Spider veins are a common aesthetic problem mainly in females , the conventional method of treatment is by microsclerotherapy (injections) but laser therapy has become increasingly efficacious and a convenient method for treatment. The present study was performed to investigate the effectiveness and safety of pulsed diode laser (810nm) by doing thermal photocoagulation. Ten patients with lower limbs spider veins were included in this prospective study. They were treated with a repetitive pulsed diode laser in non contact technique using the following laser parameters (wave length 810nm,power 1 W ,pulse duration 0.1 s., pulse interval 0.5 s, spot diameter 4mm ,power density 7.9 W/cm2). Laser therapy was performed on day zero and day fourteen. Clinical assessments were carried out before laser therapy and immediately after the first laser therapy, after 2 weeks, 4 weeks, and 6 weeks. The procedure was performed without using any type of anesthesia. Results showed that there was a remarkable improvement for all patients after the first treatment and after the second treatment. Only six patients showed a complete disappearance of the spider veins with absent peroperative and postoperative pain and complications, within short operative time in comparison with the microsclerotherapy. So the repetitive pulsed diode laser therapy (810nm) is an effective and safe treatment option for lower limbs spider veins. It's recommended that larger numbers of cases to be done to allow for a proper statistical analysis and a longer follow up period to assess the recurrence rate.
Thin films of (CdO)x (CuO)1-x (where x = 0.0, 0.2, 0.3, 0.4 and 0.5) were prepared by the pulsed laser deposition. The CuO addition caused an increase in diffraction peaks intensity at (111) and a decrease in diffraction peaks intensity at (200). As CuO content increases, the band gap increases to a maximum of 3.51 eV, maximum resistivity of 8.251x 104 Ω.cm with mobility of 199.5 cm2 / V.s, when x= 0.5. The results show that the conductivity is ntype when x value was changed in the range (0 to 0.4) but further addition of CuO converted the samples to p-type.
(9)
(10)
(11)
(10)
(67)
(45)
(1)
(1)
(1)
(1)
(2)
(3)
In this work, The effect of annealing treatment at different temperatures (373, 423 and 473) K and chemical treatment with talwen at different immersion time (40, 60 and 80) min on structural and optical properties of the bulk heterojunction (BHJ) blend copper phthalocyanine tetrasulfonic acid tetrasodium salt/poly dioxyethylenethienylene doped with polystyrenesulphonic acid (CuPcTs/PEDOT:PSS) thin films were investigated. The films were fabricated using spin coating technique. X-ray diffraction (XRD) measurements displayed only one peak at 2θ =4.5o corresponding to (001) direction which has dhkl larger than for standard CuPcTs. The dhkl increase then decrease with increasing annealing temperature and
the time of chemical treatment w