

Subjects and Methods: A prospective study was conducted at Ibn Al-Haitham eye teaching hospital, Baghdad- Iraq. Intraocular pressure (IOP) was measured pre and post SO removal in patients who have underwent retinal detachment surgery with SO injection of 1000 centistokes (cSt) viscosity. Baseline IOP was measured for all the patient before the SO

Background: Ulcerative colitis disease is a chronic inflammatory condition that affects the gastrointestinal tract. In regulation of this inflammatory process, Interleukin-6, C-reactive proteins and albumin have a major role. Overproduction of IL-6 by immunocompetent cells contributes to activate the liver to produce CRP, transudation of plasma albumin and development of the inflammatory condition. Elevated levels of IL-6 in saliva could be expected, because the saliva-producing cells are part of the digestive system. The purpose of this study was to assess salivary IL-6, CRP and albumin in ulcerative colitis patients in relation to oral findings. Materials and methods: Forty eight saliva specimens collected from three groups of subjects (s