Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.
Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

The dielectric constant of most polymers is very low; the addition of TiO2 particles into the polymers provides an attractive and promising way to reach a high dielectric constant. Polymer-based materials with a high dielectric constant show great potential for energy storage applications. Four samples were prepared, one of them was polyurethane (PU) and the other were PU with different weight percent (wt %) of TiO2 (0.1, 0.2, 0.3) powder AFM test was used to distinguish the nanoparticles. The result shows that the most shape of these nanoparticles are spherical and the roughness average is 0.798 nm. The dielectric properties were measured for all samples before and after the exposure to the UV radiation. The result illustrates that the

Iraqi calcium bentonite was activated via acidification to study its structural and electrical properties. The elemental analysis of treated bentonite was determined by using X-ray fluorescence while the unit crystal structure was studied through X-ray diffraction showing disappearance of some fundamental reflections due to the treatment processes. The surface morphology, on the other hand, was studied thoroughly by Scanning Electron microscopy SEM and Atomic Force Microscope AFM showing some fragments of montmorillonite sheets. Furthermore, the electrical properties of bentonite were studied including: The dielectric permittivity, conductivity, tangent loss factor, and impedance with range of frequency (0.1-1000 KHz) at different temperatu

Background: During the COVID-19 outbreak, the number of patients who have developed acute coronary syndromes (ACS) has soared rapidly, cardiovascular disease and mortality are influenced by the elevated inflammatory biomarkers. The aim of this study is to compare inflammatory markers between patients with ACS who hadn’t previously had COVID-19 and those who’d be infected within the preceding three months; as well as, evaluating the effect of statins on inflammatory biomarkers.

Methods: This is a comparative cross-sectional study of 42 patients who presented with ACS and had previously had COVID-19 and 48 patient who had never had CO

Cleft / palate is one of the common congenital deformities in craniofacial region, associated with different types of dental anomalies like (Tooth agenesis, impaction, and supernumerary teeth) with marked changes in palatal dimensions. This study aimed to determine the prevalence of teeth agenesis and dental anomalies in cleft lip/palate patients using CBCT, and to compare the palatal dimension of cleft group with control subjects. Twenty-eight cleft cases collected during the period from 2015 to 2022, CBCT images evaluated, the study sample classified into two groups (14 bilateral and 14 unilateral cleft lip/palate) and the non-cleft control group (14 CBCT images). The presence of dental anomalies was assessed in relation to clef

Cadmium sulphide CdS films with 200 nm have been prepared by thermal evaporation technique on glass substrate at substrate room temperature under vacuum of 10^-5mbar.In this paper, the effect of Dielectric Barrier Discharge plasma on the optical properties of the CdS film. The prepared films were exposed to different time intervals (0, 3, 5, 8) min. For every sample, the Absorption A, absorption coefficient α , energy gap Eg ,extinction coefficient K and dielectric constant ε were studied. It is found that the energy gap were decreased with exposure time, and absorption , Absorption coefficient, refractive index, extinction coefficient,  dielectric constant increased with time of exposure to the plasma. Our study conside

The acidity of spent lubricant was treated using sodium hydroxide solution. The effect of three variables on the treatment have been studied . These are mixing time rangingfrom 5-35 minutes, NaOH to lubricant weight ratio ranging from  0.25-1.25 and weight percentage  of NaOH ranging from  2-6 % .

The experimental design of Box-Wilson method is adopted to find a useful relationship between the three controllable variables and the lowering in the acidity of the spent lubricant. Then the effective variables and interactions are identified using the statistical analysis(F-test) of  three variable fractional design. The mathematical model is well represented  by a second order polynomial.

By