In this work, (CdO)1-x (CoO)x thin films were prepared on glass slides by laser-induced plasma using Nd:YAG laser with (λ=1064 nm) and duration (9 ns) at different laser energies (200-500 mJ) with ratio (x=0.5), The influence of laser energy on structural and optical properties has been studied. XRD patterns show the films have a structure of polycrystalline wurtzite. As for AFM tests results for the topography of the surface of the film, where the results showed that the grain size and the average roughness increase with increasing laser energy. The optical properties of all films were also studied and the results showed that the absorption coefficient for within the wavelength range (280-1100 nm), The value of the optical power gap fo

Thin films of (CdO)x (CuO)1-x (where x = 0.0, 0.2, 0.3, 0.4 and 0.5) were prepared by the pulsed laser deposition. The CuO addition caused an increase in diffraction peaks intensity at (111) and a decrease in diffraction peaks intensity at (200). As CuO content increases, the band gap increases to a maximum of 3.51 eV, maximum resistivity of 8.251x 104 Ω.cm with mobility of 199.5 cm2 / V.s, when x= 0.5. The results show that the conductivity is ntype when x value was changed in the range (0 to 0.4) but further addition of CuO converted the samples to p-type.

Zinc oxide (ZnO) nanostructures were synthesized through the hydrothermal method at various conditions growth times (6,7 and 8 hrs.) and a growth temperature (70, 90, and 100 ºC). The prepared ZnO nanostructure samples were described using scanning electron microscopy (SEM) and X-ray diffractometer to distinguish their surface morphologies and crystal structures. The ZnO samples were confirmed to have the same crystal type, with different densities and dimensions (diameter and length). The obtained ZnO nanostructures were used to manufacture gas sensors for NO2 gas detection. Sensing characteristics for the fabricated sensor to NO2 gas were examined at different operating temperatures (180, 200, 220, and 240) ºC with a low gas concentrati

Kamel, S.H., R.F. Al-Jassani and H.A. Al-Shammari. 2022. Effects of Pseudomonas fluorescens, Bacillus thuringiensis tenebrionis Isolates and Biologically Synthesized Silver Nanoparticles on Cellulase Enzyme Activity in Workers' Digestive System of the Termite Microcerotermes diversus Silv. Arab Journal of Plant Protection, 40(4): 315-324. https://doi.org/10.22268/AJPP-40.4.315324 The purpose of this study was to investigate the effect of different bacterial isolates of P. fluorescens and B. t. tenebrionis and silver nanoparticles on the activity of the cellulase enzyme in termites' middle digestive system and its role in glucose release by treating cellulose media with bacterial strains and nanoparticles. Ultraviolet spectroscopy re

The work of this paper is an investigation to improve the condenser performance of the automobile air conditioning system by enhancing the air-side heat transfer from the condenser through the use of an air guide net installed in front of the condenser face which is basically an aluminum plate having a circular entrance shape for the air passage.  The A/C system was examined under two types of test. The first test was conducted the air guide net, while the second was done with the air guide net. The performances of the A/C system under these tests were compared. For the second type of test, the experiment was carried out with three different size of air guide net, three different circular diameters (2, 3 and 3.5 cm) a

Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

Background: Psychological stress is considered the major etiological factor precipitating myofacial pain and temporomandibular disorders.It is known that stress induce various adaptational responses of physiologic systems. The process includes increase in the activity of the hypothalamic-pituitary-adrenal axis which promotes cortisol secretion. Salivary cortisol has been used as a measure of free circulating cortisol levels.The use of salivary biomarkers has gained increased popularity since collecting samples is non-invasive and painless. The aim of thisstudy was to evaluate the level of cortisol in saliva among sample of university students having myofacial pain, during the final exam period and whether this finding could have a significa

This study was conducted at the poultry research station to the office of Agricultural Research / Ministry of Agriculture / during the period 4/1/2016 to 5/5/2016 and 336 one-day-old Ross308 chicks were used, and fed on diets provided with dried dill (Anethum gravelens) at levels 0.4, 0.6 and 0.8% for treatments D2, D3 and D4, respectively, and they were compared with the control treatment D1. Each treatment included three replicates in each replicate contain 28 birds, in order to study the effect of adding different levels of dried dill plant on the productive performance and some characteristics of the carcass for broilers. The results showed a significant increase (p<0.05) in the average body weight at 5 weeks of age for the treatments (

The current study was conducted to determine the sensitivity of some pathogenic bacterial isolates isolated from wounds and burns water toward the disposer of the Yas Rue tested five crude bacterial isolates isolated from wounds and burns which these isolates sensitive to aqueous extract crude