The corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ΔH, and activation entropies, ΔS, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the 50 cm3/L inhibitor concentration. The polarization curves show that peach Juice is a mixed inhibitor.
This research aims to investigate the effect of four types of nanomaterial on the Marshall properties and durability of warm mix asphalt (WMA). These types are; nano silica(NS), nano carbonate calcium (NCC), nano clay(NC), and nanoplatelets (NP). For each type of Nanomaterial, three contents are tried as following; NS(1%, 3%, and 5%), NCC(2%, 4%, and 6%), NC(3%, 5%, and 7%), and NP (2%, 4%, and 6%) by weight of asphalt cement. Following Marhsall mix design method, the optimum asphalt cement content is determined, thereafter the optimum dosage for each nanomaterial is obtained based on the highest Marshall stability value. The durability of the control mix (no nanomaterial) and modified mixtures have been compared based on moisture damage, r
... Show More
(11)
(8)
The study aims to measure the impact of reporting on value creation on the earnings quality of the economic unit by presenting and discussing the conceptual aspects of the value creation process through multi-capital and the importance of reporting it in Iraqi private banks in addition to presenting and analyzing the concept of profit quality and its measurement models. Therefore, the checklist prepared for this purpose was used based on previous studies related to the subject in order to determine the level of reporting of the research sample banks by analyzing the content of the annual reports of those banks as well as adopting the Tobin's Q scale to measure the value of the economic unit and then using some statistical models to
... Show More
The current study seeks to evaluate teacher preparation programs in the scientific disciplines at the College of Education in Al-Aqsa University in the light of the requirements of the labor market. It further aims to reveal the significance of the differences in the sample members’ response averages of to the availability of labor market requirements in the program that prepares the teacher of scientific disciplines at the Faculty of Education in Al-Aqsa University taking into account the (gender, program) variables. The study followed the descriptive analytical approach, and so a questionnaire was distributed to a sample of scientific discipline students in the teacher preparation program adopted in Al-Aqsa University, (200) male and
... Show More
The research aims to determine the impact of employees’ retention strategy on organizational memory. This research is historical, descriptive, and analytical. The sample consists of 158 faculty members in five private colleges in Baghdad. The technique used to analyze the data is SEM (Structural Equation Modeling), and SPSS (Statistical Package for the Social Sciences). The research concludes that the employees retaining strategy plays a vital role in retaining employees and hence maintains organizational memory. The findings and recommendations of this research assure the administrations of private colleges that employees retention strategy play a vital role in retaining its employee and hence maintains organizational memory. T
... Show More
(4)
(8)
Activated carbon was Produced from coconut shell and was used for removing sulfate from industrial waste water in batch Processes. The influence of various parameter were studied such as pH (4.5 – 9.) , agitation time (0 – 120)min and adsorbent dose (2 – 10) gm.
The Langmuir and frandlich adsorption capacity models were been investigated where showed there are fitting with langmmuir model with squre regression value ( 0.76). The percent of removal of sulfate (22% - 38%) at (PH=7) in the isotherm experiment increased with adsorbent mass increasing. The maximum removal value of sulfate at different pH experiments is (43%) at pH=7.
The thermal method was used to produce silicoaluminophosphate (SAPO-11) with different amounts of carbon nanotubes (CNT). XRD, nitrogen adsorption-desorption, SEM, AFM, and FTIR were used to characterize the prepared catalyst. It was discovered that adding CNT increased the crystallinity of the synthesize SAPO-11 at all the temperatures which studied, wile the maximum surface area was 179.54 m2/g obtained at 190°C with 7.5 percent of CNT with a pore volume of 0.317 cm3/g ,and with nano-particles with average particle diameter of 24.8 nm, while the final molar composition of the prepared SAPO-11 was (Al2O3:0.93P2O5:0.414SiO2).
(1)
(17)
(11)
Hand-lay up method was used to prepare the samples made of epoxy (EP) as a matrix reinforced with chopped carbon fibers (CCF). The fatigue behavior of epoxy resin /chopped carbon fiber composites was studied with different weight percentage of chopped carbon fibers (2.5%,5%,7.5%,10%,12.5%). The fatigue test was carried out under alternate bending method, which was made by applying sinusoidal wave with constant displacement (15mm), stress ratio R=-1,and loading frequency 10Hz, which is believed to give a negligible temperature rise during the test. The results of the maximum stress, fatigue strength, fatigue limit and fatigue life of the tested composites are calculated from stress(S)-number of cycles(N) (S-N) curves.
It was shown that
(1)
(42)
(38)