The crystalline zeolite, namely faujasite type Y with SiO2/Al2O3 mole ratio of 5 was used as raw material for preparation of isomerization catalysts. A 0.5 wt % Pt/HY-zeolite catalyst was prepared by impregnation of the decationized HY-zeolite with chloroplatinic acid. The dectionized HY-zeolite was treated with HCl, HNO3 and HI promoters using different normalities and with different concentrations of Sn, Ni and Ti promoters by impregnation method to obtain acidic and metallic promoters' catalysts, respectively. A 0.5 wt% of Pt was added to above catalysts using impregnation method. Isomerization of n-hexane was carried out at different prepared catalysts. The isomerization temperature varied from 250–325° C over weight hourly space velocity (WHSV) 1.6 h-1. The pressure and hydrogen to feed mole ratio were kept constant at 1bar and 2 mol/mol, respectively. The comparison between the above prepared catalysts shows that the total isomer yield during the process with Sn-Pt /HY- zeolite catalyst was higher than the other catalysts and, reached to 63.95% vol. A 0.5 wt% of W and Zr was added to Sn-Pt/HY-zeolite catalyst by impregnation method to obtain W and Zr co-metal promoters catalysts. Isomerization of n-hexane was investigated using W and Zr co-metal promoters catalyst at the same operating conditions and the yield of isomers reached to 81.14% vol.and 79.07%vol.,respectively.
Cadmium sulfide (CdS) nanocrystalline thin films have been prepared by chemical bath deposition (CBD) technique on commercial glass substrates at 70ºC temperature. Cadmium chloride (CdCl2) as a source of cadmium (Cd), thiourea (CS(NH2)2) as a source of sulfur and ammonia solution (NH4OH) were added to maintain the pH value of the solution at 10. The characterization of thin films was carried out through the structural and optical properties by X-ray diffraction (XRD) and UV-VIS spectroscopy. A UV-VIS optical spectroscopy study was carried out to determine the band gap of the nanocrystalline CdS thin film and it showed a blue shift with respect to the bulk value (from 3.9 - 2.4eV). In present w
... Show More
(1)
(62)
(62)
The V2O5 films were deposited on glass substrates which produce using "radio frequency (RF)"power supply and Argon gas technique. The optical properties were investigated by, UV spectroscopy at "radio frequency" (RF) power ranging from 75 - 150 Watt and gas pressure, (0.03, 0.05 and 0.007 Torr), and substrate temperature (359, 373,473 and 573) K. The UV-Visible analysis shows that the average transmittance of all films in the range 40-65 %. When the thickness has been increased the transhumance was decreased from (65-40) %. The values of energy band gap were lowered from (3.02-2.9 eV) with the increase of thickness the films in relation to an increase in power, The energy gap decreased (2.8 - 2.7) eV with an increase in the pressure and
... Show More
(3)
Abstract: Objectives: To investigate the effect of temperature elevation on the bonding strength of resin cement to the zirconia ceramic using fractional CO2 laser. Background: Fractional CO2 laser is an effective surface treatment of zirconia ceramic, as it increases the bonding strength of zirconia to resin cement. Methods: Thirty sintered zirconia discs (10 mm diameter, 2 mm thickness) were prepared and divided to three groups (N=10) and five diffident pulse durations were used in each group (0.1, 0.5, 1, 5 and 10 ms). Group A was treated with 10 W power setting, group B with 20 W and group C with 30 W. During laser irradiation, temperature elevation measurement was recorded for each specimen. Luting cement was bonded to the treated z
... Show MoreAbstract
The current study aims to study one Firas Al- Himdani's Romeyat poems (320 – 357 AH), he was one of sham poets in the era of the Abbasid as to know the glories of the knight and Arabic poet, whose message led to preserve the honor of the nation and Islam prestige , along with exposing the better one . His message includes Arabic merits and high values in respect of chivalry , encouragement , sacrifice , forgiveness and tolerance in addition to morality and patience .
Background: The formation of white spot lesions around fixed orthodontic attachments is a common complication during and after fixed orthodontic treatment, which hinders the result of a successfully completed orthodontic treatment. The aim of the study was to assess the effectiveness of the Caries Infiltrant (ICON®) on prevention of caries on the smooth enamel surface when applied alone or combined with conventional adhesives. Materials and methods: Seventy eight human premolar enamel discs were randomly assigned to six groups (n=13). The discs were etched and treated with resins of different monomer content forming the following groups: (1)Untreated etched samples served as the negative control, (2) ICON® (DMG), (3) Adper™ S
... Show More
In this work, we study the effect of doping Sn on the structural and optical properties of pure cadmium oxide films at different concentrations of Tin (Sn) (X=0.1,0.3 and 0.5) .The films prepared by using the laser-induced plasma at wavelength of laser 1064 nm and duration 9 ns under pressure reached to 2.5×10-2 mbar. The results of X-ray diffraction tests showed that the all prepared films are polycrystalline. As for the topography of the films surface, it was measured using AFM , where the results showed that the grain size increases with an increase in the percentage of doping in addition to an increase in the average roughness. The optical properties of all films have also been studied through the absorbance s
... Show More
(6)
The present study aimed to investigate the effects of level pH and the growth phases of Coelastrella saipanensis on Chlorophyll a,b, total, and Carotene. The algae were cultured in BG11 media and grown at different pH levels. We measured chlorophyll a, b, total chlorophyll, growth phases, and carotene concentrations. The results showed that at pH 8.5, the measurements of photosynthetic pigments-chlorophyll a, Chlorophyll b, and the total chlorophyll (0.183, 0.268, and 0.433 mg L-1, respectively). The highest values of chlorophyll a (0.185 mg L-1), and b (0.339 mg L-1), and the total chlorophyll (0.492 mg L-1) were recorded in the stationary phase. In addition, the study found that at pH 8.5 and the beginning of the stationary phase,
... Show More
(2)
Objective: To determine the effectiveness of an Intervention Oriented program on the prognosis of Osteopenia among Women at Private clinics in Baghdad City. Methodology: A longitudinal design. A purposive ''non probability'' sample of (25) Women who have bone mineral density (BMD) T- test between (-1 to -2.5). The data are collected through the utilization of a constructed questionnaire and by means of interview with each client who is involved in the study. Each interview takes approximately (20) minutes. Results: The study showed that there is a good improvement in bone density accord after applicatio
(13)
(10)