This study expands the state of the art in studies that assess torsional retrofit of reinforced concrete (RC) multi-cell box girders with carbon fiber reinforced polymer (CFRP) strips. The torsional behavior of non-damaged and pre-damaged RC multi-cell box girder specimens externally retrofitted by CFRP strips was investigated through a series of laboratory experiments. It was found that retrofitting the pre-damaged specimens with CFRP strips increased the ultimate torsional capacity by more than 50% as compared to the un-damaged specimens subjected to equivalent retrofitting. This indicated that the retrofit has been less effective for the girder specimen that did not develop distortion beforehand as a result of pre-loading. From

This study presents the debonding propagation in single NiTi wire shape memory alloy into linear low-density polyethylene matrix composite the study of using the pull-out test. The aim of this study is to investigate the pull-out tests to check the interfacial strength of the polymer composite in two cases, with activation NiTinol wire and without activation. In this study, shape memory alloy NiTinol wire 2 mm diameter and linear fully annealed straight shape were used. The study involved experimental and finite element analysis and eventually comparison between them. This pull-out test is considered a substantial test because its results have a relation with behavior of smart composite materials. The pull-out test was carried out by a u

Compounds of (ZnO)1-x(SnO 2 ) x were prepared with various proportions of tin oxide (SiO 2) (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) by mixing zinc oxide (ZnO) with highpurity tin oxide and then sintering the mixture in an oven at a temperature of 1000 °C for a period of 1 h. The resulting powders were ground and pressed into tablets of 1 cm diameter and 0.5 cm thickness. The properties of (ZnO) 1-x(SnO 2 ) x composites flms were prepared and studied as sensitive to the diferent gases NO2 and H2 S. Thin flms were prepared from (ZnO) 1-x(SnO 2 ) x via pulsed laser deposition method using glass and single crystal silicon for investigation the morphology and gas sensing properties with a thickness of 150 nm. The morphology examinat

A multistep synthesis was established for the preparation of a new vanillic acid-1, 2, 4-1triazole-3-thiol conjugate (4). Finally, several aromatized aldehydes reacted with compound (4) to produce Schiff bases derivatives (5–11). The purpose of this research is to prepare new vanillic acid derivatives with 1, 2, 4-triazole-3-thiol heterocyclic ring structures and to evaluate their antimicrobial activity in a preliminary assessment. Fourier-transform infrared (FT-IR) and proton nuclear magnetic resonance spectroscopy (¹H-NMR) were used to verify the structures of the newly synthesized compounds. all the final synthesized compounds (

Background: Dental implants act as infrastructure for fixed restoration to look like as a natural tooth. Osseointegration is a biological events and considered as a base for success of dental implant. The aim of this study is to evaluate the bond strength between bone and Ti implant coated with mixture of nano hydroxyapatite-chitosan-collagen compared with Ti implants coated with nano hydroxyapatite implanted in rabbit tibia, after different period of implantation time (two and six weeks) by torque removal test. Material and methods: 36 screws of commercially pure titanium; 8mm in length and 3mm diameter , 18 screws coated with mixture of nano hydroxyapatite-chitosan-collagen and18 screws coated with nano hydroxyapatite by dip coating. St

Poly(ethylene oxide) is a promising material for solid-state lithium batteries due to its safety, ease of processing, and compatibility with lithium. However, conventional linear PEO falls short of practical requirements due to its limited ionic conductivity, a consequence of the high crystallinity of its ethylene oxide chains. This crystallinity hinders the movement of lithium ions, limiting its performance in solid-state battery applications. In this study, we successfully prepared the plasticized solid polymer electrolytes (PSPEs) based on poly(ethylene oxide) (PEO)/ tetracyanoethylene (TCE) complexed with lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) salt and studied the effect of TCE on structural, mechanical, electrical and elec