The dispersion of supported Pt and Pt–Ir reforming catalysts have been studied, after treatment with oxidative and reducing atmosphere. Methylcyclohexane dehydrogenation reaction in the absence of hydrogen was used as a test reaction. An attempt was made to relate the behavior of the catalysts upon subject to reaction, to the dispersion of the same type of catalysts upon treatment with similar atmosphere and temperatures which appeared in literature. The total conversion of reaction can be explained by a change in metal dispersion. Thus, methylcyclohexane dehydrogenation reaction appears to be a really “structure sensitive” reaction.

      The toluene yield increases as the oxidation temperature i

Between October and December 2018, 27wounds and burn swab specimens were collected by laboratories at Al-Yarmook hospital, and cultured on Mannitol salt agar. the isolate was subjected to Nd: YAG laser in different power (400mJ, 500mJ, 800mJ and 900mJ). In general the laser showed effect on bacterial growth that reach to complete killing, the statistical analysis showed that there is weak correlation between laser at 400mJ with killed percentage. While in 500mJ its exhibit complete correlation with killing percentage, this correlation was decreased with increasing in power to 800mJ and 900Mj.

In this work, ZnS thin films have been deposited by developed laser deposition technique on glass substrates at room temperature. After deposition process, the films were annealed at different temperatures (200ºC , 300 ºC and 400ºC ) using thermal furnace.The developed technique was used to obtain homogeneous thin films of ZnS depending on vaporization of this semiconductor material by continuous CO2 laser with a simple fan to ensure obtaining homogeneous films. ZnS thin films were annealed at temperature 200ºC, 300 ºC and 400ºC for (20) minute in vacuum environment. Optical properties of ZnS thin film such as absorbance, transmittance, reflectance, optical band gap, refractive index extinction coefficient and absorption coefficien

Orthodontic treatment has two major problems: being lengthy and costly procedure. The present study was designed to evaluate the clinical efficacy of locally injected vitamin D3 Keywords: Orthodontic, Calcitriol, Local injection, OTM (calcitriol) in accelerating orthodontic teeth movement (OTM) and reducing treatment time and cost in humans. The study was performed on 15 Iraqi adult orthodontic patients within the age range 17-28 years, they are randomly allocated into three groups, each of five patients and treated with either 15 pg, 25 pg, or 40 pg/0.2ml calcitriol diluted with 10% dimethylsulfoxide (DMSO). The maxillary arch of every patient was divided into control (right) and experimental (left) sides. In addition to force application,

The aim of this work was to prepare zeolite type 13X from locally available kaolin and to study the effects of using some binding materials through the process of agglomeration of this zeolite. This study was focused on using kaolin binder in different weight percents (10,15,25,35 and 45%).Physical and mechanical properties of the agglomerates such as porosity , apparent density , pore volume, crushing strength , loss on attrition , surface area and finally the adsorption capacity had been measured and evaluated .The preparation step was achieved by mixing the reactants consisting of metakaolin , source of silica as ( sodium trisilicate ) and sodium hydroxide . The conditions was temperature of 70° C and time of mixing as 8, 10,24,34,50

Nitinol (NiTi) is used in many medical applications, including hard tissue replacements, because of its suitable characteristics, including a close elastic modulus to that of bones. Due to the great importance of the mechanical properties of this material in tissue replacements, this work aims to study the hysteresis response in an attempt to explore the ability of the material to remember its previous mechanical state in addition to its ability to withstand stress and to obtain the optimal dimensions and specifications for the manufacturer of NiTi actuators. Stress-strain examination is done in a computational way using a mutable Lagoudas MATLAB code for various coil radii, environment temperatures, and coil lengths. The computational m

Copper doped Zinc oxide and (n-ZnO / p-Si and n-ZnO: Cu / p-Si) thin films thru thickness (400±20) nm were deposited by thermal evaporation technique onto two substrates. The influence of different Cu percentages (1%,3% and 5%) on ZnO thin film besides hetero junction (ZnO / Si) characteristics were investigated, with X-ray diffractions examination supports ZnO films were poly crystal then hexagonal structural per crystallite size increase from (22.34 to 28.09) nm with increasing Cu ratio. The optical properties display exceptional optically absorptive for 5% Cu dopant with reduced for optically gaps since 3.1 toward 2.7 eV. Hall Effect measurements presented with all films prepared pure and doped have n-types conductive, with a ma

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K