Polyvinyl alcohol, (PVA) was prepared using polyvinyl acetate emulsion (manufactured by Al-Jihad factory,
That-Al-Sawary Company) as a local raw material. In this investigation, polyvinyl acetate emulsion was converted to
solid form by coagulation the polymer from its emulsion using sodium sulphate salt as coagulant aid, then alcoholyzed
the solid polyvinyl acetate in methanol using sodium hydroxide as catalyst, polyvinyl alcohol produced by this method is
a dry, white to yellow powder.
Three affecting variables on the degree of hydrolysis of PVA were studied, these variable are Catalyst to
polymer weight ratio in the range of 0.01 – 0.06, reaction time in the range of 20 – 90 min, and reaction temperature in
the range of 25 – 50 oC. The effect of degree of hydrolysis of PVA produced on its properties such as water solubility
and degree of polymerization were studied also.
Finally the alcoholysis reaction kinetics were studied to determine the reaction constants such as initial rate
constant and degree of autocatalytic effect of the alcoholysis reaction. It was found that the degree of hydrolysis of
formed polyvinyl alcohol increase with increasing of variables catalyst concentration, reaction time and reaction
temperature, furthermore, the water solubility of PVA increase with increasing degree of hydrolysis up to about 87 %
after this value the solubility is decrease, also the degree of polymerization of PVA decrease with increasing of degree of
hydrolysis up to about 89 %.
(14)
(15)
Background: Dental implants act as infrastructure for fixed restoration to look like as a natural tooth. Osseointegration is a biological events and considered as a base for success of dental implant. The aim of this study is to evaluate the bond strength between bone and Ti implant coated with mixture of nano hydroxyapatite-chitosan-collagen compared with Ti implants coated with nano hydroxyapatite implanted in rabbit tibia, after different period of implantation time (two and six weeks) by torque removal test. Material and methods: 36 screws of commercially pure titanium; 8mm in length and 3mm diameter , 18 screws coated with mixture of nano hydroxyapatite-chitosan-collagen and18 screws coated with nano hydroxyapatite by dip coating. St
... Show More
(6)
(1)
(1)
BACKGROUNDS Nasoalveolar molding (NAM) application is among presurgical management (PSM) techniques used for infants with cleft lip and palate (CLP). It helps to approximate the palatal cleft and to reshape the nasoalveolar complex prior to primary lip repair. This study aimed to explore types of PSM and the dental speciality provision for infants with CLP in Baghdad. The status of NAM usage and surgeons’ perceptions toward NAM usage were assessed. MATERIALS AND METHODS This is a cross-sectional paper-based questionnaire study that collected responses of surgeons perform primary lip and nose repair regarding PSM. The questionnaire was distributed amongst public and private hospitals in Baghdad. Twenty surgeons were enrolled (only those su
... Show More
(3)
(2)
Abstract
The purpose of our study was to develop Dabigatran Etexilate loaded nanostructured lipid carriers (DE-NLCs) using Glyceryl monostearate and Oleic acid as lipid matrix, and to estimate the potential of the developed delivery system to improve oral absorption of low bioavailability drug, different Oleic acid ratios effect on particle size, zeta potential, entrapment efficiency and loading capacity were studied, the optimized DE-NLCs shows a particle size within the nanorange, the zeta potential (ZP) was 33.81±0.73mV with drug entrapment efficiency (EE%) of 92.42±2.31% and a loading capacity (DL%) of 7.69±0.17%. about 92% of drug was released in 24hr in a controlled manner, the ex-vivo intestinal p
... Show More
(18)
(7)
(31)
(30)
Incremental forming is a flexible sheet metal forming process which is performed by utilizing simple tools to locally deform a sheet of metal along a predefined tool path without using of dies. This work presents the single point incremental forming process for producing pyramid geometry and studies the effect of tool geometry, tool diameter, and spindle speed on the residual stresses. The residual stresses were measured by ORIONRKS 6000 test measuring instrument. This instrument was used with four angles of (0º,15º,30º, and 45º) and the average value of residual stresses was determined, the value of the residual stress in the original blanks was (10.626 MPa). The X-ray diffraction technology was used to measure the residual stresses
... Show More
(1)
Two quantitative, environment-friendly and easily monitored assays for Ni (II) and Co (III) ions analysis in different lipstick samples collected from 500-Iraqi dinars stores located in Baghdad were introduced. The study was based on the reaction of nickel (II) ions with dimethylglyoxime (DMG) reagent and the reaction of cobalt (III) ions with 1-nitroso-2-naphthol (NN) reagent to produce colored products. The color change was measured by spectrophotometric method at 565 nm and 430 nm for Ni and Co, respectively, with linear calibration graphs in the concentration range 0.25-100 mg L-1 (Ni) and 0.5-100 mg L-1 (Co) and LOD and LOQ of 0.11 mg L-1 and 0.36 mg L-1 (Ni), and 0.15 mg L-1 an
... Show More
(8)
(5)
This study aims to determine the reasons for the increase in the frequency of sand and dust storms in the Middle East and to identify their sources and mitigate them. A set of climatic data from 60 years (1960–2022) was analyzed. Sand storms in Iraq are a silty sand mature arkose composed of 72.7% sand, 25.1% silt, and 2.19% clay; the clay fraction in dust storms constitutes 70%, with a small amount of silt (20.6%) and sand (9.4%). Dust and sand storms (%) are composed of quartz (49.2, 67.1), feldspar (4.9, 20.9), calcite (38, 5), gypsum (4.8, 0.4), dolomite (0.8, 1.0), and heavy minerals (3.2, 6.6). Increasing temperatures in Iraq, by an average of 2 °C for sixty years, have contributed to an increase in the number of dust storm
... Show More
(66)
(6)
(3)