An investigation was conducted for the determination of the effects of the forming conditions in the production of Gamma Alumina catalyst support on the crushing strength property. Eight variables were studied , they are ;binder content which is the sodium silicate , Solvent content which is the water, speed of mixing , time of mixing, drying temperature , drying time , calcinations temperature and the calcinations time
Design of the experiments was made by using the response Surface method in Minitab 15 software which supply us 90 experiments .
The results of this investigation show that the crushing strength for the dried Gamma alumina extrudate was affected by the drying temperature and the drying time only and there is no interaction effect between the variables studied.
Furthermore, the results show that, the crushing strength for the calcined extrudate was affected by the speed of mixing only and the optimum speed is 900rpm.
The maximum crushing strength of 38.38 after calcinations and 11.865 Kg/mm after drying were obtained
Objective: preparing exercises for the third intensity zone for strength and speed for the legs, and identifying their effect on some physiological and biochemical indicators for (the level of lactic acid concentration, the concentration of sodium bicarbonate, the concentration level of (potassium K+) and (sodium Na+) in the blood, and the number of breathing times (RF) Research methodology: the experimental research method was adopted by designing the experimental and control groups on a sample of Army Sports Club players amounting to (16) players, deliberately selected (100%) from their community using a comprehensive enumeration method, and then divided into two groups of equal number, After determining the tests for physiologica
... Show More
n this work, the effect of gamma rays on blood thinning drugs was studied using the drug (Aspirin), where gamma rays were spread with the drug using a radioactive source (Co60), and 15,000 grams of Aspirin were placed in the device (gamma chamber 900). The drug was subjected to different irradiation doses (5 KGy, 10 KGy, 15 KGy) and the amount of absorption of the drug was observed in the gamma for different doses and the study of x-rays. After confirming the absorption of the drug to radiation, the effect of the drug on blood thinning was calculated using the rat model and compared with the same drug and the same dose but without exposing the drug to radiation and comparing all results with the control group. The way drugs absorbed radiati
... Show More
(2)
(1)
(2)
(1)
Folic acid and multivitamin tablets containing Aspergillus flavus Penicillia spp. and Cladosporia spores were prepared at a compression pressure of 148 MN/m2 and stored at 35°C under different relative humidifies (75,85, and 95)% within air tight containers, to study the effect of storage condition on them, as well as ,the estimation of the microbial level of the raw materials intended to be used in the two kinds of tablets . Result showed that some raw materials derived from natural origin were heavily contaminated with microorganism compared to that of synthetic origin ,the results also indicated the effect of relative humidity , types of fungal spore , and the hygroscopic nature of exicpient upon survival. Multivit
... Show More
Reuse of spent hydrodesulphurization (HDS) of middle petroleum fractions catalyst CoMo/γAl2O3 was accomplished via removal of coke and contaminants such as vanadium, Iron, Nickel, and sulfur. Three processes were adopted; extraction, leaching, decoking. Soluble and insoluble coke was removed. Leaching step used three different solvents (oxalic acid, ammonium peroxydisulfate and oxalic acid + H2O2) in separate in order to remove contaminant metals (V, S, Ni and Fe).
The effect of soluble coke removal on leaching step was studied. It was found that the removal of soluble coke significantly enhances the leaching of contaminants and barely affected the removal of active metals
... Show More
(5)
The study was conducted in the poultry field, College of Agriculture, Al-Muthanna University from 1/3/2018 to 6/4/2018 to determine the effect of commercial Ascomax powder produced from seaweed (Ascophyllum nodocum) on some productive performance of broilers. A total of 400, one day, Ross 308 broiler chicks were used for 35 days. The chicks were randomly distributed to 4 treatments, four replicates per treatment (25 chick / replicate). The treatments were as follows: T1: (control treatment), while T2, T3 and T4 added diet by Ascomax powder by 1, 1.5 and 2 g per 1 kg of the basal diet, respectively. The results of the study showed a significant superiority (P <0.05) for the added Ascomax powder treatments compared to the treatment of control
... Show More
(1)
The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn
... Show MoreBackground: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirements. Midline fracture; poor thermal conductivity and water sorption, are common problem in this material. The purpose of this study was to evaluate the effect of addition of surface treated Aluminum oxide nano fillers on some properties of heat cured (PMMA). Materials and methods: In addition to controlled group of heat cured PMMA the silanized (Al2O3) nanoparticles was added to PMMA powder by weight in three different percentages 1wt%, 2wt% and 3wt%, mixed by probe ultra-sonication machine. 200 specimens were constructed and divided into 5 groups according to the test (e
... Show MoreThis research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3
... Show More
(7)
(4)
SIFCON is characterized as a construction material of high ductility and very high strength. It is suitable for concrete structures used for special applications. However, the density of SIFCON is much higher than that of Fiber Reinforced Concrete (FRC) due to the need for a large amount of high-density steel fibers. This work examines the split tensile behavior of modified weight slurry infiltrated fiber concrete utilizing a mixture of two types of fibers, steel fiber, and polyolefin fiber. For the investigation, 30 cylinders and 15 cubes were poured. The used volume fraction (V.F) is (6 %) and the use of five series once as each type separately and once a hybrid in proportions of 2/3 polyolefin with 1/3 steel fiber and
... Show More
(4)