In the present study, MIG welding is carried out on low carbon steel type (AISI 1015) by using electrode ER308L of 1.5mm diameter with direct current straight polarity (DCSP). The joint geometry is of a single V-butt joint with one pass welding stroke for different plate thicknesses of 6, 8, and 10 mm. In welding experiments, AISI 1015 plates with dimensions of 200×100mm and edge angle of 60^o from both sides are utilized. In this work, three main parameters related to MIG welding process are investigated, which are welding current, welding speed, heat input and plate thickness, and to achieve that three groups of plates are employed each one consists of three plates. The results indicate that increasing the weld heat input (t

Background: Recently, Poly propylene fibers with and without plasma treatment have been used to reinforce heat cure denture base acrylic but, so far some of properties like tensile strength , wettability and wear resistance not evaluated yet, the aim of the study is to clarify the influence of incorporation of treated and untreated fibers on these properties. Materials and methods: Twenty one specimens were fabricated for every tested property(tensile strength, wear resistance and wettability) that classified into three groups(control, untreated poly propylene fibers reinforced specimens and Oxygen plasma treated group)and for each test sevens amples were used(n=7). Tensile strength was tested using Instron universal testing machine, wear

Carnosol, a phenolic diterpene, is one of the effective anticancer agents naturally occurring in rosemary, sage, parsley, and oregano. The chemoresistance problem increased with the routinely used chemotherapy. Therefore, the efforts to find a substitute with safe and low cost have become crucial worldwide. The current study attempts to inspect the anticancer molecular mechanisms of Carnosol on modulating up- and down- regulation of multiple genetic carcinogenesis pathways. The cytotoxicity of Carnosol on Hela cells was evaluated by MTS assay. Flow cytometry was used to assess apoptosis and cell cycle arrest. The apoptotic morphological changes were obvious by dual apoptosis assay. The differential gene expression after treatment wi

A thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.

The optical energy gap(Eopt) and the width of the tails of localized states in the band gap (?E) for Se:2%Sb thin films prepared by thermal co-evaporation method as a function of annealing temperature are studied in the photon energy range ( 1 to 5.4)eV.Se2%Sb film was found to be indirect transition with energy gap of (1.973,2.077, 2.096, 2.17) eV at annealing temperature (295,370,445,520)K respectively. The Eopt and ?E of Se:2%Sb films as a function of annealing temperature showed an increase in Eopt and a decrease in ?E with increasing the annealing temperature. This behavior may be related to structural defects and dangling bonds.

The aim of this research is to determine the uranium concentration and its distribution in many sheep organs that live in different region of Iraq. The uranium concentration in tissue samples is measured by using fission tracks registration in CR-39 detector that caused by the bombardment of U235 with thermal neutrons from (241Am-Be) neutron source of thermal flux (5x 103 n.cm-2. s-1). The results show that the maximum uranium concentration in bronchiole tissues of the animals was found in Karbala city (3.706ppm) while the minimum concentration (0.127 ppm) was found in Al-Faluja city, also the same result in lung tissue the maximum value was found in Karbala city (2.313ppm) and the minimum concentration in Al Fluja (0.082). Otherwise,

A nanocrystalline CdS thin film with 100 nm thickness has been prepared by thermal evaporation technique on glass substrate with substrate temperature of about 423 K. The films annealed under vacuum at different annealing temperature 473, 523 and 573 K. The X-ray diffraction studies show that CdS thin films have a hexagonal polycrystalline structure with preferred orientation at (002) direction. Our investigation showed the grain size of thin films increased from 9.1 to 18.9 nm with increasing the annealing temperature. The optical measurements showed that CdS thin films have direct energy band gap, which decreases with increasing the annealing temperature within the range 3.2- 2.85 eV. The absorbance edge is blue shifted. The absorption

 In this research, analytical study for simulating a Fabry-Perot bistable etalon (F-P cavity) filled with a dispersive optimized nonlinear optical material (Kerr type) such as semiconductors Indium Antimonide (InSb). An optimization procedure using reflective (~85%) InSb etalon (~50µm) thick is described. For this etalon with a (50 µm) spot diameter beam, the minimum switching power is (~0.078 mW) and switching time is (~150 ns), leading to a switching energy of (~11.77 pJ) for this device. Also, the main role played by the temperature to change the etalon characteristic from nonlinear to linear dynamics.

A metal mandrel was designed for manufacturing the cathodes of high power electron tube ( Tetrode ) used in broadcasting transmitting tubes type TH558 and CQS200.The cathodes were manufactured in the present work from thoriated tungsten wires ( 2? ThO2- W) with different diameters .These cathodes were carbonized in sequences of processes to determine the carbonization parameters (temperature, pressure, time, current and voltage).Then the carbonized cathodes dimension were accurately measured to determine the deviation due to the high temperature distortion effect at about 1800°C .the distorted cathodes due to the carbonization process was treated when it was subjected inside the vacuum chamber and heat treated again .The carbonized cat

This research seeks the effects of dubbed Turkish TV series on Iraqi audiences. The chosen sample is about 600 Iraqi students at Baghdad and al-Anbar Universities. This study consists of four sections: section one deals with the theoretical framework of the study. Section two studies the dubbed Turkish TV series. The third section explores the role of mass media in forming tendencies, and the last section seeks the field study by analyzing the tendencies if Iraqi viewers of these series.
The goal of this study is to know the role these series played in affecting the behavior and attitudes of Iraqi people and how it can change their morals.
The research ends with the number of results like the negative effect of these series on the