The catalytic activity of faujasite type NaY catalysts prepared from local clay (kaolin) with different Si/Al ratio was studied using cumene cracking as a model for catalytic cracking process in the temperature range of 450-525° C, weight hourly space velocity (WHSV) of 5-20 h1, particle size ≤75μm and atmospheric pressure. The catalytic activity was investigated using experimental laboratory plant scale of fluidized bed reactor.
It was found that the cumene conversion increases with increasing temperature and decreasing WHSV. At 525° C and WHSV 5 h-1, the conversion was 42.36 and 35.43 mol% for catalyst with 3.54 Si/Al ratio and Catalyst with 5.75 Si/Al ratio, respectively, while at 450° C and at the same WHSV, the conversion was decreased to 29.15 and 21.86 mol% respectively, and the catalyst of 5.75 Si/Al ratio gave the higher cumene activity than the catalyst with 3.54 Si/Al ratio.
(114)
(99)
The DC electrical conductivity properties of Ge60Se40-xTex alloy with x = 0, 5, 10, 15 and 20). The samples were formed in the form of discs with the thickness of 0.25–0.30 cm and the diameter of 1.5 cm. Samples were pressed under a pressure of 6 tons per cm2 , using a ton hydraulic press. They were prepared after being pressed using a ton hydraulic press using a hydraulic press. Melting point technology use to preper the samples. Continuous electrical conductivity properties were recorded from room temperature to 475 K. Experimental data indicates that glass containing 15% Te has the highest electrical conductivity allowing maximum current through the sample compared to Lu with other samples. Therefore, it is found that the DC co
... Show More
(2)
(2)
Denture bases are fabricated routinely using Poly(methyl methacrylate) (PMMA) acrylic resin. Yet, it is commonly known for its major drawbacks such as insufficient strength and ductility. The purpose of this study was to improve the performance of PMMA acrylic resin as a denture base material by reinforcement with surface treated lithium disilicate glass ceramic powder. The ceramic powder was prepared by grinding and sieving IPS e.max CAD MT blocks. Then, the powder was surface treated with an organosilane coupling agent (TMSPM) and added to PMMA in amount of 1%, 3%, 5% and 7% by weight. Characterizations of the powder was done by particle size analysis, XRD and FTIR. Transverse strength, Impact strength, Shore D hardness and surface roughn
... Show More
(2)
(2)
Abstract
In this work, pure Polypyrrole (PPy) and Polypyrrole (PPy)/Graphene (GN) was synthesized by in-situ polymerization in different weight percentages (0.1, 0.3, 0.5, 1, 3 and 5 wt.% (g)) of GN nano particles using chemical oxidation method at room temperature. The FTIR, SEM and electrical properties were studies for the nano composites. The result show that when concentration of GN Nano particle increase, the electrical conductivity increased and the graphene sheets were merging to form a continuous area of the GN through the polypyrrole base material. The FTIR spectra shows that the characteristics absorption peaks of polypyrrole that is, 1546.80, 1463.87 and 3400.27 cm-1(stretching vibration in the pyrrol
... Show More
(2)
(2)
(147)
(144)
(4)
(2)
The Chemistry of heterocyclic sulphur and nitrogen containing compounds have a great role in the field of scientific studies, The 2-amino 5-mercapto-1,3,4-thiadiazole ring for instance, has gained more importance in recent years because they are considered as potent biologically active nucleus. In this study disulfide derivative can be obtained by oxidation with hydrogen peroxide of thiol group of the heterocyclic 2-amino 5-mercapto-1,3,4-thiadiazole ring to obtain compound (3) with expected antibacterial activity. In order to use it as a diazo component to prepare some new bis azo compounds as possible antibacterial agents, the reaction of two primary amino groups on both sides of disulfide dimer with sodium nitr
... Show More
The present study was conducted to investigate the antimicrobial activity of the hot water and the hot ethanolic extracts of Thuja orientalis against some pathogenic microorganisms (Staphylococcus aureus, Pseudomonas aeruginosa, Eschericha coli, Proteus mirrablis, Salmonilla typhi, Klebsiella pneumoniae, Bacillus cereus, Bacillus subtilus, Acinobacter, Staphylococcus epidermidis and Candida albicans). Results showed that both the water and alcoholic extracts of this plant exert marked inhibitory effect against all the bacterial isolates and yeast and at different ratio, and it was shown that ethanolic extract was more effective in microbial inhibition than the water extract. Maximum inhibition (16 mm) was recorded against Staphylococcus aur
... Show MoreAlteration in the backbone structure of the endogenously released opioid peptides Leu5/Met5 enkephalins may result in compounds having comparable profile of pharmacological activity but with different physicochemical properties and side effects. Phthalyl amino acid and phthalyl esters are among the derivatives that have been synthesized and evaluated for their antibacterial and antifungal activities.This study was conducted to evaluate the possible analgesic activity of phthalyl-tyrosyl-glycin sodium that has been recently synthesized by our team.The study was carried out on 24 albino mice using hot plate method. The animals were allocated in to three groups; the first group received saline and represent a control g
... Show More