The creation and characterisation of biodegradable blend films based on chitosan and polyvinyl alcohol for application in a range of packaging is described. The compatibility between the chitosan and PVA polymers was good. Composite films had a compact and homogeneous structure, according to the morphology analysis. The mechanical test result of PVA/CH at concentrations 5% showed, that The higher values of TS recorded in sample (p1, with 40 MPa) while the lower values appeared in sample (p9, with 22.09 MPa), the TS decreased gradually as the amount of PVA increased in blend film. While the blend film of pure Chitosan exhibits a poor mechanical strength which makes it a poor candidate for packaging but Blending CH with PVA together improved

Anatomy studies were carried out in the experimental field, College of Agriculture, University of Baghdad to have better understanding of the influence of mulching with black polyethylene sheets, organic manure and chemical fertilizer on the anatomy changes in potato shoot and leaves tissues. Results showed that leaves area, leaves area index and chlorophyll percentage were significantly increased by using mulching and chemical fertilizer by (7463.70 cm2, 3.97, 45.33 SPAD units) respectively. Also this treatment significantly increased total stomata number and in both lower and upper sides of the leaf by (957,721,176) stomata /mm2 respectively. But by using mulching treatment with organic manure significantly increased vessels and sieve t

I n vitro rooting plantlets of three sugarcane genotypes(Co.j.64, Co.j.86 and Missan) were cultured in the field after exposed at different doses of gamma rays (1,2,3,4,) kr. Data of reduction percentage on vegetative growth, roots number, length per plant and their diameter were investigated. Results showed gradual reductions in number of shoots, length and diameter as according to increasing of gamma doses. The reduction percentage in shoot number, length were reached 57.86,70.36 % at 4 kr respectively which have mean number and length per plant reached (9.27 and 55.33 cm) as compared with the control treatment ,While 1 kr caused higher percent in diameter reached 9.69 % with mean of diameter per plant reached 2.57 cm. Mean time , Ge

Background: Various fluids in the oral environment can affect the surface roughness of resin composites. This in vitro study was conducted to determine the influence of the mouth rinses on surface roughness of two methacrylate-based resin (nanofilled and packable composite) and siloraine-based resin composites.

Materials and methods: Disc-shaped specimens (12 mm in diameter and 2mm in height) were prepared from three types of composi

Objective: One of the most important practical deficiencies of present denture base materials is fracture, therefore many
attempts have been made to reinforce of the repaired denture base resin. A desirable objective for this service is to obtain
optimum strength for repairs, which can be achieved by making available a good bond between original and repaired
materials.
Methodology: The present study was carried out to evaluate and compare the transverse strength of acrylic specimens
repaired by two different materials (hot-cure and cold-cure acrylic resin). A total of 50 specimens were prepared by hot
(40) repair: (10) by hot with retention bead, (10) by cold with retention bead and (10) repair by hot only, (10) repair

This study was carried out in Plant Tissue Culture Labs, College of Agricultural Engineering Sciences, University of Baghdad from November 2018 to June 2019. Fresh stem cuttings, 5 cm long were selected from 6-month old C-35 Citrange rootstock. Five concentrations of BA (0, 1, 1.5, 2 and 2.5 mg.L-1) were studied and addition of meta-Topolin (mT) at four concentrations (0, 1, 5 and 10 mg.L-1) was also studied to find out its effect individually on shoot number and shoot length in multiplication stage. Rooting media supplemented with four concentrations of IBA (0, 1, 2 and 3 mg.L-1) was also studied to find out its effect on rooting percentage, root number and root length. Results showed that BA as concentration of 2.5mg.L-1 significantly gav

In this work, an experimental research on a low voltage DC magnetron plasma sputtering (0-650) volt is used for coating gold on a glass substrate at a constant pressure of argon gas 0.2 mbar and deposition time of 30 seconds. We focused on the effects of operating conditions for the system such as, electrode separation and sputtering current on coated samples under the influence of magnetic flux. Electron temperature and electrons and ions densities are determined by a cylindrical single Langmuir probe. The results show the sensitivity of electrode separation lead to change the plasma parameters. Furthermore, the surface morphology of gold coated samples at different electrode separation and sputtering current were studied by atomic forc

Background: Ageing is a continuous accumulative ordinary physiological phenomena occurs upon all organs and body structures including saliva by its constituents which can influence the caries process, for that this study was conducted to determine the impact of ageing on selected chemical composition of saliva and their effects on dental caries experience characteristics at different age groups among apparently healthy men. Materials and method: A descriptive comparative study was conducted to compare between three study samples (young, middle and old age adults), thirty male in each study insert, aged (20 years, 40 years and 60 years) respectively. They were selected from private health center in Baghdad - Iraq, from the mid of November