Adsorption is one of the most important technologies for the treatment of polluted water from dyes. Theaim of this study is to use a low-cost adsorbent for this purpose. A novel and economical adsorbent was used to remove methyl violet dye (MV) from aqueous solutions. This adsorbent was prepared from bean peel, which is an agricultural waste. Batch adsorption experiments were conducted to study the ability of the bean peel adsorbent (BPA) to remove the methyl violet (MV) dye. The effects of different variables, such as weight of the adsorbent, pH of the MV solution, initial concentration of MV, contact time and temperature, on the adsorption behaviour were studied. It was found experimentally that the time required to achieve equilibrium was 120 min for all dye concentrations (10-50 mg/l). The BPA was characterised using Fourier transform infrared (FTIR)before and after adsorption of the MV dye. Langmuir, Freundlich and Temkin isotherm models were used to analyse the experimental isotherm data. The Freundlich isotherm gives a better fit than the other isotherm models. The adsorption kinetic data were tested using pseudo-first-order and pseudo–second-order models. Additionally, the intraparticle diffusion model was used to investigate the mechanism of the adsorption process. It was found that boundary layer diffusion (external mass transfer) is the rate-determining step. The thermodynamic parameters, including ΔH, ΔS and ΔG, were investigated at different temperatures (298, 313 and 323 K) and concentrations (5, 10, 20 and 30 mg/l) to understand the nature of the adsorption process. The thermodynamic study indicates that the adsorption of MV dye onto BPA is physical, exothermic and spontaneous in nature.
(1)
CdS and CdS:Sn thin films were successfully deposited on glass
substrates by spray pyrolysis method. The films were grown at
substrate temperatures 300 C°. The effects of Sn concentration on the
structural and optical properties were studied.
The XRD profiles showed that the films are polycrystalline with
hexagonal structure grown preferentially along the (002) axis. The
optical studies exhibit direct allowed transition. Energy band gap
vary from 3.2 to 2.7 eV.
(1)
This research presents a method of using MATLAB in analyzing a nonhomogeneous soil (Gibson-type) by
estimating the displacements and stresses under the strip footing during applied incremental loading
sequences. This paper presents a two-dimensional finite element method. In this method, the soil is divided into a number of triangle elements. A model soil (Gibson-type) with linearly increasing modulus of elasticity with depth is presented. The influences of modulus of elasticity, incremental loading, width of footing, and depth of footing are considered in this paper. The results are compared with authors' conclusions of previous studies.
(1)
This work was conducted to study limestone rock wettability alteration to enhance oil recovery by flooding using different Nano silica (NS) sizes suspended in saline water and compared with flooding solution of polyethylene glycol (PEG) polymer and sodium dodecyl sulfate (SDS) surfactant, the stability of nanofluids measured by zeta potential. In the flooding system, the secondary recovery by silica nanofluids (0.01 wt. % NS concentration) achieved an oil recovery of 35vol. % and 26.08 vol. % for 10, 52 nm after primary recovery respectively, while PEG polymer and SDS surfactant achieved oil recovery of 5 vol. % and 10 vol. % only respectively. The stability of pressure difference approved that silica nanoparticle never causes any p
... Show More
(2)
This paper studies the behavior of axially loaded RC columns which are confined with carbon fiber reinforced polymers’ sheet (CFRP) and steel jackets (SJ). The study is based on twelve axially loaded RC columns tested up to failure. It is divided into three schemes based on its strengthening type; each scheme has four columns. The main parameters in this study were the compressive strength of the concrete and steel reinforcement ratio. Furthermore, the results of the experimental test showed a substantial enhancement in the column's load-carrying capacity. When compared to the original columns, the CFRP sheet had a significant effect on improving the ductility of the column by increasing the axial deformation by about 59.2 to 95.7
... Show More
(2)
(1)
(2)
(1)
(35)
(35)
This study aims to remove Cd(II) ions from simulated wastewater by using Chlorophyceae algae (CA). Different parameters were studied to show their effects on the biosorption efficiency of CA. These parameters are: the effect of pH 3-7, initial metal ion concentration 20-200 mg/L, sorbent dos-age 0.05-2 g/L, contact time 5-180 min, and agitation speed 100-300 rpm. We found that both the Langmuir and Freundlich models appropriate for characterizing the metal removal process. The biosorption data fit best with the results of the pseudo-second-order kinetic model, demonstrating that the chemisorption process is the dominant mechanism controlling the removal. CA was char-acterized using the scanning electron microscopy test, prior to and post bi
... Show More
(10)
(6)
The Corrosion protection effectiveness of Alimina(Al2O3,50nm)and Zinc oxide (ZnO,30nm) nanoparticales were studied on carbon steel and 316 stainless steel alloys in saline water (3.5%NaCl)at four temperatures: (20,30,40,50 OC)using three electrodes potentiostat. An average corrosion protection efficiencies of 65 %and 80% was achieved using Al2O3 NP's on carbon steel and stainless steel samples respectively, and it seems that no effect of rising temperature on the performances of the coated layers. While ZnO NP'S showed protection efficiency around 65% for the two alloys and little effected by temperature rising on the performanes of the coated layers. The morphology of the coated spesiemses was examined by Atomic force microscope.
(3)
(4)
(3)