This research work involves the preparation of nano activated carbonand macro activated carbon from corn seeds with a various mixing ratio ofpotassium hydroxide (1:0, 1:0.2, 1:0.4, 1:0.6, 1:0.8 and 1:1) % using thermaland micro radiation carbonization to identify the best mixing ratio. At studyto confirmed that the efficiency and effectiveness of the prepared of activatedcarbon samples increase when ratio potassium hydroxide increase with athermal and micro radiation carbonization was used. The study of samplesexternal surface area was performed via studying the adsorption of methyleneblue from their aqueous solution, also measured the internal surface area wasperformed via studying the adsorption of iodine from their aqueous solution.Measu

Polyaniline Multi wall Carbon nanotube (PANI/MWCNTs) nanocomposite thin films have been prepared by Plasma jet polymerization at low frequency on glass substrate with preliminary deposited aluminum electrodes to form Al/PANI-MWCNT/Al surface-type capacitive humidity sensors, the gap between the electrodes about 50 μm and the MWCNTs weight concentration varied between 0, 1, 2, 3, 4%. The diameter of the MWCNTs was in the range of 8-15 nm and the length 10-55 μm. The capacitance-humidity relationships of the sensors were investigated at humidity levels from 35 to 90% RH. The electrical properties showed that the capacity increased with increasing relative humidity, and that the sensitivity of the sensor increases with the increase of the

In this paper activated carbon adsorbents produced from waste tires by chemical activation methods and application of microwave assisted KOH activation. The influence of radiation time, radiation power, and impregnation ratio on the yield and oil removal which is one of the major environmental issues nowadays and considered persistent environmental contaminants and many of them are suspected of being carcinogenic. Based on Box-Wilson central composite design, polynomial models were developed to correlate the process variables to the two responses. From the analysis of variance the significant variables on each response were identified.  Optimum conditions of 4 min radiation time, 700 W radiation power and 0.5 g/g impregnation ratio

One of the most important techniques for preparing nanoparticle material is Pulsed Laser Ablation in Liquid technique (PLAL). Carbon nanoparticles were prepared using PLAL, and the carbon target was immersed in Ultrapure water (UPW) then irradiated with Q-switched Nd:YAG laser (1064 nm) and six ns pulse duration. In this process, an Nd:YAG laser beam was focused near the carbon surface. Nanoparticles synthesized using laser irradiation were studied by observing the effects of varying incident laser pulse intensities (250, 500, 750, 1000) mJ on the particle size (20.52, 36.97, 48.72, and 61.53) nm, respectively. In addition, nanoparticles were characterized by means of the Atomic Force Microscopy (AFM) test, pH easurement

Expired drug Metoclopramide was investigated as an antibacterial corrosion inhibitor for carbon steel in 0.5M H₃PO₄ solution using the electrochemical method at 30^oC and 60^oC. The results showed that this drug is an efficient inhibitor for carbon steel and the efficiency reached to 82.244 % for 175 ppm at 30^oC and 76.146% for 225 ppm at 60^oC. The adsorption of drug on carbon steel surface follows Langmuir adsorption isotherm with small values of adsorption-desorption constant. The polarization plots revealed that Metoclopramide acts as mixed-type inhibitor. Some parameters of inhibition process were calculated and discussed. The surface morphology of the carbon steel speci

New Schiff base ligand (E)-6-(2-(4-(dimethylamino)benzylideneamino)-2-(4-hydroxyphenyl)acetamido)-3,3- dimethyl-7-oxo-4-thia-1- azabicyclo[3.2.0]heptane-2-carboxylic acid = (HL) was synthesized via condensation of Amoxicillin and 4(dimethylamino)benzaldehyde in methanol. Figure -1 Polydentate mixed ligand complexes were obtained from 1:1:2 molar ratio reactions with metal ions and HL, 2NA on reaction with MCl2 .nH2O salt yields complexes corresponding to the formulas [M(L)(NA)2Cl],where M=Fe(II),Co(II),Ni(II),Cu(II),and Zn(II), A=nicotinamide .

The (E)-4-chloro-N-(2-(dimethylamino)ethyl)-5-((8-hydroxy quinolin-5-yl)diazenyl)-2-methoxybenzamide azo ligand (L) has been synthesized through the reaction of diazonium salt for 5-amino-4-chloro-N-(2-(dimethylamino) ethyl)-2-methoxybenzamide with 8-hydroxyquinoline and identified azo ligand (L) using spectroscopic studies (FTIR, UV-Vis, 1H and 13CNMR, mass), and micro-elemental analysis (C.H.N). Metal chelates of Co(II), Ni(II), Cu(II), as well as Zn(II) have been completed as well as characterized using mass spectra, flame atomic absorption, elemental analysis (C.H.N), infrared, UV-Vis spectroscopy, as well as conductivity, magnetic measurements. The metal-to-ligand ratio in all complexes, as determined by analytical data, was 1:2 and ex